The present invention relates to a soft thermoplastic elastomer composition that is free of thermoplastic resin that can be utilized in manufacturing shoe sole inserts, seals, gaskets, wheels, and that can be overmolded on a hard substrate, such as a metal or a thermoplastic resin, for grips or hand
The present invention relates to a soft thermoplastic elastomer composition that is free of thermoplastic resin that can be utilized in manufacturing shoe sole inserts, seals, gaskets, wheels, and that can be overmolded on a hard substrate, such as a metal or a thermoplastic resin, for grips or handles on various household items. The present invention more specifically discloses a thermoplastic elastomer composition that is made by a process comprising: (1) mixing (A) a block copolymer comprising a first polymeric block that is comprised of repeat units that are derived from a vinyl aromatic monomer and a second block that is comprised of repeat units that are derived from a conjugated diolefin monomer, wherein the repeat units in the second block are hydrogenated, and wherein the repeat units in the second block are elastomeric in nature, (B) a crosslinkable elastomer, and (C) an oil, to produce an un-crosslinked three component blend; and (2) dynamically crosslinking the crosslinkable elastomer in the un-crosslinked three component blend during a thermo-mechanical mixing step; wherein the thermoplastic elastomer composition is void of thermoplastic resins.
대표청구항▼
What is claimed is: 1. A thermoplastic elastomer composition that is made by a process comprising: (1) mixing (A) a block copolymer comprising a first polymeric block that is comprised of repeat units that are derived from a vinyl aromatic monomer and a second block that is comprised of repeat unit
What is claimed is: 1. A thermoplastic elastomer composition that is made by a process comprising: (1) mixing (A) a block copolymer comprising a first polymeric block that is comprised of repeat units that are derived from a vinyl aromatic monomer and a second block that is comprised of repeat units that are derived from a conjugated diolefin monomer, wherein the repeat units in the second block are hydrogenated, and wherein the repeat units in the second block are elastomeric in nature, (B) a crosslinkable elastomer, wherein the crosslinkable elastomer is comprised of repeat units that are derived from 1,3-butadiene, isoprene, and a vinyl aromatic monomer, wherein the repeat units in the crosslinkable elastomer are distributed in a random manner, and wherein the crosslinkable elastomer is coupled with a tin coupling agent or a silicon coupling agent, and (C) an oil, to produce an un-crosslinked three component blend; and (2) dynamically crosslinking the crosslinkable elastomer in the un-crosslinked three component blend during a thermo-mechanical mixing step; wherein the thermoplastic elastomer composition is void of thermoplastic resins, wherein said thermoplastic resins are not retractable to their original shape after being stretched and released beyond their yield point. 2. A thermoplastic elastomer composition as specified in claim 1 wherein the oil is present at a level which is within the range of about 10 to about 700 parts by weight per 100 parts by weight of the block copolymer. 3. A thermoplastic elastomer composition as specified in claim 1 wherein at least about 90% of the double bonds in the repeat units in the second block are hydrogenated. 4. A thermoplastic elastomer composition as specified in claim 1 wherein the block copolymer is selected from the group consisting of styrene-ethylene, butylene-styrene block copolymers, styrene-ethylene, propylene-styrene block copolymers, styrene-ethylene, propylene block copolymers, styrene-ethylene, ethylene propylene-styrene block copolymers, partially hydrogenated products of styrene-isoprene, butadiene-styrene block copolymers, styrene-butadiene-styrene block copolymers, and styrene-isoprene-styrene block copolymers. 5. A thermoplastic elastomer composition as specified in claim 1 wherein the oil is an extender oil selected from the group consisting of paraffinic oils, naphthenic oils, and polybutene. 6. A thermoplastic elastomer composition as specified in claim 1 wherein the block copolymer is a styrene-ethylene, butylene-styrene triblock polymer, wherein the ethylene, butylene block is obtained by the hydrogenation of a butadiene mid block with a vinyl content of no less than 30 percent by weight. 7. A thermoplastic elastomer composition as specified in claim 1 wherein the block copolymer has a weight average molecular weight of at least 100,000. 8. A thermoplastic elastomer composition as specified in claim 1 wherein the crosslinkable elastomer is crosslinked with a phenolic curing system. 9. A thermoplastic elastomer composition as specified in claim 1 wherein the crosslinkable elastomer is crosslinked with sulfur. 10. A thermoplastic elastomer composition as specified in claim 1 wherein the crosslinkable elastomer is crosslinked with a peroxide curing system. 