초록 ▼

A method of making an article that is comprised of a metal foam in contact with a base metal by an intermediate braze composition, in particular, a method of brazing a metal foam to a base metal via a braze composition. In one preferred method, a polymeric foam is coated with a powdered metal compos

A method of making an article that is comprised of a metal foam in contact with a base metal by an intermediate braze composition, in particular, a method of brazing a metal foam to a base metal via a braze composition. In one preferred method, a polymeric foam is coated with a powdered metal composition and thermally-treated to volatilize the polymeric foam and form an open-cell metal foam. A second polymeric foam is coated with a braze composition. The second coated polymeric foam is thermally-treated to volatilize the polymeric foam. The metal foam is surrounded by the second coated polymeric foam to form a composite metal foam. The composite metal foam is placed in contact with a base metal to form an article. The article is thermally-treated to a brazing temperature to form a brazed metal article.

대표청구항 ▼

What is claimed is: 1. A method of making a brazed metal article, the method comprising: providing a first polymeric foam; coating the first polymeric foam with a powdered metal composition to form a coated first polymeric foam; thermally-treating the coated first polymeric foam to volatilize the f

What is claimed is: 1. A method of making a brazed metal article, the method comprising: providing a first polymeric foam; coating the first polymeric foam with a powdered metal composition to form a coated first polymeric foam; thermally-treating the coated first polymeric foam to volatilize the first polymeric foam and to form an open-cell metal foam; providing a second polymeric foam; coating the second polymeric foam with a braze composition to form a coated second polymeric foam; thermally-treating the coated second polymeric foam to an intermediate temperature to volatilize the second polymeric foam and to form a thermally-treated metal foam; applying the thermally-treated metal foam to the open-cell metal foam to form a thermally-treated metal foam composite; placing the thermally-treated metal foam composite in contact with a base metal to form an article; and thermally-treating the article to a braze temperature to partially-liquefy or fully-liquefy the applied thermally-treated metal foam of the thermally-treated metal foam composite to form a brazed metal article. 2. The method as claimed in claim 1, wherein the first polymeric foam is selected from a group consisting of polyurethane, polyester, polyether, cellulose and any other reticulated (open-cell) organic foam. 3. The method as claimed in claim 2, wherein the first polymeric foam is polyurethane. 4. The method as claimed in claim 1, wherein the first polymeric foam has from about 3 to about 130 pores per inch. 5. The method as claimed in claim 1, wherein the second polymeric foam is selected from a group consisting of polyurethane, polyester, polyether, cellulose and any other reticulated (open-cell) organic foam. 6. The method as claimed in claim 5, wherein the second polymeric foam is polyurethane. 7. The method as claimed in claim 1, wherein the second polymeric foam has from about 3 to about 130 pores per inch. 8. The method as claimed in claim 1, wherein the first polymeric foam and the second polymeric foam are polyurethane. 9. The method as claimed in claim 1, wherein the second polymeric foam has a greater number of pores per inch than the first polymeric foam. 10. The method as claimed in claim 1, wherein the second polymeric foam has at least twice the number of pores per inch as the number of pores per inch of the first polymeric foam. 11. The method as claimed in claim 1, wherein the braze composition comprises a braze metal. 12. The method as claimed in claim 11, wherein the braze metal is selected from the group consisting of BNi-3, BNi-4, BNi-6, BCo-1, BAg-8, BAg-8a, BVAg-29, and Ag. 13. The method as claimed in claim 1, wherein the base metal is solid, slightly porous, or porous. 14. The method as claimed in claim 1, wherein the brazed metal article is a metal tube.