Glass is provided so as to have high visible transmission and/or fairly clear or neutral color. In certain example embodiments, the glass may include a base glass (e.g., soda lime silica base glass) and, in addition, by weight percentage: total iron (expressed as Fe2O3): 0.01 to 0.30%
Glass is provided so as to have high visible transmission and/or fairly clear or neutral color. In certain example embodiments, the glass may include a base glass (e.g., soda lime silica base glass) and, in addition, by weight percentage: total iron (expressed as Fe2O3): 0.01 to 0.30% erbium oxide (e.g., Er2O3): 0.01 to 0.30%.
대표청구항▼
What is claimed is: 1. Glass comprising: Ingredient wt. % SiO2 67-75% Na2O 10-20% CaO 5-15% total iron (expressed as Fe2O3) 0.01 to 0.30% erbium oxide 0.01 to 0.30% wherein the glass has visible transmission of at least 75%, and at least one of a transmissi
What is claimed is: 1. Glass comprising: Ingredient wt. % SiO2 67-75% Na2O 10-20% CaO 5-15% total iron (expressed as Fe2O3) 0.01 to 0.30% erbium oxide 0.01 to 0.30% wherein the glass has visible transmission of at least 75%, and at least one of a transmissive a* color value of-1.0 to +1.0 and a transmissive b* color value of-1.0 to +1.5, and wherein the glass comprises 0-0.0002% cerium oxide. 2. The glass of claim 1, wherein the glass comprises: total iron (expressed as Fe2O3) 0.02 to 0.20% erbium oxide 0.02 to 0.20%. 3. The glass of claim 2, wherein the glass comprises: total iron (expressed as Fe2O3) 0.03 to 0.15% erbium oxide 0.03 to 0.13%. 4. The glass of claim 1, wherein the glass has a visible transmission of at least 85% at a reference thickness of about 5.6 mm. 5. The glass of claim 1, wherein the glass has a visible transmission of at least 90% at a reference thickness of about 5.6 mm. 6. The glass of claim 1, wherein the glass has a redox value (FeO/Fe2O3) no greater than 0.20. 7. The glass of claim 1, wherein the glass has a redox value (FeO/Fe2O3) no greater than 0.15. 8. The glass of claim 1, wherein the glass has a redox value (FeO/Fe2O3) no greater than 0.13. 9. The glass of claim 1, wherein the glass further comprises less than or equal to 0.020% FeO. 10. The glass of claim 1, wherein the glass comprises from 0. 0015 to 0.015% FeO. 11. The glass of claim 1, wherein the glass comprises from 0. 0015 to 0.012% FeO. 12. The glass of claim 1, wherein the glass comprises less than or equal to 0.0002% cobalt oxide. 13. The glass of claim 1, wherein the glass comprises less than or equal to 0.0001% cobalt oxide. 14. The glass of claim 1, wherein the glass comprises less than or equal to 0.0001% cerium oxide. 15. Glass comprising: Ingredient wt. % SiO2 67-75% Na2O 10-20% CaO 5-15% total iron (expressed as Fe2O3) 0.01 to 0.30% erbium oxide 0.01 to 0.30% wherein the glass has visible transmission of at least 75%, and at least one of a transmissive a* color value of-1.0 to +1.0 and a transmissive b* color value of-1.0 to +1.5, and wherein the glass comprises 0-0.12% cerium oxide. 16. Glass comprising: Ingredient wt. % SiO2 67-75% Na2O 10-20% CaO 5-15% total iron (expressed as Fe2O3) 0.01 to 0.30% erbium oxide 0.01 to 0.30% wherein the glass has visible transmission of at least 75%, and at least one of a transmissive a* color value of-1.0 to +1.0 and a transmissive b* color value of-1.0 to +1.5, and wherein the glass is substantially free of both cerium oxide and cobalt oxide. 17. The glass of claim 1, wherein the glass includes less than 2 ppm of Se. 18. The glass of claim 1, wherein the glass includes less than 1 ppm of Se. 19. The glass of claim 1, wherein the glass comprises from 0. 02 to 0.13% erbium oxide. 20. The glass of claim 1, wherein the glass has a transmissive a* color value of-1.0 to +1.0 and a transmissive b* color value of-0.7 to +1.0. 21. The glass of claim 1, wherein the glass has a transmissive a* color value of-0.60 to +0.60 and a transmissive b* color value of-0.7 to +1.0. 22. The glass of claim 1, wherein the glass comprises from 0-5% MgO, from 0-5% K2O and from 0-5% Al2O3. 23. The glass of claim 1, wherein the glass comprises from 6-12% CaO and from 10-15% Na2O. 24. A glass comprising a base portion and a colorant portion, wherein the base portion of the glass comprises: Ingredient wt. % SiO2 67-75% Na2O 10-20% CaO 5-15% wherein the colorant portion of the glass consists essentially of: total iron (expressed as Fe2O3) 0.01 to 0.30% erbium oxide 0.01 to 0.30% wherein the glass has visible transmission of at least 75%, a transmissive a* color value of-1.0 to +1.0 and a transmissive b* color value of-1.0 to +1.5, and wherein the glass comprises 0-0.12% cerium oxide. 