초록 ▼

The present invention provides a process for the preparation of an improved copper chromite catalyst for the hydrogenation of diethyl maleate to tetrahydrofuran with very high selectivity. This invention particularly relates to a process for the preparation of an improved copper chromite catalyst wi

The present invention provides a process for the preparation of an improved copper chromite catalyst for the hydrogenation of diethyl maleate to tetrahydrofuran with very high selectivity. This invention particularly relates to a process for the preparation of an improved copper chromite catalyst with specific composition and physical properties containing copper, chromium, zinc and aluminium as catalyst components in order to achieve selective production of tetrahydrofuran via single step hydrogenation of diethyl maleate. The calcination procedure has also been described to achieve the best activity. The catalyst has a life of more than 630 hours with constant activity. The used catalyst can also be regenerated to match the original hydrogenation activity.

대표청구항 ▼

We claim: 1. A copper chromite catalyst having the molar composition description="In-line Formulae" end="lead"Cu(a) Cr(b)Al(c)Zn(d) description="In-line Formulae" end="tail" wherein a=10-40 mole % b=10-40mole % c=10-30 mole % d=5-40mole % and a+b+c+d=100 and having an XRD pattern as shown i

We claim: 1. A copper chromite catalyst having the molar composition description="In-line Formulae" end="lead"Cu(a) Cr(b)Al(c)Zn(d) description="In-line Formulae" end="tail" wherein a=10-40 mole % b=10-40mole % c=10-30 mole % d=5-40mole % and a+b+c+d=100 and having an XRD pattern as shown in Table I. TABLE I XRD analysis of the copper chromite catalyst θ Intensity (%) 18. 100 26.2 100 27.4 48 35.8 92 44.2 48 56.6 44. 2. The catalyst as claimed in claim 1, wherein the catalyst consists essentially of mixed oxides of copper, chromium, aluminum and zinc. 3. A process for the preparation of a copper chromite catalyst having the molar composition description="In-line Formulae" end="lead"CU(a) Cr(b)Al(c)Zn(d) description="In-line Formulae" end="tail" wherein a=10-40 mole % b=10-40 mole % c=10-30 mole % d=0.5-40 mole % and a+b+c+d=100 and having an XRD pattern as shown in Table I TABLE I XRD analysis of the copper chromite catalyst θ Intensity (%) 18. 100 26.2 100 27.4 48 35.8 92 44.2 48 56.6 44 said process comprising the steps of: (a) preparing an aqueous solution comprising a source of copper, a source of aluminum and a source of zinc; (b) adding to the aqueous solution of step (a) a source of chromium while stirring to form a precipitate; (c) recovering the precipitate and calcining the precipitate at a temperature between 200-500째 C. for a period between 2-5 hours to obtain the catalyst. 4. A process as claimed in claim 3, wherein the source of copper is a copper salt selected from the group consisting of copper nitrate, copper sulfate, copper acetate and copper chloride. 5. A process as claimed in claim 3, wherein the source of aluminum is an aluminum salt selected from the group consisting of aluminum nitrate and aluminum oxide. 6. A process as claimed in claim 3, wherein the source of zinc is a salt of zinc selected from the group consisting of zinc nitrate, zinc sulfate, zinc chloride and zinc oxide. 7. A process as claimed in claim 3, wherein the source of chromium is an ammonium salt selected from the group consisting of ammonium dichromate and ammonium chromate. 8. A process as claimed in claim 3, wherein the source of aluminum is a chloride salt of aluminum. 9. A process as claimed in claim 3, comprising drying the precipitate recovered in step (c) at a temperature ranging between 80 to 110째 C. prior to the calcining. 10. A process as claimed in claim 3, wherein the calcining in step (c) is carried out in three steps with the temperature in each of the three calcining steps being higher than the temperature in the preceding calcining step.