초록 ▼

Advanced machine tool coatings for Ti machining are presented. The coatings of the present invention provide for protection from chemical reactivity and higher cutting temperatures. In accordance with one embodiment of the present invention, a coated machine tool is provided including a relatively

Advanced machine tool coatings for Ti machining are presented. The coatings of the present invention provide for protection from chemical reactivity and higher cutting temperatures. In accordance with one embodiment of the present invention, a coated machine tool is provided including a relatively hard underlayer and a chemically inert overlayer. The relatively hard underlayer is formed over the base material of the machine tool. The overlayer is formed over the underlayer, is chemically inert with respect to titanium, and comprises an oxide of yttrium or another metal oxide. In accordance with another embodiment of the present invention, a coated machine tool is provided including an alkaline earth metal fluoride overlayer that is substantially chemically inert with respect to titanium. The overlayer includes a metal intermixed with the metal fluoride. The intermixed metal is softer than the base material.

대표청구항 ▼

What is claimed is: 1. A coated machine tool comprising a multilayer wear resistant coating applied to a base material of said machine tool, said coating comprising a relatively hard underlayer and a chemically inert rare earth oxide overlayer, wherein: said relatively hard underlayer is formed ove

What is claimed is: 1. A coated machine tool comprising a multilayer wear resistant coating applied to a base material of said machine tool, said coating comprising a relatively hard underlayer and a chemically inert rare earth oxide overlayer, wherein: said relatively hard underlayer is formed over said base material of said machine tool and comprises at least two layers; one of said layers of said underlayer comprises a metal and is formed over said base material; another of said layers of said underlayer comprises a metal nitride, metal carbide, or metal carbo-nitride and is formed over said metal layer; said rare earth oxide overlayer is formed over said underlayer and said overlayer constitutes the outermost layer of the coated machine tool; and said rare earth oxide overlayer comprises a rare earth oxide that exhibits positive free energies of reaction with titanium. 2. A coated machine tool as claimed in claim 1 wherein said rare earth oxide comprises an oxide of scandium. 3. A coated machine tool as claimed in claim 1 wherein said rare earth oxide comprises an oxide of lanthanum. 4. A coated machine tool as claimed in claim 1 wherein said rare earth oxide comprises an oxide of yttrium. 5. A coated machine tool comprising a multilayer wear resistant coating for application to a base material of said machine tool, said coating comprising a relatively hard underlayer, an yttrium oxide overlayer, and an interlayer between said underlayer and said overlayer, wherein: said relatively hard underlayer is formed over said base material of said machine tool; said yttrium oxide overlayer is formed over said interlayer and said overlayer constitutes the outermost layer of the coated machine tool; said interlayer comprises first and second components; said first component of said interlayer comprises yttrium; relative proportions of said first and second components of said interlayer are graded across said interlayer such that a quantity of said yttrium in said interlayer increases from a side of said interlayer adjacent to said underlayer to a side of said interlayer adjacent to said overlayer; and said yttrium oxide overlayer exhibits positive free energies of reaction with titanium.