초록 ▼

Acidic metal-bearing wastewaters are treated to produce a finished water of sufficient purity to meet discharge standards while recovering metals removed in forms which are commercially valuable. The metals are selectively precipitated, either in a batch or in a continuous system, for removal of ind

Acidic metal-bearing wastewaters are treated to produce a finished water of sufficient purity to meet discharge standards while recovering metals removed in forms which are commercially valuable. The metals are selectively precipitated, either in a batch or in a continuous system, for removal of individual metal products in a specific sequence of steps from the wastewater. In each step, the pH is adjusted to the specific pH range and sulfide ion is introduced to precipitate the metals, excepting the removal of ferric iron and aluminum which is achieved using hydroxide precipitation. Bioconversion process using unique equipment converts sulfate in the wastewater to the hydrogen sulfide gas required for the precipitation process. This bioconversion process reduces the sulfate in the wastewater so that the water can be directly discharged or used for agricultural applications.

대표청구항 ▼

What is claimed is: 1. A method for removing at least one of metals and sulfates from acidic wastewaters, for recovering metals and for producing water suitable for discharge, comprising: (a) precipitating each metal in the wastewater in a separate stage comprising maintaining the Eh and adding an

What is claimed is: 1. A method for removing at least one of metals and sulfates from acidic wastewaters, for recovering metals and for producing water suitable for discharge, comprising: (a) precipitating each metal in the wastewater in a separate stage comprising maintaining the Eh and adding an aqueous solution of a hydroxide to maintain the pH in a range for effective formation of precipitates sequentially in the following order of removal: copper, ferric iron, zinc, aluminum, ferrous iron and manganese; (b) introducing gas containing hydrogen sulfide into the wastewater into the stages in which copper, zinc, ferrous iron and manganese are removed; (c) adding an aqueous solution of a hydroxide at a suitable concentration to precipitate ferric hydroxide and aluminum hydroxide in their appropriate order; (d) recovering the metal precipitated at each stage individually or as mixtures as a precipitate selected from the group consisting of cupric sulfide, ferric hydroxide, zinc sulfide, aluminum hydroxide, ferrous sulfide, and manganese sulfide, to produce a metal-free sulfate containing water; (e) treating the ferrous sulfide with an oxidizing agent to convert the ferrous sulfide to iron products selected from the group consisting of goethite, magnetite, hematite, lipidocrocite, and feroxyhyte; (f) treating the metal-free sulfate-containing water in a hydrogen utilizing sulfate reducing bacteria (SRB) bioreactor to convert the sulfate to hydrogen sulfide, and removing and recovering the hydrogen sulfide for re-use in the metal precipitation stages, wherein excess hydrogen sulfide is recovered. 2. The method according to claim 1 wherein the method is a batch process. 3. The method according to claim 1 wherein the method is a continuous process. 4. The method according to claim 1 wherein the oxidizing agent is a mixture of hydrogen peroxide and a stabilizer for hydrogen peroxide. 5. The method according to claim 1 wherein the bioreactor contains silica gel beads containing an encapsulated bacterial suspension that are made by a process comprising: (a) adding bacteria, sodium alginate and distilled water to a colloidal silica solution to form a mixture and maintaining the pH of the mixture between about 6 and about 7; (b) dropping the mixture into a 5% calcium chloride aqueous solution to form silica gel beads; (c) curing the silica gel beads in the mixture. 6. The method according to claim 1 wherein the bioreactor contains polyvinyl alcohol gel beads containing an encapsulated bacterial suspension that are made by a process comprising: (a) mixing polyvinyl alcohol, sodium alginate and distilled water and heating the mixtures until all material is dissolved to form a homogeneous mixture; (b) cooling the mixture and adding a bacterial suspension; (c) adding the mixture from (b) to a solution of sodium nitrate and calcium chloride to form polyvinyl alcohol sodium nitrate gel beads. 7. The method according to claim 1 wherein the cupric sulfide is precipitated at a pS of from 10 to 15 and an Eh of from-100 to-120 mV. 8. The method according to claim 1 wherein ferric hydroxide is precipitated at a pS of less than 2 with nitrogen gas sparging. 9. The method according to claim 1 wherein zinc sulfide is precipitated at a pS of from 10 to 15 and an Eh of from-100 to-120 mV. 10. The method according to claim 1 wherein ferrous sulfide is precipitated at a pS of from 5 to 8 and an Eh of from-180 to-200 mV. 11. The method according to claim 1 wherein manganese sulfide is precipitated at a pS of from 10 to 15 and an Eh of from-100 to-120 mV. 12. The method according to claim 1 wherein all metals are recovered together in step (d) as mixtures of the metals. 13. The method according to claim 1 wherein the bioreactor contains silica gel beads or polyvinyl alcohol gel beads containing alginate and an encapsulated bacterial suspension. 14. The method according to claim 1 wherein the bioreactor comprises a hollow fiber membrane. 15. A process for reducing sulfates in metal-free wastewater comprising contacting the wastewater in a membrane bioreactor comprising sulfate reducing bacteria and alginate encapsulated within polyvinyl alcohol gel beads or silica gel beads, to reduce the sulfates to hydrogen sulfide.