초록 ▼

This invention relates to an improved method for preparing stretchable multiple-component bonded composite sheets which involves bonding a fibrous layer of spirally-crimpable multiple-component continuous filaments or staple fibers to one or more non-spirally-crimpable layers using an array of inter

This invention relates to an improved method for preparing stretchable multiple-component bonded composite sheets which involves bonding a fibrous layer of spirally-crimpable multiple-component continuous filaments or staple fibers to one or more non-spirally-crimpable layers using an array of intermittent mechanical, chemical, or thermal bonds, and heating the bonded composite to activate the spiral crimp of the fibers in the spirally-crimpable layer. Multi-layer nonwoven fabrics prepared according to the method of the current invention have an improved combination of strength, aesthetics, stretch-recovery properties, and textile hand and drape compared to multiple-component nonwoven fabrics known in the art.

대표청구항 ▼

What is claimed is: 1. A stretchable multi-layer composite sheet comprising: a first polymeric layer comprising at least 20 weight percent of spirally-crimped multiple-component fibers, the multiple-component fibers having a cross-section and a length, and comprising a first polymeric component and

What is claimed is: 1. A stretchable multi-layer composite sheet comprising: a first polymeric layer comprising at least 20 weight percent of spirally-crimped multiple-component fibers, the multiple-component fibers having a cross-section and a length, and comprising a first polymeric component and a second polymeric component arranged in substantially distinct laterally eccentric zones across the cross-section of the multiple-component filaments and extending substantially continuously along the length of the multiple-component filaments; a second polymeric layer comprising less than 20 weight percent of laterally eccentric spirally-crimped multiple-component fibers and intermittently bonded to the first layer; the spirally-crimped multiple-component fibers in the first layer forming spirally-crimped fiber segments positioned substantially in the plane of the first layer and connecting the bonds; and the second layer forming buckled out-of-plane segments between the bonds; wherein the bonds are spaced between about 2 to 6 per centimeter with about 3.9 to 35 bonds/cm2 measured when the multi-layer composite sheet is in a substantially tensionless state. 2. The multi-layer composite sheet according to claim 1 wherein the second layer is intermittently bonded to the first layer by a method selected from the group consisting of thermal point bonding, ultrasonic point bonding, mechanical needling, hydraulic needling, chemical bonding, and adhesive bonding. 3. The multi-layer composite sheet according to claim 1 wherein the composite sheet has a thickness less than about 4 mm. 4. The multi-layer composite sheet according to claim 1 wherein the composite sheet has a bulk less than about 30 cc/g. 5. The multi-layer composite sheet according to claim 1, wherein the first polymeric layer comprises at least 50 weight percent of spirally-crimped multiple-component fibers and the second polymeric layer comprises less than 10 weight percent of spirally-crimped multiple-component fibers. 6. The multi-layer composite sheet according to claim 5, wherein the first polymeric layer comprises at least 70 weight percent of spirally-crimped multiple-component fibers and the second layer comprises 0 weight percent of spirally-crimped multiple-component fibers. 7. The multi-layer composite sheet according to claim 6, wherein the first polymeric layer consists essentially of spirally crimped multiple-component fibers. 8. The multi-layer composite sheet according to claim 1, wherein the first polymeric layer is a nonwoven web selected from the group consisting of carded webs, cross-laid webs, air-laid webs and multiple-component spunbond webs. 9. The multi-layer composite sheet according to claim 1, wherein the first polymeric layer comprises a warp of multiple-component filaments. 10. The multi-layer composite sheet according to claim 1, wherein the second polymeric layer is selected from the group consisting of nonwoven webs, films, knit fabrics, and woven fabrics. 11. The multi-layer composite sheet according to claim 1, wherein the first polymeric component is a partly crystalline polyester in which the chemical repeat-units of its crystalline region are in a non-extended stable conformation that does not exceed 90% of the length of the conformation of its fully extended chemical repeat-units and the second polymeric component is a partly crystalline polyester in which the chemical repeat-units of the crystalline region are in a conformation more closely approaching the length of the conformation of its fully extended chemical repeat-units than the first polymer. 12. The multi-layer composite sheet according to claim 11, wherein the non-extended first polymeric component is selected from the group consisting of poly(trimethylene terephthalate), poly(tetramethylene terephthalate), poly(propylene dinaphthalate), poly(propylene bibenzoate), copolymers thereof with ethylene sodium sulfoisophthalate, and polyester ethers and the extended second polymeric component is selected from the group consisting of poly(ethylene terephalate), poly(cyclohexyl 1,4-dimethylene terephthalate), copolymers thereof, and copolymers of ethylene terephthalate and the sodium salt of ethylene sulfoisophthalate. 13. The multi-layer composite sheet according to claim 12, wherein the first and second polymeric components are arranged in a side-by-side configuration. 14. The multi-layer composite sheet according to claim 1, wherein the composite sheet has a recoverable elastic stretch of at least 12% in at least one direction. 