초록 ▼

An object of the present invention is to provide: a water-absorbent resin which can sufficiently overcome the problem of the gel blocking, can manifest sufficient absorption capacity without load and sufficient absorption capacity under load and, at the same time, can also exert excellent liquid per

An object of the present invention is to provide: a water-absorbent resin which can sufficiently overcome the problem of the gel blocking, can manifest sufficient absorption capacity without load and sufficient absorption capacity under load and, at the same time, can also exert excellent liquid permeability under load; and a process for producing the same. As a means of achieving this object, a first production process among the processes according to the present invention for producing a water-absorbent resin having a treated surface is a process comprising: a step of mixing a water-absorbent resin having an internal crosslinked structure obtained by polymerizing a monomer containing acrylic acid and/or a salt thereof as a main component, a complex containing a polyvalent metal atom as a central atom and an organic secondary crosslinking agent in the presence of an aqueous liquid; and a step of crosslinking a surface of the water-absorbent resin with the organic secondary crosslinking agent. And a second production process is a process comprising a step of mixing a water-absorbent resin having an internal crosslinked structure and a crosslinked surface obtained by polymerizing a monomer containing acrylic acid and/or a salt thereof as a main component, and a complex containing a polyvalent metal atom as a central atom in the presence of an aqueous liquid.

대표청구항 ▼

What is claimed is: 1. A water-absorbent resin having a treated surface, wherein a trivalent or tetravalent polyvalent metal atom is present on a surface of a water-absorbent resin having an internal crosslinked structure and a crosslinked surface obtained by polymerizing a monomer containing acryl

What is claimed is: 1. A water-absorbent resin having a treated surface, wherein a trivalent or tetravalent polyvalent metal atom is present on a surface of a water-absorbent resin having an internal crosslinked structure and a crosslinked surface obtained by polymerizing a monomer containing acrylic acid and/or a salt thereof as a main component, wherein the extraction ratio of the polyvalent metal atom is 80% by mass or smaller. 2. The water-absorbent resin having a treated surface according to claim 1, wherein the polyvalent metal atom is at least one kind of metal atom selected from the group consisting of Ti, Zr, and Hf. 3. The water-absorbent resin having a treated surface according to claim 1, wherein the saline flow conductivity (SFC) is 30 to 2000 (��10-7 cm3��s/g). 4. The water-absorbent resin having a treated surface according to claim 1, wherein the polyvalent metal atom/carbon ratio, as determined from surface polyvalent metal concentration measurement by Ar ion sputtering and ESCA, is at the maximum value in a sputtering time of within 203 seconds. 5. The water-absorbent resin having a treated surface according to claim 1, which has a mass-average particle size of 100 to 600 μm. 6. The water-absorbent resin having a treated surface according to claim 1, which is surface-crosslinked by a surface-crosslinking agent including polyhydric alcohol compounds. 7. The water-absorbent resin having a treated surface according to claim 1, which is obtained by surface-crosslinking of the water-absorbent resin having an amount of an agglomerate of a fine powder of 5% by mass or larger. 8. The water-absorbent resin having a treated surface according to claim 1, wherein the polyvalent metal atom is derived from a water-soluble complex containing a polyvalent metal. 9. The water-absorbent resin having a treated surface according to claim 1, which has an absorption capacity without load (CRC) of 25 g/g or larger and a saline flow conductivity (SFC) of 80 to 2000 (��10-7 cm3��s/g). 10. The water-absorbent resin having a treated surface according to claim 1, which contains a polyvalent metal atom which is not extracted by the extraction operation in an amount of 0.002 to 1% by mass.