One aspect of the invention relates to a dehydrogenation catalyst composite containing alumina, chromium oxide, lithium oxide, and sodium oxide. The invention also relates to methods of making the dehydrogenation catalyst composite. Another aspect of the invention relates to method of dehydrogenati
One aspect of the invention relates to a dehydrogenation catalyst composite containing alumina, chromium oxide, lithium oxide, and sodium oxide. The invention also relates to methods of making the dehydrogenation catalyst composite. Another aspect of the invention relates to method of dehydrogenating a dehydrogenatable hydrocarbon involving contacting the dehydrogenatable hydrocarbon with a dehydrogenation catalyst composite containing alumina, chromium oxide, lithium oxide, and sodium oxide to provide a dehydrogenated hydrocarbon, such as an olefin.
대표청구항▼
What is claimed is: 1. A dehydrogenation catalyst composite comprising: about 60% or more and about 95% by weight or less of alumina; about 5% or more and about 30% by weight or less of chromium oxide; about 0.1% or more and about 1% by weight or less of lithium oxide; and about 0.01% or more and
What is claimed is: 1. A dehydrogenation catalyst composite comprising: about 60% or more and about 95% by weight or less of alumina; about 5% or more and about 30% by weight or less of chromium oxide; about 0.1% or more and about 1% by weight or less of lithium oxide; and about 0.01% or more and about 5% by weight or less of sodium oxide. 2. The dehydrogenation catalyst composite of claim 1, wherein the chromium oxide, lithium oxide, and sodium oxide are incorporated into a porous matrix of alumina. 3. The dehydrogenation catalyst composite of claim 1, wherein the chromium oxide and sodium oxide are incorporated into a porous matrix of alumina and lithium oxide. 4. The dehydrogenation catalyst composite of claim 1, wherein the dehydrogenation catalyst composite comprises about 75% or more and about 85% by weight or less of alumina, about 15% or more and about 22% by weight or less of chromium oxide, about 0.1% or more and about 1% by weight or less of lithium oxide, about 0.1% or more and about 1% by weight or less of sodium oxide. 5. The dehydrogenation catalyst composite of claim 1 further comprising about 0.01% or more and about 10% by weight or less of an additive comprising at least one selected from the group consisting of an extrusion agent, a rheology control agent, a binder, a surface active agent, and a clay. 6. The dehydrogenation catalyst composite of claim 1, wherein the dehydrogenation catalyst composite has a surface area of about 50 m2/g or more and about 250 m2/g or less. 7. The dehydrogenation catalyst composite of claim 1, wherein the dehydrogenation catalyst composite has a shape selected from the group consisting of at least one of spheres, tablets, cylinders, stars, tri-lobes, quadra-lobes, pellets, pills, granules, honeycombs, and cubes. 8. The dehydrogenation catalyst composite of claim 1, with the proviso that the dehydrogenation catalyst composite does not comprise nickel, platinum, palladium or zinc. 9. The dehydrogenation catalyst composite of claim 1, wherein the dehydrogenation catalyst composite has a ratio of chromium oxide to lithium oxide is from about 1:1 to about 500:1 on a weight basis. 10. A method of making a catalyst composite comprising: mixing alumina and a lithium compound to form a first mixture; shaping the first mixture; combining the shaped mixture with a chromium compound and a sodium compound to form a second mixture; and heating the second mixture at a temperature of about 500째 C. or more and about 900째 C. or less for about 1 minute or more and about 400 minutes or less. 11. The method of claim 10, further comprising heating the shaped mixture at a temperature of about 500째 C. or more and about 1,000째 C. or less for about 1 minute or more and about 300 minutes or less. 12. The method of claim 10, wherein the first mixture comprises about 85% or more and about 99.9% by weight or less of alumina and about 0.1% or more and about 15% by weight or less of the lithium compound. 13. The method of claim 10, wherein shaping the first mixture comprises extruding the first mixture to form the shaped mixture. 14. The method of claim 10, wherein the shaped mixture has a surface area of about 50 m2/g or more and about 400 m2 /g or less. 15. The method of claim 10, further comprising; drying the shaped mixture before combining the shaped mixture with a chromium compound and a sodium compound; and drying the second mixture before heating the second mixture. 