Chemically and thermally stabilized alumina for Fischer-Tropsch catalysts
IPC분류정보
국가/구분
United States(US) Patent
등록
국제특허분류(IPC7판)
B01J-023/00
C07C-027/06
C07C-027/00
출원번호
US-0657585
(2003-09-08)
발명자
/ 주소
Fraenkel,Dan
출원인 / 주소
ConocoPhillips Company
대리인 / 주소
Conley Rose P.C.
인용정보
피인용 횟수 :
19인용 특허 :
57
초록▼
This invention is generally related to the field of Fischer-Tropsch catalysts. In particular, the present invention is related to a Fischer-Tropsch catalyst and method of making same. More particularly, the present invention discloses a catalyst comprising a support and at least one catalytically ac
This invention is generally related to the field of Fischer-Tropsch catalysts. In particular, the present invention is related to a Fischer-Tropsch catalyst and method of making same. More particularly, the present invention discloses a catalyst comprising a support and at least one catalytically active metal wherein the support comprises a transition alumina including theta-alumina, delta-alumina, or combinations thereof, and a surface coverage comprising at least one rare-earth oxide.
대표청구항▼
The invention claimed is: 1. A method of making a catalyst support comprising a) applying at least one compound of a rare-earth metal to an aluminum-comprising material to provide a rare-earth metal modified alumina precursor; b) drying the rare-earth metal modified alumina precursor under suitable
The invention claimed is: 1. A method of making a catalyst support comprising a) applying at least one compound of a rare-earth metal to an aluminum-comprising material to provide a rare-earth metal modified alumina precursor; b) drying the rare-earth metal modified alumina precursor under suitable conditions to provide a dried rare-earth metal modified alumina precursor; and c) calcining the dried rare-earth metal modified alumina precursor in a manner effective for converting at least a portion of the aluminum-comprising material to an alumina comprising at least one alumina phase selected from the group consisting of delta-alumina, theta-alumina, and combination thereof; and creating a surface coverage comprising an oxide of said at least one rare-earth metal, wherein said surface coverage coats the alumina at least partially, and wherein at least one rare-earth metal is trivalent, and further wherein the surface coverage is between about 0.2 nm and about 0.5 nm in thickness. 2. The method according to claim 1 wherein the aluminum-comprising material comprises at least one material selected from the group consisting of aluminum oxides, aluminum salts, aluminum alkoxides, aluminum hydroxides, pseudoboehmite, boehmite, gibbsite, bayerite, gamma-alumina, theta-alumina, delta-alumina, eta-alumina, rho-alumina, chi-alumina, kappa-alumina and any combinations thereof. 3. The method according to claim 1 wherein the aluminum-comprising material comprises a gamma-alumina. 4. The method according to claim 3 wherein the gamma-alumina has a surface area between about 100 m2/g and about 300 m 2/g; and a pore volume of at least about 0.2 ml/g. 5. The method according to claim 3 wherein the gamma-alumina comprises no more than about 0.1% by weight Na2O. 6. The method according to claim 1 wherein the compound of the rare-earth metal comprises a counterion selected from the group consisting of nitrate, acetate, oxalate, acetylacetonate, any alkanoate, any halide and sulfate. 7. The method according to claim 6 wherein the compound of the rare-earth metal is in a hydrated form. 8. The method according to claim 1 wherein the rare-earth metal is selected from the group consisting of yttrium, lanthanum, praseodymium, neodymium, samarium and gadolinium. 9. The method according to claim 1 wherein applying a compound of the rare-earth metal is carried out by an impregnation technique. 10. The method according to claim 9 wherein the impregnation technique is performed at about or below ambient pressure. 11. The method according to claim 9 wherein the impregnation technique is incipient wetness impregnation. 12. The method according to claim 1 wherein calcining is effective for creating a rare-earth metal oxide surface layer that completely covers the alumina surface. 13. The method according to claim 1 wherein calcining is effective for converting at least a portion of the aluminum-comprising material to a transition alumina comprising theta-alumina. 14. The method according to claim 1 wherein calcining is performed at a temperature between about 800° C. and about 1,400 ° C. 15. The method according to claim 14 wherein calcining is performed at a temperature between about 1,000° C. and about 1,300° C. 16. The method of making a catalyst support according to claim 1 further comprising applying at least one compound of another rare-earth metal. 