Method of forming a steel wire oven rack for later porcelain coating
원문보기
IPC분류정보
국가/구분
United States(US) Patent
등록
국제특허분류(IPC7판)
B23P-010/04
B23P-039/00
B23P-015/12
B23P-015/00
C10C-003/12
C10C-003/00
출원번호
US-0040641
(2005-01-21)
등록번호
US-7290320
(2007-11-06)
발명자
/ 주소
Blankenship,David James
출원인 / 주소
SSW Holding Company, Inc.
대리인 / 주소
Marshall, Gerstein & Borun LLP
인용정보
피인용 횟수 :
4인용 특허 :
18
초록▼
A wire oven rack, capable of being later-coated with porcelain, including, a plurality of elongated steel wire members joined together to form an oven rack having an outer surface. The plurality of elongated steel wire members are made from a steel rod material containing from about 80 to about 99.9
A wire oven rack, capable of being later-coated with porcelain, including, a plurality of elongated steel wire members joined together to form an oven rack having an outer surface. The plurality of elongated steel wire members are made from a steel rod material containing from about 80 to about 99.9% by weight of iron, from about 0.001 to about 0.08% by weight of carbon and from about 0.001 to about 0.2% by weight of a carbon stabilizing transition metal, preferably selected from the group consisting of Vanadium, Tantalum, Titanium and Niobium. The plurality of elongated steel wire members are preferably made from the steel rod material by drawing the steel rod material to form steel wire; wherein the diameter of the cross-sectional area of the steel rod material is reduced by at least about 20% when the steel rod material is drawn to form the steel wire, so as to prevent chipping of the glass coating material from the outer surface, when the porcelain coating is later applied, due to the release of hydrogen gas from the coated steel wire members when the steel wire is heated above 900째 F.
대표청구항▼
What is claimed is: 1. A method of making a steel wire oven rack designed to be coated with porcelain, comprising the steps of: a) providing a carbon-containing steel rod material containing from about 80 to about 99.9% by weight of iron, up to about 0.08% by weight of carbon and from about 0.001 t
What is claimed is: 1. A method of making a steel wire oven rack designed to be coated with porcelain, comprising the steps of: a) providing a carbon-containing steel rod material containing from about 80 to about 99.9% by weight of iron, up to about 0.08% by weight of carbon and from about 0.001 to about 0.2% by weight of carbon stabilizing transition metal selected from the group consisting of Vanadium, Tantalum, Titanium and Niobium; b) drawing the steel rod material to form steel wire, wherein the diameter of the cross-sectional area of the steel rod material is reduced by at least about 20%; c) forming a plurality of elongated steel wire members from said steel wire; and d) joining the plurality of steel wire members to one another to form interconnected parts of a steel wire oven rack, wherein the amount of carbon in the steel road material, the amount of carbon stabilizing transition metal in the steel rod material and the degree to which the diameter of the cross-sectional area of the steel rod material is reduced, when the steel wire is drawn from the steel rod material, are selected to prevent chipping of the later-applied glass material away from the outer surface of the article due to the release of hydrogen gas from the steel wire members when the steel wire members are heated to a temperature above 900째F. 2. The method of claim 1, wherein the steel rod is repeatedly drawn in a cold die to gradually reduce the diameter of the steel rod at least about 20%. 3. The method of claim 2, wherein the steel rod is drawn to reduce the diameter of the steel rod at least about 30%. 4. The method of claim 3, wherein the steel rod is drawn to reduce the diameter of the steel rod at least about 40%. 5. The method of claim 4, wherein the steel rod is drawn to reduce the diameter of the steel rod at least about 45%. 6. The method of claim 5, wherein the steel rod is drawn to reduce the diameter of the steel rod at least about 50%. 7. The method of claim 1, wherein the steel rod comprises 0.046% to 0.051% carbon; and 0.012% to 0.014% transition metal, and wherein the rod is reduced in diameter 31% to 53%. 8. The method of claim 7, wherein the steel wire has a diameter in the range of 0.192 inch to 0.259 inch. 9. The method of claim 1, wherein the steel rod material further includes 0.34% to 0.36% Mn; 0.003% to 0.004% P; 0.004% to 0.005% S; 0.130% to 0.140% Si; and 0.100% to 0.120% Cu, by weight. 10. The method of claim 9, wherein the steel rod material includes iron in an amount in the range of 99.329% to 99.342% by weight. 11. The method of claim 1, wherein the article is a cooking surface selected from an oven rack and a barbeque grill rack. 12. The method of claim 1, wherein the amounts of iron, carbon, and transition metal and the degree of diameter reduction of the steel rod material are selected to provide sufficient cavities in the drawn steel such that the later-applied glass coating will not chip or crack when the article is heated to a temperature above 900째 F. 13. The method of claim 1, wherein the steel rod is drawn repeatedly through a cold die to gradually reduce the rod diameter. 14. The method of claim 1, wherein the steel rod is drawn in a cold die to provide sufficient cavities in the drawn steel for receiving hydrogen emitted from the drawn steel such that the later-applied glass coating is not damaged by the emitted hydrogen when the article once coated is heated to a temperature above 900째 F. 15. A method of manufacturing a steel wire article capable of being coated with a glass material and maintaining the glass coating when used at a temperature above 900째 F. comprising: joining together a plurality of elongated steel wire members to form an oven rack having an outer surface; the plurality of elongated steel wire members being made from a carbon-containing steel rod material containing from about 80 to about 99.9% by weight of iron, up to about 0.08% by weight of carbon and from about 0.001 to about 0.2% by weight of a carbon stabilizing transition metal selected from the group consisting of Vanadium, Tantalum, Titanium and Niobium; the plurality of elongated steel wire members being made from the steel rod material by drawing the steel rod material to form steel wire; wherein the diameter of the cross-sectional area of the steel rod material is reduced by at least about 20% when the steel rod material is drawn to form the steel wire; wherein the amount of carbon in the steel road material, the amount of carbon stabilizing transition metal in the steel rod material and the degree to which the diameter of the cross-sectional area of the steel rod material is reduced, when the steel wire is drawn from the steel rod material, are selected to prevent chipping of the later-applied glass material away from the outer surface of the article due to the release of hydrogen gas from the steel wire members when the steel wire members are heated to a temperature above 900째 F.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (18)
Sarin Vinod K., Abrasion resistant coated articles.
Platkiewicz Leonard (Poznan PLX) Debski Wlodzimierz (Poznan PLX) Glowacki Jerzy (Poznan PLX), Low friction slide lining composition and a method of producing the slide lining composition.
Gardner Larry E. (Tipp City OH) Grenawalt John J. (Boardman Township ; County of Mahoning OH) Birkle Adolph John (Jackson MI), Process for producing rimmed enameling steel.
Teracher Pascal,FRX ; Porcet Jean-Pierre,FRX, Titanium-containing hot-rolled steel sheet with high strength and high drawability and its manufacturing processes.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.