초록 ▼

A hermetically sealed glass package and method for manufacturing the hermetically sealed glass package are described herein using an OLED display as an example. Basically, the hermetically sealed OLED display is manufactured by providing a first substrate plate and a second substrate plate and depos

A hermetically sealed glass package and method for manufacturing the hermetically sealed glass package are described herein using an OLED display as an example. Basically, the hermetically sealed OLED display is manufactured by providing a first substrate plate and a second substrate plate and depositing a frit onto the second substrate plate. OLEDs are deposited on the first substrate plate. An irradiation source (e.g., laser, infrared light) is then used to heat the frit which melts and forms a hermetic seal that connects the first substrate plate to the second substrate plate and also protects the OLEDs. The frit is glass that was doped with at least one transition metal and possibly a CTE lowering filler such that when the irradiation source heats the frit, it softens and forms a bond. This enables the frit to melt and form the hermetic seal while avoiding thermal damage to the OLEDs.

대표청구항 ▼

What is claimed is: 1. A method for manufacturing an organic light emitting diode device, said method comprising the steps of: providing a first glass plate; providing a second glass plate; positioning a frit made from glass doped with at least one transition metal and a coefficient of thermal expa

What is claimed is: 1. A method for manufacturing an organic light emitting diode device, said method comprising the steps of: providing a first glass plate; providing a second glass plate; positioning a frit made from glass doped with at least one transition metal and a coefficient of thermal expansion (CTE) lowering filler between said first and second glass plates, said filler comprising no more than about 30% of said frit and wherein a mean particle size of said frit is less than or equal to about 20 μm; positioning an organic light emitting diode between said first and second glass plates; and heating said frit with a laser in a manner that would cause said frit to soften and form a hermetic seal between said first and second glass plates, thereby hermetically sealing said organic light emitting diode between said which first and second glass plates. 2. The method of claim 1, further comprising the step of placing an adhesive within a gap located between outer edges of said first and second glass plates, wherein said gap is caused by the presence of the hermetic seal. 3. The method of claim 1, wherein a Tg of said frit is less than about 350�� C. 4. The method of claim 1, wherein said CTE lowering filler is an additive filler including lithium alumino-silicate compounds. 5. The method of claim 1, wherein said frit comprises vanadium or neodymium. 6. The method of claim 1, wherein said frit excluding said CTE lowering filler has the following composition: K2O (0-10 mole %) Fe2O3 (0-20 mole %) Sb2O3 (0-40 mole %) P2O5 (20-40 mole %) V2O5 (30-60 mole %) TiO2 (0-20 mole %) Al2O3 (0-5 mole %) B2O3 (0-5 mole %) WO3 (0-5 mole %) Bi2O3 (0-5 mole %). 7. The method of claim 1, wherein said frit excluding said CTE lowering filler has the following composition: K2O (0-10 mole %) Fe2O3 (0-20 mole %) Sb2O3 (0-20 mole %) ZnO (0-20 mole %) P2O5 (20-40 mole %) V2O5 (30-60 mole %) TiO2 (0-20 mole %) Al2O3 (0-5 mole %) B2O3 (0-5 mole %) WO3 (0-5 mole %) Bi2O3(0-5 mole %). 8. The method of claim 1, wherein said frit is selected from the group of glasses consisting of a titano-vanadium-phosphate glass, a vanadate-iron-phosphate glass, a zinc-vanadium-phosphate glass, a Sn--Zn-phosphate glass, a mixed alkali zinc-phosphate glass, a vanadium-phosphate glass, a Pb-borate glass, and a mixed alkali zinc-phosphate glass with vanadium and lead. 9. A method for manufacturing an organic light emitting diode device, said method comprising the steps of: providing a first substrate plate; providing a second substrate plate; positioning a frit made from lead-free glass comprising vanadium and a coefficient of thermal expansion (CTE) lowering filler between said first and second substrate plates, said frit having a Tg less than about 350�� C.; and positioning an organic light emitting diode between said first and second substrate plates; and heating said frit with a laser in a manner that would cause said frit to melt and bond to said first and second substrate plates, thereby forming a hermetic seal between said first and second substrate plates, and wherein a temperature of said organic light emitting diode does not exceed about 100�� C. during said heating. 10. The method of claim 9, wherein said CTE lowering filler is an inversion filler or an additive filler. 11. The method according to claim 1, wherein a mean particle size of said frit is between about 15 μm and 20 μm. 12. The method of claim 1, wherein a mean particle size of said frit is between about 5 μm and about 10 μm. 13. The method of claim 1, wherein said frit was deposited by screen printing. 14. The method of claim 1, wherein a maximum temperature of said organic light emitting diode during said heating is less than about 100�� C. 15. The method of claim 1 wherein a maximum temperature of said organic light emitting diode during said heating is less than about 80�� C. 16. The method of claim 1 wherein said frit is lead free. 17. The method of claim 1 wherein said filler comprises between about 20% and about 30% of said frit: 18. The method of claim 9 wherein a thickness variation of said frit prior to said heating is less than about 10 μm. 19. The method of claim 9 wherein a thickness variation of said frit prior to said heating is less than about 5 μm. 20. The method of claim 9 wherein a mean particle size of said frit is less than or equal to about 20 μm. 21. The method of claim 9 wherein a mean particle size of said frit is between about 15 μm and about 20 μm. 22. The method of claim 9 wherein a mean particle size of said frit is between about 5 μm and 10 μm. 23. A method for manufacturing a hermetically sealed glass package, said method comprising the steps of: providing a first glass plate; providing a second glass plate; positioning a frit made from glass doped with at least one transition metal and a coefficient of thermal expansion (CTE) lowering filler between said first glass plate and said second glass plate, said filler comprising no more than about 30% of said fit and wherein a mean particle size of said frit is less than or equal to about 20 μm; positioning a temperature sensitive material between said first and second glass plates; and heating said frit with a laser in a manner that would cause said frit to soften and form a hermetic seal between said first and second glass plates, thereby hermetically sealing said temperature sensitive material between said first and second glass plates and wherein a temperature of said temperature sensitive material does not exceed about 100�� C. during said heating. 24. The method of claim 23 wherein said temperature sensitive material is an organic material.