17. The method according to claim 16 wherein the application of at least one compound of another rare-earth metal is performed simultaneously to step a). 18. The method according to claim 16 wherein the application of at least one compound of another rare-earth metal is performed after step c). 19. The method according to claim 18 further comprising calcining at a temperature between about 300° C. and 900° C. 20. A Fischer-Tropsch catalyst comprising at least one catalytically active metal comprising cobalt, wherein the cobalt metal is dispersed in crystallites having an average size of between about 5 nm and about 20 nm; optionally, at least one promoter; and a rare-earth metal oxide modified catalyst support including at least one alumina material comprising an alumina phase selected from the group consisting of delta-alumina, theta-alumina, and combination thereof; and optionally gamma-alumina; and a surface coverage comprising an oxide of at least one rare-earth metal, wherein said coverage coats the alumina material at least partially, and wherein the at least one rare-earth metal is trivalent. 21. The catalyst of claim 20 wherein the catalytically active metal is present in an amount between about 1% and about 50% by weight of metal to final weight of catalyst. 22. The catalyst of claim 20 wherein the promoter comprises one element from Groups 1-14 of the Periodic Table of Elements. 23. The catalyst of claim 20 wherein the promoter comprises at least one metal selected from the group consisting of platinum, palladium, silver, ruthenium, iridium, rhodium, and rhenium. 24. The catalyst of claim 20 wherein the cobalt metal is dispersed in crystallites arranged on the surface coverage comprising at least one trivalent rare-earth metal oxide. 25. The catalyst according to claim 20 wherein the trivalent rare-earth metal is selected from the group consisting of yttrium, lanthanum, praseodymium, neodymium, samarium and gadolinium. 26. The catalyst of claim 20 wherein the rare-earth metal oxide modified catalyst support further comprises a structural modifier, and said structural modifier comprises one element selected from the group consisting of boron, magnesium, silicon, calcium, titanium, chromium, manganese, iron, cobalt, nickel, copper, zinc, gallium, strontium, zirconium, molybdenum, tin, and barium. 27. The catalyst according to claim 20 wherein the catalyst is used to practice any process for converting a reactant gas mixture comprising synthesis gas under suitable conditions to a product mixture comprising linear hydrocarbons. 28. The catalyst according to claim 27 wherein the conditions suitable for converting a reactant gas mixture comprise a temperature no less than 160° C. and a pressure no less than about 5 atm. 29. The catalyst according to claim 28 further comprising no more than about 10 mol% aluminate spinels comprising the catalytically active metal before, during or after said process. 30. The catalyst according to claim 28 wherein the alumina that comprises the support retains its original phase upon exposure to said process. 31. The catalyst according to claim 28 wherein the promoter retains a majority of its original activity upon exposure to said process. 32. The catalyst of claim 20 wherein the catalyst comprises between about 5 and about 40% cobalt. 33. The catalyst according to claim 20 wherein the catalyst comprises between about 15% and about 35% by weight of cobalt to final weight of catalyst. 34. The catalyst according to claim 20 wherein the trivalent rare-earth metal is present in an amount between about 1% and about 15% by weight of metal to final weight of modified support. 35. The catalyst according to claim 20 wherein the at least one rare-earth metal is present in an amount between about 3% and about 10% by weight of metal based on the final weight of the modified support. 36. The catalyst according to claim 20 wherein the trivalent rare-earth metal is selected from the group consisting of lanthanum, praseodymium and neodymium. 37. The catalyst according to claim 20 wherein the rare-earth metal oxide modified catalyst support has a surface area between about 40 m2/g and about 150 m2/g; and a pore volume between about 0.1 cm3/g and about 0.5 cm3/g. 38. The catalyst according to claim 20 wherein the rare-earth metal oxide modified catalyst support has a surface area between about 70 m2/g and about 130 m2/g. 39. The catalyst according to claim 20 wherein the surface coverage coats the alumina material completely. 