초록 ▼

There is provided: a production process for a water-absorbing agent having stable properties in a short time; and a water-absorbing agent. The production process comprises the step of blending an acid-group-containing water-absorbent resin powder with a noncrosslinkable water-soluble inorganic base

There is provided: a production process for a water-absorbing agent having stable properties in a short time; and a water-absorbing agent. The production process comprises the step of blending an acid-group-containing water-absorbent resin powder with a noncrosslinkable water-soluble inorganic base and/or an irreducible alkaline-metal-salt pH buffer and further with a dehydratable crosslinking agent reactable with the acid group, thereby subjecting the resin powder to crosslinking treatment, or comprises the step of blending an acid-group-containing water-absorbent resin powder with the above base and/or pH buffer and further with a crosslinking agent reactable with the acid group, thereby subjecting the resin powder to crosslinking treatment, wherein the resin powder has a weight-average particle diameter of 300 to 600 μm wherein the ratio of fine powders having particle diameters of not larger than 150 μm in the resin powder is not more than 10 weight %.

대표청구항 ▼

The invention claimed is: 1. A water-absorbing agent, which is a particulate water-absorbing agent of which the major proportion is comprised of a water-absorbent resin that is obtained by a process including the step of polymerizing an unsaturated monomer component and has a crosslinked structure,

