초록 ▼

A preform and method for forming preforms and structural members are provided. The preform can be formed by cold spraying a structural material onto a base member, such that the preform has dimensions approximating the dimensions of the machined structural member to thereby reduce material waste and

A preform and method for forming preforms and structural members are provided. The preform can be formed by cold spraying a structural material onto a base member, such that the preform has dimensions approximating the dimensions of the machined structural member to thereby reduce material waste and machining time when forming the structural member from the preform. In addition, the preforms can be plastically deformed to more closely correspond with the desired dimensions of the structural member. Further, hydrogen can be provided in a mixed stream of gas and structural material for spraying, and the resulting structural member can be subjected to a sub-atmospheric pressure to release hydrogen therefrom.

대표청구항 ▼

That which is claimed: 1. A method of forming a structural member having predetermined dimensions, the method comprising: introducing particles of a structural material into a gas comprising hydrogen; mixing the gas and particles to form a mixed stream having a temperature less than a melting tempe

That which is claimed: 1. A method of forming a structural member having predetermined dimensions, the method comprising: introducing particles of a structural material into a gas comprising hydrogen; mixing the gas and particles to form a mixed stream having a temperature less than a melting temperature of the structural material; directing the mixed stream of the gas and particles toward a base member such that the structural material is deposited on the base member, thereby forming a structural member; and subjecting the structural member to a sub-atmospheric pressure, thereby releasing hydrogen from the structural material of the structural member. 2. A method according to claim 1 further comprising providing the particles of the structural material, the particles being between about 1 and 50 microns in diameter. 3. A method according to claim 1 further comprising heating the particles to a temperature less than the melting temperature of the structural material. 4. A method according to claim 1 further comprising providing the particles of the structural material, the particles comprising titanium. 5. A method according to claim 1 further comprising providing the base member and the particles of the structural material, each of the base member and the particles of the structural material comprising titanium. 6. A method according to claim 1 further comprising providing the gas, the gas comprising at least about 99% hydrogen by weight. 7. A method according to claim 1 wherein said mixing step comprises accelerating the gas and particles to a supersonic speed. 8. A method according to claim 1 wherein said step of subjecting the structural member to a sub-atmospheric pressure comprises subjecting the structural member to a pressure less than about 0.0001 torr. 9. A method according to claim 1 wherein said step of subjecting the structural member to a sub-atmospheric pressure comprises subjecting the structural member to the sub-atmospheric pressure for at least about 60 minutes. 10. A method according to claim 1 further comprising heating the structural member in conjunction with said step of subjecting the structural member to a sub-atmospheric pressure. 11. A method according to claim 1 further comprising removing the structural material from the base member. 12. A method according to claim 1 further comprising forging the structural member and thereby shaping the structural member to the predetermined dimensions. 13. A method according to claim 1 further comprising machining the structural member to the predetermined dimensions. 14. A method according to claim 1, further comprising: prior to said directing step, determining desired dimensions of the structural member and providing the base member according to the determined dimensions of the structural member; and subsequent to said directing step, plastically deforming at least the base member and machining the structural member to remove excess material to thereby form the structural member having the predetermined desired dimensions, wherein said subjecting step comprises heating the structural member.