25. The glass of claim 24, wherein the colorant portion consists essentially of: total iron (expressed as Fe2O3) 0.02 to 0.20% erbium oxide 0.02 to 0.20%. 26. The glass of claim 24, wherein the colorant portion consists essentially of: total iron (expressed as Fe2O3) 0.03 to 0.15% erbium oxide 0.03 to 0.13%. 27. The glass of claim 24, wherein the glass has a visible transmission of at least 85% at a reference thickness of about 5.6 mm. 28. The glass of claim 24, wherein the glass has a visible transmission of at least 90% at a reference thickness of about 5.6 mm. 29. The glass of claim 24, wherein the glass has a redox value (FeO/Fe2O3) no greater than 0.20. 30. A high transmittance glass comprising: SiO2 67-75% Na2O 10-20% CaO 5-15% total iron (expressed as Fe2O3) 0.01 to 0.30% erbium oxide 0.01 to 0.30% wherein the glass has visible transmission of at least 88% at a references thickness of 5.6 mm, a transmissive a* color value of-1.0 to +1.0 and a transmissive b* color value of-1.0 to +1.5, and wherein the glass comprises 0-0.12% cerium oxide. 31. The glass of claim 30, wherein the glass comprises: total iron (expressed as Fe2O3) 0.02 to 0.20% erbium oxide 0.02 to 0.20%. 32. The glass of claim 30, wherein the glass comprises: total iron (expressed as Fe2O3) 0.03 to 0.15% erbium oxide 0.03 to 0.13%. 33. The glass of claim 30, wherein the glass has a visible transmission of at least 90% at a reference thickness of 5.6 mm. 34. The glass of claim 30, wherein the glass has a visible transmission of at least 90.5% at a reference thickness of 5.6 mm. 35. The glass of claim 30, wherein the glass has a redox value (FeO/Fe2O3) no greater than 0.20. 36. The glass of claim 30, wherein the glass has a redox value (FeO/Fe2O3) of from 0.10 to 0.20. 37. The glass of claim 30, wherein the glass is a soda-lime-silica based glass.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (33)
Krashkevich David G. (Dallas PA) Pucilowski Sally (Luzerne PA), Brown contrast enhancement glass.
Gulotta Joseph A. (New Kensington PA) Krumwiede John F. (Cheswick PA) Kutilek Luke A. (Oakmont PA) Longobardo Anthony V. (Butler PA) Heithoff Robert B. (Gibsonia PA), Dark gray, infrared absorbing glass composition and coated glass for privacy glazing.
Jeanvoine Pierre (Poissy FRX) Lismonde Michel (Courbevoie FRX) Vieslet Jacques (Ceroux Mousty BEX), Glass compositions intended for the production of panes.
Landa, Ksenia A.; Landa, Leonid; Longobardo, Anthony V.; Thomsen, Scott V.; Hall, Jr., David R., Grey glass composition including erbium, holmium, and/or yttrium.
Yukihito Nagashima JP; Akihiro Koyama JP; Isamu Kuroda JP; Masahiro Hirata JP; Masato Hyodo JP; Koichiro Nakamura JP, Light-colored glass of high transmittance and method for production thereof, glass plate with electrically conductive film and method for production thereof, and glass article.
Maugendre Stephane (Chantilly FRX) Dubois Bernard (Paris FRX), Process of production of a glass intended to be transformed into continuous or stable fibers.
Pecoraro George A. (Lower Burrell PA) Shelestak Larry J. (West Deer Township ; Allegheny County PA) ..AP: PPG Industries ; Inc. (Pittsburgh PA 02), Transparent infrared absorbing glass and method of making.
Lu, Yiwei; den Boer, Willem, Front electrode including transparent conductive coating on patterned glass substrate for use in photovoltaic device and method of making same.
Thomsen, Scott V.; Hulme, Richard; Landa, Leonid M.; Landa, Ksenia A., Low iron high transmission float glass for solar cell applications and method of making same.
Thomsen, Scott V.; Hulme, Richard; Landa, Leonid M.; Landa, Ksenia A., Low iron transmission float glass for solar cell applications and method of making same.
Thomsen, Scott V.; Lu, Yiwei; Krasnov, Alexey, Method of making front electrode of photovoltaic device having etched surface and corresponding photovoltaic device.
Lu, Yiwei; den Boer, Willem; Krasnov, Alexey, Photovoltaic device including front electrode having titanium oxide inclusive layer with high refractive index.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.