초록 ▼

The present invention provides an optical information medium having excellent weather resistance and repeating characteristics. The optical information medium has a barrier layer between a protective layer and a recording layer. The barrier layer includes GeN or GeON, and at least one element selec

The present invention provides an optical information medium having excellent weather resistance and repeating characteristics. The optical information medium has a barrier layer between a protective layer and a recording layer. The barrier layer includes GeN or GeON, and at least one element selected from the group consisting of Al, B, Ba, Bi, C, Ca, Ce, Cr, Dy, Eu, Ga, H, In, K, La, Mn, N, Nb, Ni, Pb, Pd, S, Si, Sb, Sn, Ta, Te, Ti, V, W, Yb, Zn and Zr.

대표청구항 ▼

What is claimed is: 1. A method of producing a phase change optical information recording medium comprising: a) forming a protective layer; b) forming a recording layer that generates a reversible phase-change, which can be optically detected according to an irradiation of an energy beam; c) formin

What is claimed is: 1. A method of producing a phase change optical information recording medium comprising: a) forming a protective layer; b) forming a recording layer that generates a reversible phase-change, which can be optically detected according to an irradiation of an energy beam; c) forming a first barrier layer by sputtering using a target containing a barrier material in an atmosphere gas containing nitrogen; and d) forming a second barrier layer by sputtering using a target containing a barrier material in an atmosphere gas containing nitrogen; wherein said first barrier layer is formed between said protective layer and said recording layer, said protective layer comprises sulfur, said recording layer has a thickness less than or equal to 20 nm and comprises tellurium, said second barrier layer is formed at a side of said recording layer opposite to said first barrier layer; and wherein a nitrogen partial pressure in the atmosphere gas for forming said first barrier layer is higher than a nitrogen partial pressure in the atmosphere gas for forming said second barrier layer. 2. A method of producing a phase change optical information recording medium comprising: a) forming a protective layer; b) forming a recording layer that generates a reversible phase-change, which can be optically detected according to an irradiation of an energy beam; c) forming a first barrier layer by sputtering in a mixed gas containing a rare gas and nitrogen using a target including at least Ge and X, where X is at least one element selected from the group consisting of elements belonging to Groups IIIa, IVa, Va, VIa, VIIa, VIII, Ib and IIb and C; and d) forming a second barrier layer by sputtering in a mixed gas containing a rare gas and nitrogen using a target including a barrier material; wherein said first barrier layer is formed between said protective layer and said recording layer, said protective layer comprises sulfur, said recording layer has a thickness less than or equal to 20 nm and comprises tellurium, said second barrier layer is formed on said recording layer; wherein said first barrier layer comprises either one selected from the group consisting of GeXN and GeXON as a main component; and wherein a content ratio of nitrogen in the mixed gas in forming the first barrier layer is different from a content ratio of nitrogen in forming the second barrier layer. 3. The method according to claim 2, wherein a content ratio of nitrogen in the mixed gas in forming the first barrier layer is larger than a content ratio of nitrogen in the mixed gas forming the second barrier layer. 4. A method of producing a phase change optical information recording medium comprising: a) forming a protective layer; b) forming a recording layer that generates a reversible phase-change, which can be optically detected according to an irradiation of an energy beam; c) forming a first barrier layer by sputtering with a target including at least Ge and X, where X is at least one element selected from the group consisting of elements belonging to Groups IIIa, IVa, Va, VIa, VIIa, VIII, Ib, IIb and C, in a mixed gas comprising a rare gas and nitrogen; and forming a second barrier layer by sputtering with a target including at least Ge and X in a mixed gas comprising a rare gas and nitrogen; wherein said first barrier layer is formed between said protective layer and said recording layer, said protective layer comprises sulfur, said recording layer has a thickness less than or equal to 20 nm and comprises tellurium, said second barrier layer is formed on the recording layer; wherein said first barrier layer comprises at least one selected from the group consisting of GeXN and GeXON as a main component; and wherein a composition ratio of Ge and X in the target used in forming the first barrier layer is represented by Ge1-mXm and a composition ratio of Ge and X in the target used in forming the second barrier layer is represented by Ge1-nXn, and the following inequality is satisfied: m<n, where 0<m<1, 0< n<1.