The invention claimed is: 1. A water-absorbing agent, which is a particulate water-absorbing agent of which the major proportion is comprised of a water-absorbent resin that is obtained by a process including the step of polymerizing an unsaturated monomer component and has a crosslinked structure, where the particulate water-absorbing agent includes particles having particle diameters of smaller than 850 μm but not smaller than 150 μm in an amount of not less than 90 weight % of all particles of the particulate water-absorbing agent; and where the particles include at least two members selected from the group consisting of: particles (A1) having particle diameters of smaller than 850 μm but not smaller than 600 μm; particles (A2) having particle diameters of smaller than 600 μm but not smaller than 500 μm; particles (A3) having particle diameters of smaller than 500 μm but not smaller than 300 μm; and particles (A4) having particle diameters of smaller than 300 μm but not smaller than 150 μm; and where the water-absorbing agent further has the following properties: a 30-minute absorption capacity of not less than 31 g/g without load for a 0.90 weight % physiological saline (CRC); a 60-minute absorption capacity of not less than 24 g/g under a load of 4.83 kPa for a 0.90 weight % physiological saline (AAP); a saline flow conductivity of not less than 20 (unit: 10-7횞cm3횞s횞g-1) for a 0.69 weight % physiological saline (SFC); and an SFC variation index of 0 to 25% wherein the SFC variation index is defined by the following equation (1): description="In-line Formulae" end="lead"SFC variation index (%)=[(standard deviation of SFCs of particles A1 to A4)/(SFC of entire particulate water-absorbing agent)]횞100 (1).description="In-line Formulae" end="tail" 2. A water-absorbing agent according to claim 1, wherein said water-absorbing agent comprises particles A1, A2, A3 and A4, each being present in an amount of not less than 0.1 weight % respectively. 3. A water-absorbing agent according to claim 1, which has an SFC variation coefficient of 0 to 0.25, wherein the SFC variation coefficient is defined by the following equation (2): description="In-line Formulae" end="lead"SFC variation coefficient=(standard deviation of SFCs of particles A1 to A4)/(average of SFCs of particles A1 to A4) (2).description="In-line Formulae" end="tail" 4. A water-absorbing agent according to claim 1, which has an SFC variation rate of 0.65 to 1.00, wherein the SFC variation rate is defined by the following equation (3): description="In-line Formulae" end="lead"SFC variation rate=(minimum SFC among SFCs of particles A1 to A4)/(maximum SFC among SFCs of particles A1 to A4) (3).description="In-line Formulae" end="tail" 5. A water-absorbing agent according to claim 1, which further comprises a cationic polymer compound and/or a water-insoluble fine particle. 6. A water-absorbing agent, which is a particulate water-absorbing agent of which the major proportion is comprised of a water-absorbent resin that is obtained by a process including the step of polymerizing an unsaturated monomer component and has a crosslinked structure, where the particulate water-absorbing agent includes particles having particle diameters of smaller than 850 μm but not smaller than 150 μm in an amount of not less than 90 weight % of all particles of the particulate water-absorbing agent; and where the particles include at least two members selected from the group consisting of: particles (A1) having smaller than 850 μm but not smaller than 600 μm; particles (A2) having particle diameters of smaller than 600 μm but not smaller than 500 μm; particles (A3) having particle diameters of smaller than 500 μm but not smaller than 300 μm; and particles (A4) having particle diameters of smaller than 300 μm but not smaller than 150 μm; and where said water-absorbing agent further has the following properties: a 30-minute absorption capacity of not less than 31 g/g without load for a 0.90 weight % physiological saline (CRC); a 60-minute absorption capacity of not less than 24 g/g under a load of 4.83 kPa for a 0.90 weight % physiological saline (AAP); a saline flow conductivity of not less than 20 (unit: 10-7횞cm3횞s횞g-1) for a 0.69 weight % physiological saline (SFC); and an SFC variation coefficient of 0 to 0.25, wherein the SFC variation coefficient is defined by the following equation (2): description="In-line Formulae" end="lead"SFC variation coefficient=(standard deviation of SFCs of particles A1 to A4)/(average of SFCs of particles A1 to A4) (2).description="In-line Formulae" end="tail" 7. A continuously produced water-absorbing agent, which is a particulate water-absorbing agent of which the major proportion is comprised of a water-absorbent resin that is obtained by a process including the step of polymerizing an unsaturated monomer component and has a crosslinked structure, where the particulate water-absorbing agent includes particles having particle diameters of smaller than 850 μm but not smaller than 150 μm in an amount of not less than 90 weight % of all particles of the particulate water-absorbing agent; and where the particles include at least two members selected from the group consisting of: particles (A1) having particle diameters of smaller than 850 μm but not smaller than 600 μm; particles (A2) having particle diameters of smaller than 600 μm but not smaller than 500 μm; particles (A3) having particle diameters of smaller than 500 μm but not smaller than 300 μm; and particles (A4) having particle diameters of smaller than 300 μm but not smaller than 150 μm; and where the water-absorbing agent further has the following properties: a 30-minute absorption capacity of not less than 31 g/g without load for a 0.90 weight % physiological saline (CRC); a 60-minute absorption capacity of not less than 24 g/g under a load of 4.83 kPa for a 0.90 weight % physiological saline (AAP); a saline flow conductivity of not less than 20 (unit: 10-7횞cm3횞s횞g-1) for a 0.69 weight % physiological saline (SEC); and an SFC standard deviation of not more than 5.0 in a continuous production system, wherein the SFC standard deviation in a continuous production system is defined by the following equation (4): description="In-line Formulae" end="lead"SFC standard deviation in a continuous production system=standard deviation of SEC of each lot (4)description="In-line Formulae" end="tail" where: the CRC, AAP, and SEC are on average of the lots; each lot has a weight of not less than 20 kg; and the number of the lots is not smaller than 10. 8. A water-absorbing agent, which is a particulate water-absorbing agent obtained by a process including the steps of: polymerizing a monomer including an acid-group-containing monomer (salt); and then post-neutralizing the resultant polymer; and then surface-crosslinking the resultant water-absorbent resin, where the particulate water-absorbing agent or the water-absorbent resin has a neutralization index of not less than 15 and exhibits a 60 minutes' absorption capacity of not less than 20 g/g under a load of 4.83 kPa for a 0.90 weight % physiological saline (AAP) after the surface-crosslinking. 9. A water-absorbing agent, which is obtained by a production process comprising the step of blending a water-absorbent resin powder (a) with a noncrosslinkable water-soluble inorganic base (b1) and/or an irreducible alkaline-metal-salt pH buffer (b2) and further with a dehydratable crosslinking agent (c1), thereby subjecting the water-absorbent resin powder (a) to crosslinking treatment, wherein the water-absorbent resin powder (a) contains an acid group, and wherein the dehydratable crosslinking agent (c1) is reactable with the acid group. 10. A sanitary material, which comprises the water-absorbing agent as recited in claim 1. 11. A sanitary material, which comprises the water-absorbing agent as recited in claim 6. 12. A sanitary material, which comprises the water-absorbing agent as recited in claim 7. 13. A sanitary material, which comprises the water-absorbing agent as recited in claim 8. 14. A sanitary material, which comprises the water-absorbing agent as recited in claim 9. 15. A water-absorbing agent according to claim 9, wherein the water-soluble inorganic base (b1) is at least one member selected from the group consisting of alkaline metal salts, ammonium salts, alkaline metal hydroxides, and ammonia or its hydroxide. 16. A water-absorbing agent according to claim 9, wherein the pH buffer (b2) is an inorganic salt comprised of a weak acid and a strong base. 17. A water-absorbing agent according to claim 9, wherein the pH buffer (b2) is a partially alkaline-metal-neutralized salt of a polybasic acid. 18. A water-absorbing agent according to claim 9, wherein the dehydratable crosslinking agent (c1) is a polyhydric alcohol compound.