초록 ▼

Carbon or activated carbon nanofibers are made from fibrillated nanofibers having a Canadian Standard Freeness of less than about 100, and/or a fiber diameter of less than or equal to about 400 nm. BET surface areas are greater than about 800 m2/g The fibrillated nanofibers can be made into a precu

Carbon or activated carbon nanofibers are made from fibrillated nanofibers having a Canadian Standard Freeness of less than about 100, and/or a fiber diameter of less than or equal to about 400 nm. BET surface areas are greater than about 800 m2/g The fibrillated nanofibers can be made into a precursor paper and subjected to heat treatment to form carbon or activated carbon nanofiber sheets. A method of making is disclosed wherein carbonization occurs at a temperature of less than about 600째 C. Activation occurs at temperatures greater than about 875째 C. in less than or equal to about 30 minutes in an oxidizing atmosphere. Single step carbonization and activation in an oxidizing atmosphere is also disclosed. The carbon nanofibers or structures made therefrom are useful as filter media providing efficient adsorption and interception of microbiological contaminants due to the microporous carbon nanofiber structure.

대표청구항 ▼

What is claimed is: 1. A sheet comprising activated, carbonized fibrillated lyocell fibers and a microbiological interception enhancing agent, wherein prior to carbonization said fibrillated lyocell fibers have a Canadian Standard Freeness of less than about 100 and a fiber diameter of less than or

What is claimed is: 1. A sheet comprising activated, carbonized fibrillated lyocell fibers and a microbiological interception enhancing agent, wherein prior to carbonization said fibrillated lyocell fibers have a Canadian Standard Freeness of less than about 100 and a fiber diameter of less than or equal to about 400 nm, said sheet carbonized at a temperature of less than about 600째 C., said microbiological interception enhancing agent comprising a biologically active metal precipitated with a counter ion of a cationic material that is adsorbed on at least a portion of said fibers to form a metal colloidal precipitate complex on a portion of a surface of at least some of said activated, carbonized fibers. 2. A sheet of claim 1 wherein said sheet is further heated to form an activated carbon sheet having a BET surface area of greater than about 800 m2/g. 3. A sheet of claim 1 wherein the fibrillated fibers have a Canadian Standard Freeness of less than about 45 or a fiber diameter of less than about 250 nm. 4. A sheet of claim 1 further including active agents captured therein. 5. A sheet of claim 4 wherein the active agents comprise metals, metal salts, metal oxides, glass, alumina, carbon, activated carbon, silicates, ceramics, zeolites, diatomaceous earth, activated bauxite, fuller's earth, calcium sulfate, titanium dioxide, magnesium hydroxide, manganese oxides, magnesia, perlite, talc, clay, bone char, pitch, calcium hydroxide, calcium salts, or combinations thereof. 6. A sheet of claim 1 wherein the fibrillated fibers are admixed with active agents, and made into a paper prior to carbonization. 7. A sheet of claim 1 wherein said sheet is used as an electrode. 8. A sheet of claim 1 further including a catalyst or a catalyst support. 9. A filter medium comprising the sheet of claim 1. 10. A sheet comprising activated, carbonized fibrillated lyocell fibers and a microbiological interception enhancing agent comprising a biologically active metal precipitated with a counter ion of a cationic material on at least a portion of said fibers to form a metal colloidal complex on a portion of a surface of at least some of said activated, carbonized fibrillated lyocell fibers, said fibrillated lyocell fibers having a BET surface area of greater than about 800 m2/g, wherein prior to carbonization and activation, the fibrillated fibers have a Canadian Standard Freeness of less than about 100 or a fiber diameter of less than or equal to about 400 nm and wherein activation occurs in less than or equal to about 30 minutes at a temperature greater than about 875째 C. in an oxidizing atmosphere. 11. A sheet of claim 10 wherein the fibrillated fibers have a Canadian Standard Freeness of less than about 45 or a fiber diameter of less than about 250 nm. 12. A sheet of claim 10 wherein the fibrillated fibers comprise polymers, liquid crystal polymers, engineered resins, cellulose, rayon, ramie, wool, silk, or combinations thereof. 13. A sheet of claim 10 further including active agents captured therein. 14. A sheet of claim 13 wherein the active agents comprise metals, metal salts, metal oxides, glass, alumina, carbon, activated carbon, silicates, ceramics, zeolites, diatomaceous earth, activated bauxite, fuller's earth, calcium sulfate, titanium dioxide, magnesium hydroxide, manganese oxides, magnesia, perlite, talc, clay, bone char, pitch, calcium hydroxide, calcium salts, or combinations thereof. 15. A sheet of claim 10 wherein the fibrillated fibers are admixed with active agents, and made into a paper prior to carbonization and activation. 16. A sheet of claim 10 further including a catalyst or a catalyst support. 17. A sheet comprising activated, carbonized fibrillated fibers having a microbiological interception enhancing agent on at least a portion of at least some of said fibrillated fibers, said microbiological interception enhancing agent comprising a biologically active metal precipitated with a counter ion of a cationic material that is adsorbed on said at least portion of said fibrillated fibers to form a metal colloidal complex on a portion of a surface of at least some of said activated, carbonized fibrillated fibers. 18. The sheet of claim 17 wherein prior to carbonization said fibrillated fibers have a Canadian Standard Freeness of less than about 100. 19. The sheet of claim 17 wherein prior to carbonization said fibrillated fibers have a Canadian Standard Freeness of less than about 45. 20. The sheet of claim 17 wherein prior to carbonization said fibrillated fibers have a fiber diameter of less than about 250 nm. 21. The sheet of claim 17 further including active agents captured therein. 22. The sheet of claim 17 further including a catalyst or a catalyst support. 23. The sheet of claim 17 wherein said cationic material is selected from the group consisting of a colloid, a charged molecule, and a linear or branched polymer having positively charged atoms along a length of said polymer chain having said counter ion associated therewith. 24. A sheet comprising activated, carbonized fibrillated lyocell fibers having a microbiological interception enhancing agent on at least a portion of at least some of said fibrillated fibers, said microbiological interception enhancing agent comprising a biologically active metal precipitated with a counter ion of a cationic material that is adsorbed on said at least portion of said fibrillated fibers to form a metal colloidal complex on a portion of a surface of at least some of said activated, carbonized fibrillated fibers. 25. The sheet of claim 24 wherein prior to carbonization said fibrillated fibers have a Canadian Standard Freeness of less than about 100. 26. The sheet of claim 24 wherein prior to carbonization said fibrillated fibers have a Canadian Standard Freeness of less than about 45. 27. The sheet of claim 24 wherein prior to carbonization said fibrillated fibers have a fiber diameter of less than about 250 nm. 28. The sheet of claim 24 further including active agents captured therein. 29. The sheet of claim 24 further including a catalyst or a catalyst support. 30. The sheet of claim 24 wherein said cationic material is selected from the group consisting of a colloid, a charged molecule, and a linear or branched polymer having positively charged atoms along a length of said polymer chain having said counter ion associated therewith.