40. The catalyst according to claim 20 wherein the surface coverage has a thickness of at least about 0.2 nanometer. 41. The catalyst according to claim 20 wherein the surface coverage is between about 0.2 nm and about 0.5 nm in thickness. 42. The catalyst according to claim 20 wherein the rare-earth metal oxide modified catalyst support comprises at least 20% delta-alumina; at least 20% theta-alumina or at least 20% of combined delta-theta-alumina. 43. The catalyst according to claim 20 wherein the rare-earth metal oxide modified catalyst support comprises at least 20% theta-alumina. 44. The catalyst according to claim 20 wherein the catalyst is in the form of particles which are embedded in oil or solid hydrocarbon. 45. A method of making a Fischer-Tropsch catalyst comprising applying at least one compound of a catalytically active metal to a rare-earth metal oxide modified catalyst support to form a catalyst precursor, wherein the rare-earth metal oxide modified catalyst support includes at least one alumina material comprising an alumina phase selected from the group consisting of theta-alumina, delta-alumina, eta-alumina, rho-alumina, chi-alumina, kappa-alumina, and any combinations thereof; and optionally gamma-alumina; and a surface coverage comprising an oxide of at least one rare-earth metal, wherein said coverage coats the alumina material at least partially, and wherein the at least one rare-earth metal is trivalent; calcining said catalyst precursor; and reducing calcined catalyst precursor to form a reduced catalyst; and further embedding the reduced catalyst in oil or solid hydrocarbon. 46. The method of claim 45 wherein the trivalent rare-earth metal is selected from the group consisting of yttrium, lanthanum, praseodymium, neodymium, samarium and gadolinium. 47. The method of claim 46 wherein the rare-earth metal oxide modified catalyst support comprises between about 1 wt% and about 15 wt% of rare-earth metal. 48. The method of claim 45 wherein the rare-earth metal oxide modified catalyst support comprises an alumina phase containing essentially theta-alumina. 49. The method of claim 45 wherein applying at least one compound of a catalytically active metal is done by impregnation. 50. The method of claim 45 wherein the catalytically active metal comprises cobalt. 51. The method of claim 50 wherein the catalyst comprises between about 5 and about 40% cobalt. 52. The method of claim 50 wherein the compound of the catalytically active metal comprises cobalt nitrate, cobalt nitrate hexahydrate, cobalt acetate, cobalt acetylacetonate, or combinations thereof. 53. The method of claim 50 wherein the cobalt metal is dispersed in crystallites having an average size of between about 1 nm and about 20 nm. 54. The method of claim 50 wherein the cobalt metal is dispersed in crystallites having an average size of between about 5 nm and about 20 nm. 55. The method of claim 45 wherein the catalytically active metal comprises iron. 56. The method of claim 45 further comprising applying a compound of a promoter. 57. The method of claim 56 wherein the compounds of catalytically active metal and of the promoter are applying simultaneously by impregnation. 58. The method of claim 56 wherein the catalytically active metal is cobalt and the promoter comprises at least one metal selected from the group consisting of platinum, palladium, silver, ruthenium, iridium, rhodium, and rhenium. 59. The catalyst of claim 56 wherein the catalytically active metal is iron, and the promoter comprises at least one metal selected from the group consisting of sodium, copper, potassium, lithium, and silver. 60. A process for convening synthesis gas to hydrocarbons, wherein the process comprises converting a reactant gas mixture comprising hydrogen and carbon monoxide under conditions effective for producing a product mixture comprising waxy paraffinic hydrocarbons over a hydrocarbon synthesis catalyst comprising at least one catalytically active metal comprising cobalt, wherein the cobalt metal is dispersed in crystallites having an avenge size of between about 5 nm and about 20 nm; optionally, at least one promoter; and a rare-earth metal oxide modified catalyst support comprising an alumina material comprising optionally gamma-alumina, and at least one alumina phase selected from the group consisting of delta-alumina, theta-alumina, and combinations thereof; and a surface coverage comprising at least one rare-earth metal oxide, wherein the at least one rare-earth metal is trivalent, and wherein said coverage coats the alumina material at least partially. 