IPC분류정보
국가/구분 |
United States(US) Patent
등록
|
국제특허분류(IPC7판) |
|
출원번호 |
US-0416206
(2001-11-21)
|
우선권정보 |
DE-100 58 700(2000-11-25) |
국제출원번호 |
PCT/FR01/003657
(2001-11-21)
|
§371/§102 date |
20031001
(20031001)
|
국제공개번호 |
WO02/042234
(2002-05-30)
|
발명자
/ 주소 |
- Schicht,Heinz
- Schindler,Herbert
- Schmidt,Uwe
- Marold,Axel
|
출원인 / 주소 |
- Saint Gobain Glass France
|
대리인 / 주소 |
Oblon, Spivak, McClelland, Maier &
|
인용정보 |
피인용 횟수 :
3 인용 특허 :
8 |
초록
▼
A glass pane is provided with a multilayer system having metallic reflection and a high thermal resistance. The multilayer system comprises a dielectric base layer, a metal layer having a high reflection, made of chromium or a metal alloy containing at least 45 wt % chromium, and a nitride top layer
A glass pane is provided with a multilayer system having metallic reflection and a high thermal resistance. The multilayer system comprises a dielectric base layer, a metal layer having a high reflection, made of chromium or a metal alloy containing at least 45 wt % chromium, and a nitride top layer. The dielectric base layer is composed of at least one oxide partial layer made of SnO2, ZnO and/or TiO 2, close to the surface of the glass, and a nitride partial layer, close to the metal layer.
대표청구항
▼
The invention claimed is: 1. A transparent pane having a transmission of visible light of between 2% and 15%, comprising: a substrate and a multilayer coating, wherein said multilayer coating comprises (i) a dielectric base layer comprising at least one oxide partial layer having a reflective index
The invention claimed is: 1. A transparent pane having a transmission of visible light of between 2% and 15%, comprising: a substrate and a multilayer coating, wherein said multilayer coating comprises (i) a dielectric base layer comprising at least one oxide partial layer having a reflective index of 2 or greater and a nitride partial layer, (ii) a metal layer comprising a chromium alloy containing at least 45 weight percent chromium, wherein the metal layer is contiguous with the nitride partial layer; and (iii) a dielectric nitride covering layer, wherein the chromium alloy is selected from the group consisting of a CrAl alloy containing from 75 to 80 weight percent chromium, a CrSi alloy containing from 45 to 85 weight percent chromium, and a CrSiAl alloy containing from 70 to 80 weight percent chromium. 2. The transparent pane of claim 1, wherein the at least one oxide partial layer is contiguous with the substrate. 3. The transparent pane of claim 1, wherein the at least one oxide partial layer is not contiguous with the substrate. 4. The transparent pane of claim 1, wherein the dielectric base layer comprises SnO2, ZnO, TiO2, and mixtures thereof. 5. The transparent pane of claim 1, wherein the dielectric base layer has a thickness ranging from 30 nm to 90 nm. 6. The transparent pane of claim 1, wherein the nitride partial layer has a thickness of at least 10 nm. 7. The transparent pane of claim 1, wherein the metal layer has a thickness ranging from 15 nm to 50 nm. 8. The transparent pane of claim 1, further comprising a metal or metal alloy protective layer that can be converted after heat treatment into an oxide layer, wherein the protective layer is in contact with dielectric nitride covering layer. 9. The transparent pane of claim 8, wherein the protective layer is selected from the group consisting of Zr, Ti, TiCr, ZrCr, TiNi, and mixtures thereof. 10. The transparent pane of claim 8, wherein the protective layer has a thickness ranging from 1 nm to 3 nm. 11. The transparent pane of claim 1, wherein the dielectric nitride covering layer comprises Si3N4, AlN, or a mixture thereof. 12. The transparent pane of claim 11, wherein the dielectric nitride covering layer has a thickness ranging from 1 nm to 3 nm. 13. The transparent pane of claim 1, wherein the multilayer coating is a continuous coating. 14. The transparent pane of claim 1, wherein the multilayer coating is a discontinuous coating. 15. A transparent pane having a minimum reflectance of visible light of at least 30%, comprising: a substrate and a multilayer coating, wherein said multilayer coating comprises (i) a dielectric base layer comprising at least one oxide partial layer having a reflective index of 2 or greater and a nitride partial layer, (ii) a metal layer comprising a chromium alloy containing at least 45 weight percent chromium, wherein the metal layer is contiguous with the nitride partial layer; and (iii) a dielectric nitride covering layer, wherein the chromium alloy is selected from the group consisting of a CrAl alloy containing from 75 to 80 weight percent chromium, a CrSi alloy containing from 45 to 85 weight percent chromium, and a CrSiAl alloy containing from 70 to 80 weight percent chromium. 16. The transparent pane of claim 15, wherein the at least one oxide partial layer is contiguous with the substrate. 17. The transparent pane of claim 15, wherein the at least one oxide partial layer is not contiguous with the substrate. 18. The transparent pane of claim 15, wherein the dielectric base layer comprises SnO2, ZnO, TiO2, and mixtures thereof. 19. The transparent pane of claim 15, wherein the dielectric base layer has a thickness ranging from 30 nm to 90 nm. 20. The transparent pane of claim 15, wherein the nitride partial layer has a thickness of at least 10 nm. 21. The transparent pane of claim 15, wherein the metal layer has a thickness ranging from 15 nm to 50 nm. 22. The transparent pane of claim 15, further comprising a metal or metal alloy protective layer that can be converted after heat treatment into an oxide layer, wherein the protective layer is in contact with dielectric nitride covering layer. 23. The transparent pane of claim 15, wherein the protective layer is selected from the group consisting of Zr, Ti, TiCr, ZrCr, TiNi, and mixtures thereof. 24. The transparent pane of claim 15, wherein the protective layer has a thickness ranging from 1 nm to 3 nm. 25. The transparent pane of claim 15, wherein the dielectric nitride covering layer comprises Si3N4, AIN, or a mixture thereof. 26. The transparent pane of claim 25, wherein the dielectric nitride covering layer has a thickness ranging from 1 nm to 3 nm. 27. The transparent pane of claim 15, wherein the multilayer coating is a continuous coating. 28. The transparent pane of claim 15, wherein the multilayer coating is a discontinuous coating.