초록 ▼

An electrochromic material having improved durability and more pleasing color characteristics is composed of a single-phase compound of formula W1-xTaxO3-x/2, x having a value in a range of from about 0.15 to about 0.5. Thin films of the electrochromic material can be manufactured by pulse laser dep

An electrochromic material having improved durability and more pleasing color characteristics is composed of a single-phase compound of formula W1-xTaxO3-x/2, x having a value in a range of from about 0.15 to about 0.5. Thin films of the electrochromic material can be manufactured by pulse laser deposition (PLD). Thin films of the electrochromic material are useful in the fabrication of electrochromic devices, such as "smart" windows, mirrors, information displays and variable emittance surfaces.

대표청구항 ▼

The invention claimed is: 1. A film comprising an electrochromic material comprising a single-phase electrochromic compound of formula W1-xTaxO3-x/2, x having value in a range of from 0.15 to 0.5. 2. The film of claim 1 having a durability at least 5 times greater than a film of WO3 in a proton-b

The invention claimed is: 1. A film comprising an electrochromic material comprising a single-phase electrochromic compound of formula W1-xTaxO3-x/2, x having value in a range of from 0.15 to 0.5. 2. The film of claim 1 having a durability at least 5 times greater than a film of WO3 in a proton-based electrolyte. 3. The film of claim 1 having a durability at least 10 times greater than a film of WO3 in a proton-based electrolyte. 4. The film of claim 1 having a thickness in a range of from 200 nm to 6000 nm. 5. The film of claim 1 having a thickness in a range of from 300 nm to 4000 nm. 6. The film of claim 1, wherein the compound has a cubic crystal structure. 7. An electrochromic device comprising an ion storage layer, an ion conducting layer and an electrochromic layer between first and second transparent conductor layers, the electrochromic layer comprising a film of claim 1. 8. The electrochromic device of claim 7, further comprising one or more transparent substrate layers. 9. The electrochromic device of claim 8, wherein x has a value in a range of from 0.2 to 0.5. 10. The electrochromic device of claim 9, wherein the film of electrochromic material has a durability at least 5 times greater than a film of WO3 in a proton-based electrolyte. 11. The electrochromic device of claim 10, wherein the film has a thickness in a range of from 200 nm to 6000 nm. 12. The electrochromic device of claim 8, wherein the compound has a cubic crystal structure. 13. The film of claim 1, wherein x has a value in a range of from 0.2 to 0.5. 14. The film of claim 1, wherein x has a value in a range of from 0.25 to 0.35. 15. The film of claim 14, wherein the compound has a cubic crystal structure. 16. An electrochromic device comprising a nickel oxide ion storage layer, a proton-based liquid/polymer gel type ion conducting layer and an electrochromic layer between first and second transparent indium-tin oxide conducting layers, the first and second transparent indium-tin oxide conducting layers supported on first and second transparent substrates, the electrochromic layer comprising a film of an electrochromic material, the film having a thickness in a range of from 300 nm to 4000 nm, the electrochromic material comprising a single-phase compound of formula W1-xTaxO3-x/2 having a cubic crystal structure, x having a value in a range of from 0.2 to 0.5 17. The electrochromic device of claim 16, wherein the electrochromic layer has a durability at least 5 times greater than a film of WO3 in a proton-based electrolyte. 18. The electrochromic device of claim 16, wherein the electrochromic layer has a durability at least 10 times greater than a film of WO3 in a proton-based electrolyte. 19. The electrochromic device of claim 16, wherein the electrochromic layer has a colored state having a neutral color pleasing to a human eye.