11. A thermoplastic elastomer composition as specified in claim 1 wherein the crosslinkable elastomer is crosslinked with a hydrosilation curing system. 12. A thermoplastic elastomer composition as specified in claim 1 wherein at least about 95% of the double bonds in the repeat units in the second block are hydrogenated. 13. A thermoplastic elastomer composition as specified in claim 1 wherein the crosslinkable elastomer is dynamically crosslinked with a metal fatty acid salt cure system. 14. A thermoplastic elastomer composition as specified in claim 11 wherein the hydrosilation cure system is comprised of a hydrosilation agent and a hydrosilation catalyst. 15. A thermoplastic elastomer composition as specified in claim 14 wherein the hydrosilation agent contains at least two silicon hydride (Si--H) groups per molecule and contains 0.003 to 2.0 weight percent of hydrogen bonded to silicon, and is selected from the group consisting of trimethylsiloxy terminated methylhydrosiloxane-dimethylsiloxane copolymers, hydride terminated polydimethylsiloxanes, hydride terminated methylhydrosiloxane-dimethylsiloxane copolymers, trimethylsiloxy terminated polymethylhydrosiloxanes, poly(dimethylhydrogensiloxy)silanes, tetrakis(dimethylsiloxy)silanes, tetrakis(dimethylsiloxy)silane, methyl tris (dimethyl siloxy) silane, phenyl tris (dimethylsiloxy)silane, polymethylcyclotetrasiloxanes and silicon hydrides of methylsiloxanes or polymethyldi-and polymethylsiloxanes. 16. A thermoplastic elastomer composition as specified in claim 14 wherein the hydrosilation catalyst is selected from the group consisting of a platinum, platinum zero compounds complexed with compounds selected from carbon monoxide, fumarates, maleates, phosphines, divinyltetramethyldisiloxanes or tetravinyltetramethylcycliesiloxanes, palladium, chloroplatinic acid, platinum chloride complexes in alcohols, and rhodium, that is complexed with a member selected from divinyltetramethyldisiloxanes or polyvinylmethyldisiloxanes or cyclovinylmethylsiloxanes wherein additional divinylsiloxanes or polyvinylsiloxanes or polyvinylmethylcyclosiloxanes are present, wherein the catalyst or catalyst complexed compounds are incorporated on the block copolymer, crosslinkable elastomer, and/or oil, and are preferably present from about 0.0015 to about 1 parts metal by weight of the crosslinkable elastomer. 17. A thermoplastic elastomer composition as specified in claim 14 wherein the hydrosilation catalyst is added by incorporating onto an inert carrier selected from the group consisting of fumed silica, precipitated silica, talc, calcium carbonate, paraffinic oil, and carbon black. 18. A thermoplastic elastomer composition as specified in claim 17 wherein the inert carrier is present at a level which is within the range of 0.01 to 10 parts by weight per 100 parts by weight of the crosslinkable elastomer. 19. A thermoplastic elastomer composition as specified in claim 17, wherein said thermoplastic elastomer composition is in the form of pellets, and wherein the soft thermoplastic elastomer composition is pelletized as it is being discharged from the thermo-mechanical mixing step. 20. A thermoplastic elastomer composition of claim 14 wherein the hydrosilation agent is tetrakis (dimethylhydrogensiloxy)silane. 21. A thermoplastic elastomer composition of claim 14 wherein the hydrosilation catalyst is a platinum zero compound that is complexed with carbon monoxide and polyvinylmethylcyclicsiloxanes to give a platinum carbonyl complex in cyclic methylvinylsiloxanes. 22. A thermoplastic elastomer composition as specified in claim 1 wherein the oil is present at a level which is within the range of about 50 to about 500 parts by weight per 100 parts by weight of the block copolymer. 23. A thermoplastic elastomer composition as specified in claim 1 wherein the oil is present at a level which is within the range of about 70 to about 400 parts by weight per 100 parts by weight of the block copolymer. 24. A thermoplastic elastomer composition as specified in claim 1 wherein the crosslinkable elastomer is present at a level which is within the range of about 5 to about 400 parts by weight per 100 parts by weight of the block copolymer. 25. A thermoplastic elastomer composition as specified in claim 1 wherein the crosslinkable elastomer is present at a level which is within the range of about 15 to about 200 parts by weight per 100 parts by weight of the block copolymer. 26. A thermoplastic elastomer composition as specified in claim 1 wherein the crosslinkable elastomer is present at a level which is within the range of about 25 to about 120 parts by weight per 100 parts by weight of the block copolymer. 