초록

Supports for Fischer-Tropsch catalysts are formed by forming a particulate material from titania, alumina and optionally silica. A cobalt compound is incorporated into the particulate material which then is calcined to convert at least part of the alumina to cobalt aluminate.

대표청구항 ▼

What is claimed is: 1. A catalyst support composition which comprises: a major amount of titania; and at least 3 to less than 30 wt % of a binder comprising cobalt aluminate, wherein the atomic ratio of cobalt to aluminum in the composition is greater than 0.25. 2. The composition of claim 1 whe

What is claimed is: 1. A catalyst support composition which comprises: a major amount of titania; and at least 3 to less than 30 wt % of a binder comprising cobalt aluminate, wherein the atomic ratio of cobalt to aluminum in the composition is greater than 0.25. 2. The composition of claim 1 wherein said atomic ratio is about 0.5. 3. The composition of claim 1 containing about 0 wt % alumina. 4. The composition of claim 1 wherein the binder includes alumina. 5. The composition of claim 4 wherein the binder includes silica in an amount less than 50 wt % of the total amount of the binder. 6. A method for preparing a catalyst support composition comprising: spray drying a material comprising a major amount of titania and a minor amount of alumina to form spray dried product; incorporating a cobalt compound into the spray dried product to obtain a cobalt containing material, the cobalt compound being incorporated in an amount sufficient to convert, upon calcination, at least part of the alumina to cobalt aluminate; and calcining the cobalt containing material to form a binder material having at least 3 wt % to less than 30 wt % of cobalt aluminate on said catalyst support composition. 7. The method of claim 6 wherein the calcining of the spray dried product in air is at about 700째 C. to about 1000째 C. after incorporating the cobalt compound. 8. The method of claim 7 wherein the amount of cobalt compound added is sufficient to provide a Co/Al atomic ratio in the range of 0.25:1 to 2:1. 9. The method of claim 8 wherein the cobalt compound is incorporated in an amount sufficient to convert, upon calcination, substantially all the alumina to cobalt aluminate. 10. The method of claim 9 wherein the cobalt compound is cobalt nitrate. 11. The method of claim 9 wherein the cobalt containing material is calcined in air at temperature in the range of about 800째 C. to about 900째 C. 12. A Fischer-Tropsch catalyst composition comprising a catalytic metal selected from the group consisting essentially of cobalt, rhenium and mixtures thereof on a support comprising a major amount of titania and at least 3 to less than 30 wt % of a binder comprising cobalt aluminate, wherein the atomic ratio of cobalt to aluminum in the binder is greater than 0.25. 13. The catalyst of claim 12 wherein the catalytic metal is cobalt and wherein the atomic ratio of cobalt to aluminum in the binder is in the range of 0.25:1 to 2:1. 14. The catalyst of claim 13 wherein the binder includes silica in an amount less than 50 wt % of the total weight of the binder.