61. The process according to claim 60 wherein the reactant gas mixture has a H2:CO ratio between 0.67:1 and 5:1. 62. The process according to claim 60 wherein the reactant gas mixture has a H2:CO ratio between 1.4:1 and 2.3:1. 63. The process according to claim 60 wherein the waxy paraffinic hydrocarbons comprise linear hydrocarbons having at least 18 carbon atoms. 64. The process according to claim 60 wherein the process produces a hydrocarbon mixture having an alpha value of at least 0.85. 65. The process according to claim 60 wherein the process produces methane and has a methane selectivity not more than about 10 wt %. 66. The process according to claim 60 wherein the waxy hydrocarbons contain no more than 100 ppm of catalytically active metal. 67. The process of claim 60 wherein the catalytically active metal is cobalt, and the hydrocarbon synthesis catalyst further comprises a promoter, and further wherein said promoter comprises at least one metal selected from the group consisting of platinum, palladium, silver, ruthenium, iridium, rhodium, and rhenium. 68. The process according to claim 60 wherein the rare-earth metal is selected from the group consisting of yttrium, lanthanum, praseodymium, neodymium, samarium and gadolinium. 69. The process according to claim 60 wherein the rare-earth metal oxide modified catalyst support comprises between about 1 wt % and about 15 wt % of rare-earth metal. 70. The process according to claim 60 wherein the trivalent rare-earth metal is present in an amount between about 3% and about 10% by weight of rare-earth metal to final weight of modified support. 71. The process according to claim 60 wherein the catalyst comprises between about 15% and about 35% by weight of cobalt to final weight of catalyst. 72. The process according to claim 60 wherein the rare-earth metal oxide modified catalyst support comprises at least 20% theta-alumina. 73. The process according to claim 60 wherein the rare-earth metal oxide modified catalyst support has a surface area between about 40 m2/g and about 150 m2/g; and a pore volume between about 0.1 cm3/g and about 0.5 cm3/g. 74. The process according to claim 60 wherein the catalyst further comprising no more than about 10 mol% aluminate spinels comprising the catalytically active metal before, during or after said process. 75. The process according to claim 60 wherein the catalyst is essentially free of aluminate spinels comprising the catalytically active metal before said process or during said process or both.
Eri Sigrid (Trondheim PA NOX) Goodwin ; Jr. James G. (Pittsburgh PA) Marcelin George (Pittsburgh PA) Riis Trygve (Oslo NOX), Catalyst for production of hydrocarbons.
Murrell Lawrence L. (South Plainfield NJ) Dispenziere ; Jr. Nicholas C. (Wall NJ), Catalysts comprising silica supported on a boehmite-like surface, their preparation and use.
Le Quang N. (Cherry Hill NJ) Thomson Robert T. (Voorhees NJ), Catalytic process for hydrocarbon cracking using synthetic mesoporous crystalline material.
Fraenkel Dan (71 Independence Dr. East Brunswick NJ 08816) Moselle Inez L. (245 Cristol St. Metuchen NJ 08840), Co oxidation promoter and use thereof for catalytic cracking.
Beuther Harold (Cheswick PA) Kibby Charles L. (Gibsonia PA) Kobylinski T. P. (Prospect PA) Pannell Richard B. (Allison Park PA), Fluid bed catalyst for synthesis gas conversion and utilization thereof for preparation of diesel fuel.
Williamson W. Burton (Broken Arrow OK) Linden Douglas G. (Tulsa OK) Summers ; II Jack C. (Tulsa OK), High durability and exhuast catalyst with low hydrogen sulfide emissions.
Lindquist David A. ; Rooke Sterling S., High surface area alumina and other aluminum products method of preparing by Schiff base mediated hydrolysis products made thereof.
Yamashita Hisao (Hitachi JPX) Kato Akira (Hitachi JPX) Uno Shigeo (Toukai JPX) Mizumoto Mamoru (Hitachi JPX) Matsuda Shinpei (Hitachi JPX), High temperature stable catalyst and process for preparing same.
Yamashita Hisao (Hitachi JPX) Kato Akira (Hitachi JPX) Uno Shigeo (Toukai JPX) Mizumoto Mamoru (Hitachi JPX) Matsuda Shinpei (Hitachi JPX), High temperature stable catalyst, process for preparing same, and process for conducting chemical reaction using same.
Williamson W. Burton (Broken Arrow OK) Linden Douglas G. (Tulsa OK) Summers ; II Jack C. (Tulsa OK), High-temperature three-way catalyst for treating automotive exhaust gases.