27. A thermoplastic elastomer composition that is made by a process comprising: (1) mixing (A) a block copolymer comprising a first polymeric block that is comprised of repeat units that are derived from a vinyl aromatic monomer and a second block that is comprised of repeat units that are derived from a conjugated diolefin monomer, wherein the repeat units in the second block are hydrogenated, and wherein the repeat units in the second block are elastomeric in nature, (B) a crosslinkable elastomer, wherein the crosslinkable elastomer is an acrylic copolymer, wherein the acrylic copolymer is functionalized with a halogen, and (C) an oil, to produce an un-crosslinked three component blend; and (2) dynamically crosslinking the crosslinkable elastomer in the un-crosslinked three component blend during a thermo-mechanical mixing step; wherein the thermoplastic elastomer composition is void of thermoplastic resins. 28. A thermoplastic elastomer composition as specified in claim 27 wherein the oil is present at a level which is within the range of about 10 to about 700 parts by weight per 100 parts by weight of the block copolymer. 29. A thermoplastic elastomer composition as specified in claim 27 wherein at least about 90% of the double bonds in the repeat units in the second block are hydrogenated. 30. A thermoplastic elastomer composition as specified in claim 27 wherein the block copolymer is selected from the group consisting of styrene-ethylene, butylene-styrene block copolymers, styrene-ethylene, propylene-styrene block copolymers, styrene-ethylene, propylene block copolymers, styrene-ethylene, ethylene propylene-styrene block copolymers, partially hydrogenated products of styrene-isoprene, butadiene-styrene block copolymers, styrene-butadiene-styrene block copolymers, and styrene-isoprene-styrene block copolymers. 31. A thermoplastic elastomer composition as specified in claim 27 wherein the oil is an extender oil selected from the group consisting of paraffinic oils, naphthenic oils, and polybutene. 32. A thermoplastic elastomer composition as specified in claim 27 wherein the block copolymer is a styrene-ethylene, butylene-styrene triblock polymer, wherein the ethylene, butylene block is obtained by the hydrogenation of a butadiene mid block with a vinyl content of no less than 30 percent by weight. 33. A thermoplastic elastomer composition as specified in claim 27 wherein the block copolymer has a weight average molecular weight of at least 100,000. 34. A thermoplastic elastomer composition as specified in claim 27 wherein the oil is present at a level which is within the range of about 50 to about 500 parts by weight per 100 parts by weight of the block copolymer. 35. A thermoplastic elastomer composition as specified in claim 27 wherein the oil is present at a level which is within the range of about 70 to about 400 parts by weight per 100 parts by weight of the block copolymer. 36. A thermoplastic elastomer composition as specified in claim 27 wherein the crosslinkable elastomer is present at a level which is within the range of about 5 to about 400 parts by weight per 100 parts by weight of the block copolymer. 37. A thermoplastic elastomer composition as specified in claim 27 wherein the crosslinkable elastomer is present at a level which is within the range of about 15 to about 200 parts by weight per 100 parts by weight of the block copolymer. 38. A thermoplastic elastomer composition as specified in claim 27 wherein the crosslinkable elastomer is present at a level which is within the range of about 25 to about 120 parts by weight per 100 parts by weight of the block copolymer. 39. A thermoplastic elastomer composition that is made by a process comprising: (1) mixing (A) a block copolymer comprising a first polymeric block that is comprised of repeat units that are derived from a vinyl aromatic monomer and a second block that is comprised of repeat units that are derived from a conjugated diolefin monomer, wherein the repeat units in the second block are hydrogenated, and wherein the repeat units in the second block are elastomeric in nature, (B) a crosslinkable elastomer, wherein the crosslinkable elastomer is a polyamide elastomer, and (C) an oil, to produce an un-crosslinked three component blend; and (2) dynamically crosslinking the crosslinkable elastomer in the un-crosslinked three component blend during a thermo-mechanical mixing step; wherein the thermoplastic elastomer composition is void of thermoplastic resins. 40. A thermoplastic elastomer composition as specified in claim 39 wherein a black copolymer is grafted onto the polyamide elastomer, wherein the block copolymer is comprised of a first polymeric block that is comprised of repeat units that are derived from a vinyl aromatic monomer and a second block that is comprised of repeat units that are derived from a conjugated diolefin monomer, wherein the repeat units in the second block are hydrogenated, and wherein the repeat units in the second block are elastomeric in nature. 41. A thermoplastic elastomer composition as specified in claim 39 wherein the oil is present at a level which is within the range of about 10 to about 700 parts by weight per 100 parts by weight of the block copolymer. 42. A thermoplastic elastomer composition as specified in claim 39 wherein at least about 90% of the double bonds in the repeat units in the second block are hydrogenated. 