초록 ▼

While steam is supplied to flow channels to heat inner cavity surfaces to a temperature equal to or higher than the heat distortion temperature of a molding resin, the resin mixed with a supercritical fluid is injected from an injection molding machine into a mold cavity. When the injection of a pre

While steam is supplied to flow channels to heat inner cavity surfaces to a temperature equal to or higher than the heat distortion temperature of a molding resin, the resin mixed with a supercritical fluid is injected from an injection molding machine into a mold cavity. When the injection of a predetermined quantity of the resin is completed, the supply of the steam to the flow channels is stopped, and cooling water starts to be supplied to the flow channels. The inner cavity surfaces are thus quickly switched from a heated state to a cooled state, cooling and solidifying the resin into a molded product of good appearance which is free of broken cell marks on its surface.

대표청구항 ▼

What is claimed is: 1. A method of manufacturing a molded product of foamed resin by injecting a molten resin into a mold and foaming the resin in the mold, comprising: injecting supercritical fluid into a molten resin; injecting the molten resin into a mold while keeping a surface of the mold at a

What is claimed is: 1. A method of manufacturing a molded product of foamed resin by injecting a molten resin into a mold and foaming the resin in the mold, comprising: injecting supercritical fluid into a molten resin; injecting the molten resin into a mold while keeping a surface of the mold at a temperature equal to or higher than a heat distortion temperature of the resin; and supplying a cooling medium in a cooling channel defined in said mold to cool and solidify the resin, wherein the supplying of the cooling medium is started less than 10 seconds after the filling of said mold with a predetermined quantity of the resin is completed, whereby as a result of the supplying of the cooling medium, a molded foamed resin product having substantially no cells formed in its surface is produced while being foamed by the supercritical fluid inside. 2. A method according to claim 1, wherein said mold is cooled substantially as the same time that the filling of said mold with a predetermined quantity of the resin is completed. 3. A method according to claim 1, wherein said mold is cooled after the filling of said mold with a predetermined quantity of the resin is completed and before a surface layer of the resin starts foaming at latest. 4. A method according to claim 1, wherein said mold is alternately heated and cooled by alternately supplying a heating medium and a cooling medium to a common flow channel defined in said mold. 5. A method according to claim 4, wherein steam is supplied as said heating medium to said flow channel in order to keep the surface of the mold at the temperature equal to or higher than the heat distortion temperature of the resin. 6. A method according to claim 5, wherein water is supplied as the cooling medium to said flow channel to cool said mold. 7. A method according to claim 1, wherein the temperature of the surface of the mold is monitored, and said resin starts to be injected into said mold when the monitored temperature of the surface of the mold is detected as being equal to or higher than said heat distortion temperature of the resin. 8. A method according to claim 1, wherein the filling of said mold with the predetermined quantity of the resin is detected as being completed by a signal from an injection molding machine which injects the resin into said mold. 9. A method according to claim 1, wherein said resin includes a base resin and a reinforcing material added thereto, and said heat distortion temperature is a heat distortion temperature of said base resin exclusive of said reinforcing material. 10. A method of manufacturing a molded product made of foamed resin, comprising: heating an inner surface of a mold at a temperature equal to or higher than a heat distortion temperature of a molten resin-to-be-used; injecting supercritical fluid into the resin in a molten state; injecting a predetermined amount of resin into the mold; discontinuing the heating of the mold, substantially simultaneously with the completion of the injecting of the resin; and after the discontinuing of the heating, continuously supplying a cooling medium in a cooling channel defined in the mold to cool and solidify a surface of the injected resin in contact with the surface of the mold, wherein the supplying of the cooling medium is started less than 10 seconds after the filling of said mold with a predetermined quantity of the resin is completed, and whereby as a result of the supplying of the cooling medium, a molded foamed product having substantially no cells formed in its surface is produced while being foamed by the supercritical fluid inside. 11. The method according to claim 10, wherein the cooling of the mold begins before the surface of the injected resin starts foaming.