초록 ▼

A wind blade spar cap for strengthening a wind blade including an integral, unitary three-dimensional woven material having a first end and a second end, corresponding to a root end of the blade and a tip end of the blade, wherein the material tapers in width from the first to the second end while m

A wind blade spar cap for strengthening a wind blade including an integral, unitary three-dimensional woven material having a first end and a second end, corresponding to a root end of the blade and a tip end of the blade, wherein the material tapers in width from the first to the second end while maintaining a constant thickness and decreasing weight therebetween, the cap being capable of being affixed to the blade for providing increased strength with controlled variation in weight from the root end to the tip end based upon the tapered width of the material thereof. The present inventions also include the method of making the wind blade spar cap and a wind blade including the wind blade spar cap.

대표청구항 ▼

What is claimed is: 1. A wind blade spar cap for strengthening a wind blade comprising: an integral, unitary three-dimensional woven material having a first end and a second end, corresponding to a root end of the blade and a tip end of the blade, wherein the material tapers in width from the first

What is claimed is: 1. A wind blade spar cap for strengthening a wind blade comprising: an integral, unitary three-dimensional woven material having a first end and a second end, corresponding to a root end of the blade and a tip end of the blade, wherein the material tapers in width from the first to the second end while maintaining a constant thickness and decreasing weight therebetween, the cap being capable of being affixed to the blade for providing increased strength with controlled variation in weight from the root end to the tip end based upon the tapered width of the material thereof. 2. The spar cap of claim 1, wherein the material comprises carbon fibers. 3. The spar cap of claim 1, wherein the material comprises E-glass filaments. 4. The spar cap of claim 1, wherein the material is a hybrid of carbon and E-glass filaments. 5. The spar cap of claim 1, wherein the material is resin-infused. 6. The spar cap of claim 1, wherein the 3-D woven structure includes 3-D orthogonal yarn systems. 7. The spar cap of claim 1, wherein the cap is affixed to the blade by infusion. 8. The spar cap of claim 1, wherein the material substantially comprises warp yarns in the spar cap length direction. 9. A method of making a wind blade spar cap comprising the steps of: providing a plurality of yarn systems for supplying input to a weaving machine; introducing the yarn to the machine for manipulation in each of x-, y-, and z-directions, where the directions produce intersecting points; forming an integral, unitary three-dimensional woven material having a predetermined, controlled and constant thickness from the yarn where the x-and y-direction yarns are disposed to each other without interlacing, and where the z-direction yarns are manipulated to secure the x-and y-direction yarns in respective planes; cutting the material to form a tapered spar cap section; applying the tapered section to a wind blade spar such that the taper direction of the section decreases from a root end of the blade to a tip end of the blade. 10. The method of claim 9, further including the step of introducing a resin to the section during application to the blade. 11. The method of claim 9, wherein the step of cutting the material to form a tapered spar cap section is performed by cutting the material into two identical pieces. 12. The method of claim 11, wherein the step of applying one identical piece of the tapered section to the spar further comprises the step of applying the other identical piece of the tapered section such that the taper direction of the section decreases from a root end of the blade to a tip end of the blade. 13. A wind blade comprising: a spar cap further comprising an integral, unitary three-dimensional woven material having a first end and a second end, corresponding to a root end of the blade and a tip end of the blade, wherein the material tapers in width from the first to the second end while maintaining a constant thickness and decreasing weight therebetween, the cap being capable of being affixed to the blade for providing increased strength with controlled variation in weight from the root end to the tip end based upon the tapered width of the material thereof. 14. The spar cap of claim 13, wherein the cap is affixed to the blade by infusion. 15. The spar cap of claim 13, wherein the material substantially comprises warp yarns in the spar cap length direction.