43. A thermoplastic elastomer composition that is made by a process comprising: (1) mixing (A) a block copolymer comprising a first polymeric block that is comprised of repeat units that are derived from a vinyl aromatic monomer and a second block that is comprised of repeat units that are derived from a conjugated diolefin monomer, wherein the repeat units in the second block are hydrogenated, and wherein the repeat units in the second block are elastomeric in nature, (B) a crosslinkable elastomer, wherein the crosslinkable elastomer is a polyurethane elastomer, and (C) an oil, to produce an un-crosslinked three component blend; and (2) dynamically crosslinking the crosslinkable elastomer in the un-crosslinked three component blend during a thermo-mechanical mixing step; wherein the thermoplastic elastomer composition is void of thermoplastic resins. 44. A thermoplastic elastomer composition as specified in claim 43 wherein a block copolymer is grafted onto the polyurethane elastomer, wherein the block copolymer is comprised of a first polymeric block that is comprised of repeat units that are derived from a vinyl aromatic monomer and a second block that is comprised of repeat units that are derived from a conjugated diolefin monomer, wherein the repeat units in the second block are hydrogenated, and wherein the repeat units in the second block are elastomeric in nature. 45. A thermoplastic elastomer composition that is made by a process comprising: (1) mixing (A) a block copolymer comprising a first polymeric block that is comprised of repeat units that are derived from a vinyl aromatic monomer and a second block that is comprised of repeat units that are derived from a conjugated diolefin monomer, wherein the repeat units in the second block are hydrogenated, and wherein the repeat units in the second block are elastomeric in nature, (B) a crosslinkable elastomer, wherein the crosslinkable elastomer is hydrogenated nitrile rubber and is compatibilized with a polyamide elastomer, and (C) an oil, to produce an un-crosslinked three component blend; and (2) dynamically crosslinking the crosslinkable elastomer in the un-crosslinked three component blend during a thermo-mechanical mixing step; wherein the thermoplastic elastomer composition is void of thermoplastic resins.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (41)
Azizian Hormoz (No. 1210 ; 3620 Kaneff Crescent Mississauga Ontario CAX L5A 3X1), Deuteration of unsaturated polymers and copolymers.
Takeichi Hideo ; Graves Daniel F. ; Sarkar Sunil B. ; Lawson David F., Diene polymers and copolymers incorporating partial coupling and terminals formed from hydrocarboxysilane compounds.
Takeichi Hideo,JPX ; Graves Daniel F. ; Sarkar Sunil B. ; Lawson David F. ; Hergenrother William L. ; Cole William M. ; Oziomek James, Diene polymers and copolymers incorporating partial coupling and terminals formed from hydrocarboxysilane compounds.
Puydak Robert C. (Cranbury NJ) Hazelton Donald R. (Chatham NJ) Cartasegna Silvestro (Brussels BEX) Dogniez Leonard (Brussels BEX), Dynamically vulcanized alloys of crystalline polyolefin resin and halobutyl rubber material.
Medsker Robert E. ; Hazelton Donald R. ; Gilbertson Gary W. ; Abdou-Sabet Sabet ; Shen Kuo-Shein ; Hazelton Ronald L. ; Ravishankar Periagaram S., Hydrosilylation crosslinking of thermoplastic elastomer.
Lawson David F. ; Hergenrother William L. ; Kerns Michael L., Polymers, elastomeric compounds and products thereof, derived from novel amine compounds containing side-chain organolit.
Medsker Robert E. ; Zhao Jianqun ; Gilbertson Gary W. ; Shen Kuo-Shein ; Wang Donald, Preferred process for silicon hydride addition and preferred degree of polymerization for silicon hydride for thermoplastic vulcanizates.
Dozeman Albertus O,NLX ; Gijsman Pieter,NLX ; Schepers Herman A. J.,NLX ; Debets Wilhelmus A. M.,NLX, Process for the preparation of a thermoplastic elastomer.
Inui Naoki (Yamatokoriyama JPX) Yamamoto Kazuaki (Toyonaka JPX) Nagasaki Hideo (Osaka JPX) Sasaki Manji (Nishinomiya JPX) Yachigo Shinichi (Toyonaka JPX), Rubber composition having excellent gripping power and rolling resistance, and production thereof.
Venkataswamy Krishna ; Horrion Jacques,BEX, Thermoplastic elastomer triblend from an engineering thermoplastic, functionalized ethylene and or diene polymer, and brominated isobutylene p-methylstyrene copolymer.
Patel Raman (578 Sun Valley Dr. Akron OH 44313) Abdou-Sabet Sabet (3568 Knollwood La. Akron OH 44313), Thermoplastic vulcanizates from isobutylene rubber and either EPDM or a conjugated diene rubber.
Medsker Robert E. ; Patel Raman ; Gilbertson Gary W. ; Hazelton Donald R., Vulcanization of carboxyl containing elastomers using reductive hydrosilylation with extension into dynamic vulcanization.
Aldrovandi Enrico (Bologna ITX) Norfo Luca (Bologna ITX) Piancastelli Patrizia (Bologna ITX) Saggese Gian A. (Ferrara ITX) Lionnet Roger (Brussels BEX), Vulcanized polyolefinic plastoelastomer composition and a process for its preparation.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.