초록 ▼

A blowing agent blend for making thermoplastic polymer foams comprises methyl formate. The blowing agent blend can further comprise at least one co-blowing agent. The co-blowing agent is either a physical co-blowing agent (e.g. an inorganic agent, a hydrocarbon, a halogenated hydrocarbon, a hydrocar

A blowing agent blend for making thermoplastic polymer foams comprises methyl formate. The blowing agent blend can further comprise at least one co-blowing agent. The co-blowing agent is either a physical co-blowing agent (e.g. an inorganic agent, a hydrocarbon, a halogenated hydrocarbon, a hydrocarbon with polar, functional group(s), water or any combination thereof), or a chemical co-blowing agent, or combinations thereof. The thermoplastic polymer foam can be an alkenyl aromatic polymer foam, e.g. a polystyrene foam. The blowing agent blend can comprise 100 mol % methyl formate, or it can comprise any combination of methyl formate and one or more co-blowing agents. The methyl formate-based blowing agent blends produce stable foams. A process for the preparation of such foams is also provided.

대표청구항 ▼

What is claimed is: 1. A process for making an alkenyl aromatic polymer foam sheet comprising: melting a thermoplastic alkenyl aromatic polymer; dissolving an effective amount of a blowing agent blend in the alkenyl aromatic polymer to define a mixture, the blowing agent blend consisting of methyl

What is claimed is: 1. A process for making an alkenyl aromatic polymer foam sheet comprising: melting a thermoplastic alkenyl aromatic polymer; dissolving an effective amount of a blowing agent blend in the alkenyl aromatic polymer to define a mixture, the blowing agent blend consisting of methyl formate and carbon dioxide, and optionally water; forming an extrudate from the mixture; and expanding the extrudate to produce the alkenyl aromatic polymer foam sheet, wherein the blowing agent blend is the sole blowing agent in the polymer. 2. The process of claim 1, wherein the blowing agent blend consists of about 80 percent methyl formate and 20 percent carbon dioxide by weight. 3. The process of claim 1, wherein the blowing agent blend includes water in an amount of about 15 percent by weight of the blowing agent blend. 4. The process of claim 1, wherein the alkenyl aromatic polymer foam sheet is dimensionally stable. 5. The process of claim 4, wherein the alkenyl aromatic polymer foam sheet has an absolute percent gauge change less than about 15 percent after aging up to 7 days. 6. The process of claim 1, wherein the alkenyl aromatic polymer foam sheet has an average cell size of about 165 to about 255 micron. 7. The process of claim 1, wherein the extrudate contains from about 1 to about 18 percent by weight of the blowing agent. 8. The process of claim 1, wherein the alkenyl aromatic polymer is polystyrene. 9. The process of claim 1, further comprising mixing a nucleating agent with the alkenyl aromatic polymer prior to the extrudate forming step. 10. The process of claim 9, wherein the nucleating agent is selected from the group consisting of clay, talc, silica, diatomaceous earth, citric acid, sodium bicarbonate, carbon dioxide, nitrogen and mixtures thereof. 11. The process of claim 9, wherein the nucleating agent is a combination of an alkali metal salt of a polycarboxylic acid with a carbonate or bicarbonate. 12. The process of claim 1, wherein the alkenyl aromatic polymer foam sheet has a density from about 2 to about 9 lb/ft3. 13. The process of claim 12, wherein the alkenyl aromatic polymer foam sheet has a density from about 6 to about 9 lb/ft3. 14. The process of claim 1, wherein the alkenyl aromatic polymer foam sheet has a thickness up to about 0.5 inch.