초록 ▼

A subject for the invention is to provide an unshaped refractory composition having not only high thermal resistance but also improved corrosion resistance and improved unsusceptibility to slag infiltration. The invention is "an unshaped refractory composition comprising: (1) 20 to 70% by weight raw

A subject for the invention is to provide an unshaped refractory composition having not only high thermal resistance but also improved corrosion resistance and improved unsusceptibility to slag infiltration. The invention is "an unshaped refractory composition comprising: (1) 20 to 70% by weight raw spinel material comprising an MgO--Al2O3 spinel phase and containing 2 to 20% by weight magnesia and/or raw spinel/corundum material comprising an MgO--Al 2O3 spinel phase and a corundum phase and containing 2 to 20% by weight magnesia; (2) 3 to 12% by weight raw magnesia material having a particle diameter of 0.3 mm or smaller, containing particle sizes of 75 μm or smaller in an amount of 55 to 85% by weight, and having a magnesia purity of 90% by weight or higher; (3) 3 to 10% by weight alumina cement having a calcia content lower than 20% by weight; (4) 0.3 to 1.5% by weight ultrafine powder consisting mainly of silica; and (5) a raw alumina material as the remainder".

대표청구항 ▼

The invention claimed is: 1. An unshaped refractory composition comprising: 20 to 70% by weight of (i) raw spinel material comprising an MgO--Al2O3 spinel phase and containing from 2 to 20% by weight of magnesia based on the total weight of the raw spinel material and/or (ii) raw spinet/corundum ma

The invention claimed is: 1. An unshaped refractory composition comprising: 20 to 70% by weight of (i) raw spinel material comprising an MgO--Al2O3 spinel phase and containing from 2 to 20% by weight of magnesia based on the total weight of the raw spinel material and/or (ii) raw spinet/corundum material comprising an MgO--Al2 O3 spinel phase and a corundum phase and containing from 2 to 20% by weight of magnesia based on the total weight of the raw spinel/corundum material; 3 to 12% by weight of raw magnesia material having a particle diameter of 0.3 mm or smaller, containing particle sizes of 75 μm or smaller in an amount of from 55 to 85% by weight, and having a magnesia purity of 90% by weight or higher; 3 to 10% by weight of alumina cement having a calcia content of lower than 20% by weight; 0.3 to 1.5% by weight of ultrafine powder consisting mainly of silica; and a raw alumina material as a remainder. 2. An unshaped refractory composition comprising: 20 to 70% by weight of (i) raw spinel material comprising an MgO--Al2O3 spinel phase, containing from 2 to 20% by weight of magnesia based on the total weight of the raw spinel material, and having a particle size of 1.0 mm or larger and/or (ii) raw spinet/corundum material comprising an MgO--A2O3 spinel phase and a corundum phase, containing from 2 to 20% by weight of magnesia based on the total weight of the raw spinel/corundum material, and having a particle size of 1.0 mm or larger; 3 to 12% by weight of raw magnesia material having a particle diameter of 0.3 mm or smaller, containing particle sizes of 75 μm or smaller in an amount of from 55 to 85% by weight, and having a magnesia purity of 90% by weight or higher; 3 to 10% by weight of alumina cement having a calcia content of lower than 20% by weight; 0.3 to 1.5% by weight ultrafine powder consisting mainly of silica; and a raw alumina material as a remainder. 3. The unshaped refractory composition according to claim 1 or 2, which is for use in application by casting or application by shotcreting after having been mixed together with water.