초록 ▼

A process for the preparation of platy precipitated calcium carbonate comprising the steps of providing a suspension of calcium hydroxide, carbonating the suspension of calcium hydroxide, adding a polyacrylate to the suspension prior to the completion of carbonation to precipitate platy calcium carb

A process for the preparation of platy precipitated calcium carbonate comprising the steps of providing a suspension of calcium hydroxide, carbonating the suspension of calcium hydroxide, adding a polyacrylate to the suspension prior to the completion of carbonation to precipitate platy calcium carbonate. Also provided are a paper that is filled and a paper that is coated using the platy precipitated calcium carbonate according to the present invention.

대표청구항 ▼

What is claimed is: 1. A process for the preparation of platy precipitated calcium carbonate comprising the steps of: providing a suspension of calcium hydroxide, carbonating the suspension of calcium hydroxide, adding a polyacrylate to the suspension wherein the polyacrylate is added during the ch

What is claimed is: 1. A process for the preparation of platy precipitated calcium carbonate comprising the steps of: providing a suspension of calcium hydroxide, carbonating the suspension of calcium hydroxide, adding a polyacrylate to the suspension wherein the polyacrylate is added during the characteristic drop in specific conductivity of the suspension that occurs at about 60 to about 70 percent carbonation. 2. The process for the preparation of platy precipitated calcium carbonate according to claim 1, wherein the step of providing a suspension of calcium hydroxide is comprised of hydrating lime to form the calcium hydroxide suspension having a concentration of about 0.09 grams to about 0.14 grams calcium hydroxide per milliliter of suspension. 3. The process for the preparation of platy precipitated calcium carbonate according to claim 1, wherein the initial temperature of the suspension of calcium hydroxide prior to carbonation is in a range from about 8 degrees Celsius to about 18 degrees Celsius. 4. The process for the preparation of platy precipitated calcium carbonate according to clam 1, wherein citric acid is added in an amount up to about 0.15 percent dry citric acid on dry PCC by weight. 5. The process for the preparation of platy precipitated calcium carbonate according to claim 1, wherein the step of carbonating the suspension is performed until the pH of the resultant solution reaches about 7.5 to about 8.0. 6. The process for the preparation of platy precipitated calcium carbonate according to claim 1, wherein the step of adding a polyacrylate to the suspension is performed without discontinuing the step of carbonating the suspension. 7. The process for the preparation of platy precipitated calcium carbonate according to claim 1, wherein the step of adding a polyacrylate is performed by discontinuing the carbonating step, adding the polyacrylate as an aqueous solution, mixing the suspension, and resuming carbonating the suspension to precipitate platy PCC. 8. The process for the preparation of platy precipitated calcium carbonate according to claim 1, wherein the polyacrylate is added to the suspension during carbonation when the specific conductivity decreases at a rate of about 0.02 milliSiemens to about 0.04 milliSiemens per centimeter per second. 9. The process for the preparation of platy precipitated calcium carbonate according to claim 1, wherein the polyacrylate added to the suspension is selected from the group consisting of a polyacrylic acid and a neutralized polyacrylic acid salt. 10. The process for the preparation of platy precipitated calcium carbonate according to claim 1, wherein the polyacrylate added to the suspension has a molecular weight of from about 2,000 to about 10,000. 11. The process for the preparation of platy precipitated calcium carbonate according to claim 1, wherein the polyacrylate is added in an amount of at least about 1 percent by weight of dry polyacrylate on dry PCC yield.