15. A process for preparing a stretchable multi-layer composite sheet comprising the steps of: providing a spirally-crimpable polymeric layer comprising at least 20 weight percent of spirally-crimpable multiple-component fibers, the multiple-component fibers having a cross-section and a length, and comprising a first polymeric component and a second polymeric component arranged in substantially distinct laterally eccentric zones across the cross-section of the multiple-component filaments and extending substantially continuously along the length of the multiple-component filaments; providing a non-spirally-crimpable polymeric layer comprising less than about 20 weight percent of laterally eccentric spirally-crimpable multiple-component fibers; intermittently bonding the first polymeric layer to the second polymeric layer with a plurality of bonds to form a bonded multi-layer composite sheet; heating the bonded multi-layer composite sheet to a temperature sufficient to cause the spirally-crimpable fibers in the first layer to develop three-dimensional spiral crimp, causing the bonded multi-layer composite sheet to shrink by at least 10% in area based on the original sheet area and the second polymeric layer to buckle between the bonds. 16. The process according to claim 15, wherein the bonded multi-layer composite sheet shrinks by at least 20% in area based on the original sheet area during the heating step. 17. The process according to claim 16, wherein the spirally-crimpable layer comprises at least 50 weight percent of spirally-crimpable multiple-component fibers and the non-spirally-crimpable layer comprises less than 10 weight percent of spirally-crimpable multiple-component fibers. 18. The process according to claim 17, wherein the spirally-crimpable layer comprises at least 70 weight percent of spirally-crimpable multiple-component fibers and the non-spirally-crimpable layer comprises substantially 0 weight percent of spirally-crimpable multiple-component fibers. 19. The process according to claim 15, wherein the spirally-crimpable layer is selected from the group consisting of warps of multiple-component filaments and multiple-component nonwoven webs. 20. The process according to claim 15, wherein the non-spirally-crimpable layer is selected from the group consisting of films, nonwoven webs, knit fabrics, and woven fabrics. 21. The process according to claim 19, wherein the spirally-crimpable layer is a nonwoven web selected from the group consisting of multiple-component carded webs, multiple-component cross-laid webs, multiple-component air-laid webs, and multiple-component spunbond webs. 22. The process according to claim 20, wherein the non-spirally-crimpable layer is a nonwoven web selected from the group consisting of carded webs, multiple-component cross-laid webs, air-laid webs, and spunbond webs. 23. The process according to claim 15, further comprising the step of pre-consolidating the non-spirally-crimpable layer prior to bonding to the spirally-crimpable layer. 24. The process according to claim 23, wherein the non-spirally-crimpable layer is pre-consolidated by mechanically flattening the layer. 25. The process according to claim 24, wherein the non-spirally-crimpable layer is flattened by passing the layer between a nip formed by two rotating rolls. 26. The process according to claim 15, wherein the intermittent bonds are formed using a bonding method selected from the group consisting of thermal point bonding, ultrasonic point bonding, mechanical needling, hydraulic needling, chemical bonding, and adhesive bonding. 27. The process according to claim 26, wherein the bonds are spaced between about 2 to 6 per centimeter with approximately 3.9 to 35 bonds/cm2. 28. The process according to claim 15, wherein the heating step is performed under free-shrinkage conditions. 29. The process according to claim 15, wherein the heating step comprises a wet finishing process. 30. The process according to claim 29, wherein the wet finishing process is a dyeing process. 31. The process according to claim 15, wherein the first polymeric component is a partly crystalline polyester in which the chemical repeat-units of its crystalline region are in a non-extended stable conformation that does not exceed 90% of the length of the conformation of its fully extended chemical repeat-units and the second polymeric component is a partly crystalline polyester in which the chemical repeat-units of the crystalline region are in a conformation more closely approaching the length of the conformation of its fully extended chemical repeat-units than the first polymer. 32. The process according to claim 31, wherein the non-extended first polymeric component is selected from the group consisting of poly(trimethylene terephthalate), poly(tetramethylene terephthalate), poly(propylene dinaphthalate), poly(propylene bibenzoate), copolymers thereof with ethylene sodium sulfoisophthalate, and polyester ethers and the extended second polymeric component is selected from the group consisting of poly(ethylene terephthalate), poly(cyclohexyl 1,4-dimethylene terephthalate), copolymers thereof, and copolymers of ethylene terephthalate and the sodium salt of ethylene sulfoisophthalate. 33. The process according to claim 32, wherein the first and second polymeric components of the multi-layer composite sheet are arranged in a side-by-side configuration. 34. The process according to claim 15, wherein the intermittently bonding step and the heating step are performed substantially at the same time. 35. An article of fabric comprising a stretchable multi-layer composite sheet further comprising: a first polymeric layer comprising at least 20 weight percent of spirally-crimped multiple-component fibers, the multiple-component fibers having a cross-section and a length, and comprising a first polymeric component and a second polymeric component arranged in substantially distinct laterally eccentric zones across the cross-section of the multiple-component filaments and extending substantially continuously along the length of the multiple-component filaments; a second polymeric layer comprising less than 20 weight percent of laterally eccentric spirally-crimped multiple-component fibers and intermittently bonded to the first layer; the spirally-crimped multiple-component fibers in the first layer forming spirally-crimped fiber segments positioned substantially in the plane of the first layer and connecting the bonds; and the second layer forming buckled out-of-plane segments between the bonds.