16. The method of claim 11, wherein the temperature at which the shaped mixture is heated is higher than the temperature at which the second mixture is heated. 17. A method of making a catalyst composite comprising: mixing and shaping alumina to form a shaped mixture; combining the shaped mixture with a chromium compound, a lithium compound, and a sodium compound to form a second mixture and heating the second mixture at a temperature of about 500째 C. or more and about 900째 C. or less for about 1 minute or more and about 400 minutes or less. 18. The method of claim 17, further comprising heating the shaped mixture at a temperature of about 500째 C. or more and about 1,000째 C. or less for about 1 minute or more and about 300 minutes or less. 19. The method of claim 17, further comprising; drying the shaped mixture before combining the shaped mixture with a chromium compound, a lithium compound, and a sodium compound; and drying the second mixture before heating the second mixture. 20. The method of claim 17, wherein shaping alumina comprises extruding alumina to form the shaped mixture. 21. A dehydrogenation catalyst composite comprising: about 60% or more and about 95% by weight or less of alumina; about 5% or more and about 30% by weight or less of chromium oxide; about 0.1% or more and about 1% by weight or less of lithium oxide; and about 0.1% or more and about 1% by weight or less of sodium oxide, wherein the chromium oxide and sodium oxide are incorporated into a porous matrix of alumina and lithium oxide. 22. The dehydrogenation catalyst composite of claim 21, wherein the chromium oxide, lithium oxide, and sodium oxide are incorporated into a porous matrix of alumina. 23. The dehydrogenation catalyst composite of claim 21, further comprising about 0.01% or more and about 10% by weight or less of an additive comprising at least one selected from the group consisting of an extrusion agent, a rheology control agent, a binder, a surface active agent, and a clay. 24. The dehydrogenation catalyst composite of claim 21, wherein the dehydrogenation catalyst composite comprises about 75% or more and about 85% by weight or less of alumina, about 15% or more and about 22% by weight or less of chromium oxide, about 0.1% or more and about 1% by weight or less of lithium oxide, about 0.1% or more and about 1% by weight or less of sodium oxide. 25. The dehydrogenation catalyst composite of claim 21, wherein the dehydrogenation catalyst composite has a surface area of about 50 m2/g or more and about 250 m2/g or less. 26. The dehydrogenation catalyst composite of claim 21, wherein the dehydrogenation catalyst composite has a shape selected from the group consisting of at least one of spheres, tablets, cylinders, stars, tri-lobes, quadra-lobes, pellets, pills, granules, honeycombs, and cubes. 27. The dehydrogenation catalyst composite of claim 21, with the proviso that the dehydrogenation catalyst composite does not comprise nickel, platinum, palladium or zinc. 28. The dehydrogenation catalyst composite of claim 21, wherein the dehydrogenation catalyst composite has a ratio of chromium oxide to lithium oxide is from about 1:1 to about 500:1 on a weight basis.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (14)
Cortright Randy D. ; Dumesic James A., Catalyst to dehydrogenate paraffin hydrocarbons.
Crosbie Gary M. (Dearborn MI) Tennenhouse Gerald J. (Southfield MI) Tischer Ragnar P. (Birmingham MI) Wroblowa Halina S. (West Bloomfield MI), Electronically conductive lithia doped oxide ceramics for use in sodium sulfur batteries.
Iezzi Rodolfo (San Donato Milanese ITX) Bartolini Andrea (San Donato Milanese ITX) Buonomo Franco (San Donato Milanese ITX), Process for activating catalyst precursors for the dehydrogenation of C2-C5 paraffins, and a catalytic composition activ.
Carin, Christianne; Gorbell, Brian N.; Carin, legal representative, Christianne; Fedkenheuer, Alvin W.; Jonasson, John S.; Starosud, Alexander, Process and system for drying and heat treating materials.
Carin, Christianne; Gorbell, Brian N.; Fedkenheuer, Alvin W.; Jonasson, John S.; Starosud, Alexander, Process and system for drying and heat treating materials.
Gorbell, Brian N.; Carin, legal representative, Christianne; Fedkenheuer, Alvin W.; Jonasson, John S.; Starosud, Alexander, Process and system for drying and heat treating materials.
Carin, Christianne; Gorbell, Brian N.; Carin, legal representative, Christianne; Fedkenheuer, Alvin W.; Jonasson, John S.; Starosud, Alexander, Systems for prevention of HAP emissions and for efficient drying/dehydration processes.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.