Lussier Roger Jean ; Plecha Stanislaw ; Wear Charles Cross, Hydrothermally stable high pore volume aluminum oxide/swellable clay composites and methods of their preparation and use.
Foster Alan I. (Ashford GB2) McCarroll John J. (Camberley GB2) Tennison Stephen R. (Weybridge GB2), Method for preparing a modified alumina catalyst support and a composition comprising said support and a catalyst.
Galaj Stanislas (Arcueil FRX) Besland Marie-Paule (Saintonge FRX) Wicker Alain (Paris FRX) Gillot Jacques (LaLoubere FRX) Soria Raymond (Bazet FRX), Method of making a membrane filter.
Park, Sang-Eon; Jun, Ki-Won; Roh, Hyun-Seog; Baek, Seung-Chan; Oh, Young-Sam; Baek, Young-Soon; Choi, Ri-Sang; Song, Taek-Yong, Modified θ-Al2O3-supported nickel reforming catalyst and its use for producing synthesis gas from natural gas.
Williamson W. Burton (Broken Arrow OK) Silver Ronald G. (Tulsa OK) Summers Jack C. (Newtown PA), Paladium-containing three-way automotive catalysts having unique support.
Murrel Lawrence L. (South Plainfield NJ) Dispenziere ; Jr. Nicholas C. (Wall NJ), Preparation and use of catalysts comprising a mixture of tungsten oxide and silica supported on a boehmite-like surface.
Murrell Lawrence L. (South Plainfield NJ) Dispenziere ; Jr. Nicholas C. (Wall NJ), Preparation and use of catalysts comprising a mixture of tungsten oxide and silica supported on a boehmite-like surface.
Casanave Dominique,FRX ; Galtier Pierre,FRX ; Viltard Jean-Charles,FRX, Process and apparatus for operation of a slurry bubble column with application to the fischer-tropsch synthesis.
Durand Daniel,FRX ; Mabilon Gil,FRX ; Guibard Isabelle,FRX, Process for preparing a catalyst suitable for the treatment of exhaust gases from internal combustion engines.
McLaughlin Kevin J. ; Decker Ben L. ; Chavez Mark M., Process for producing stabilized alumina having enhanced resistance to loss of surface area at high temperatures.
Tolpin Thomas W. (Highland Park IL) Kretchmer Richard A. (Clarendon Hills IL), Process for simultaneously removing nitrogen oxides, sulfur oxides, and particulates.
Mauldin Charles H. (Baton Rouge LA) Riley Kenneth L. (Baton Rouge LA), Process for the preparation of surface impregnated dispersed cobalt metal catalysts.
Eri Sigrid (Trondheim PA NOX) Goodwin ; Jr. James G. (Pittsburgh PA) Marcelin George (Pittsburgh PA) Riis Trygve (Oslo NOX), Process using a supported catalyst for hydrocarbon synthesis.
Lewis Duane J. (Ponca City OK) McNeese William H. (Aberdeen MS), Production and recovery of alumina from vapor phase hydrolysis of aluminum trialkoxides.
Pieters ; Wim J. M. ; Carlson ; Emery J. ; Gates ; William E. ; Conner ; Jr. ; William C., Pyrogenic silica or titania or alpha-alumina cuprous chloride catalyst of hydrogen chloride/oxygen reaction.
Eri Sigrid (Trondheim PA NOX) Goodwin ; Jr. James G. (Pittsburgh PA) Marcelin George (Pittsburgh PA) Riis Trygve (Oslo NOX), Supported catalyst for hydrocarbon synthesis.
Subramanian Somasundaram (Melvindale MI) Watkins William L. H. (Toledo OH) Chattha Mohinder S. (Northville MI), Three-way catalyst for treating emissions from compressed natural gas fueled engines.
Woodfield, Brian F.; Bartholomew, Calvin H.; Brunner, Kyle; Hecker, William; Ma, Xuchu; Xu, Fen; Astle, Lynn, Iron and cobalt based fischer-tropsch pre-catalysts and catalysts.
Bartholomew, Calvin H.; Woodfield, Brian F.; Huang, Baiyu; Olsen, Rebecca Elizabeth; Astle, Lynn, Method for making highly porous, stable metal oxides with a controlled pore structure.