Method for making product from fiber glass waste
원문보기
IPC분류정보
국가/구분
United States(US) Patent
등록
국제특허분류(IPC7판)
D01F-013/00
C03B-019/09
C03B-019/00
C04B-035/00
출원번호
US-0725171
(2003-12-01)
등록번호
US-7416690
(2008-08-26)
발명자
/ 주소
Haun,Michael J.
출원인 / 주소
Haun,Michael J.
인용정보
피인용 횟수 :
2인용 특허 :
16
초록▼
The invention provides a method to transform large quantities of fiber glass waste into useful ceramic products by a low-cost manufacturing process. The method consists of reducing the fiber glass waste into a glass powder; mixing the glass powder with additives into a glass-additives mixture; granu
The invention provides a method to transform large quantities of fiber glass waste into useful ceramic products by a low-cost manufacturing process. The method consists of reducing the fiber glass waste into a glass powder; mixing the glass powder with additives into a glass-additives mixture; granulating the glass-additives mixture into granulated particles; forming the granulated particles into a green ceramic article; and heating the green ceramic article into the ceramic product. Water and clay can be included in the processing. Only one firing step is needed with a low peak firing temperature of about 700�� C. to about 1000�� C. The method conserves energy and natural resources compared to clay-based traditional ceramic manufacturing. High-quality impervious ceramic products can be produced by the invention.
대표청구항▼
What is claimed is: 1. A method for making a ceramic product from fiber glass waste, comprising: heating the fiber glass waste; reducing the heated fiber glass waste into a glass powder; mixing the glass powder with additives into a glass-additives mixture; granulating the glass-additives mixture i
What is claimed is: 1. A method for making a ceramic product from fiber glass waste, comprising: heating the fiber glass waste; reducing the heated fiber glass waste into a glass powder; mixing the glass powder with additives into a glass-additives mixture; granulating the glass-additives mixture into granulated particles; forming the granulated particles into a green ceramic article; and heating the green ceramic article into the ceramic product. 2. The method according to claim 1, wherein the heating of the fiber glass waste comprises heating to remove water, burn out organic matter, and/or increase the friability of the fiber glass waste. 3. The method according to claim 1, wherein the reducing of the fiber glass waste into the glass powder comprises reducing the fiber glass waste to pieces with fiber lengths less than about 0.6 mm. 4. The method according to claim 1, wherein the reducing of the fiber glass waste into the glass powder comprises reducing the fiber glass waste with a liquid added. 5. The method according to claim 1, wherein the reducing of the fiber glass waste into the glass powder comprises reducing the fiber glass waste with water added. 6. The method according to claim 1, wherein the reducing of the fiber glass waste into the glass powder comprises reducing the fiber glass waste without a liquid added. 7. The method according to claim 1, wherein 70-100 weight percent of the glass-additives mixture is comprised of the waste glass, 0-20 weight percent of the glass-additives mixture is comprised of fillers, and 0-10 weight percent of the glass-additives mixture is comprised of organic binders. 8. The method according to claim 1, wherein the additives are comprised of fillers, consisting of silica, alumina, zirconia, clay, feldspar, and/or any other ceramic raw material. 9. The method according to claim 1, wherein the additives are comprised of fillers, consisting of clay, sodium silicate, and/or any other inorganic binder. 10. The method according to claim 1, wherein the additives are comprised of filler, consisting of inorganic colorants. 11. The method according to claim 1, wherein the additives are comprised of fillers, consisting of coarse-sized particles added to roughen a surface texture of the ceramic product. 12. The method according to claim 1, wherein the additives are comprised of fillers added to improve a property of the ceramic product, including but not limited to mechanical, chemical durability, and thermal properties. 13. The method according to claim 1, wherein the additives are comprised of aqueous organic binders. 14. The method according to claim 1, wherein the additives are comprised of nonaqueous organic binders. 15. The method according to claim 1, wherein the mixing of the glass powder with additives into a glass-additives mixture is comprised of mixing of the glass powder with additives in a liquid. 16. The method according to claim 1, wherein the mixing of the glass powder with additives into a glass-additives mixture is comprised of mixing of the glass powder with additives in water. 17. The method according to claim 1, wherein the mixing of the glass powder with additives into a glass-additives mixture is comprised of mixing of the glass powder with additives without a liquid added. 18. The method according to claim 1, wherein the granulating of the glass-additives mixture into granulated particles is comprised of drying the glass-additives mixture in a drier, including but not limited to a spray drier or fluid-bed drier. 19. The method according to claim 1, wherein the forming of the granulated particles into a green ceramic article is comprised of pressing or extrusion. 20. The method according to claim 1, wherein the heating of the green ceramic article into the ceramic product comprises firing the green ceramic article to a maximum temperature of about 700�� C. to about 1000�� C. 21. The method according to claim 1, wherein the heating of the green ceramic article into the ceramic product comprises drying the green ceramic article to remove liquid, followed by firing to a maximum temperature of about 700�� C. to about 1000�� C. 22. The method according to claim 1, wherein the heating of the green ceramic article into the ceramic product causes partial crystallization of the ceramic product. 23. The method according to claim 1, wherein the ceramic product comprises tile or brick. 24. The method according to claim 1, wherein the ceramic product has a smooth glossy surface. 25. The method according to claim 1, wherein the ceramic product is further processed by applying a glaze thereon.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (16)
Dutton John S. (Conway GB7), Building product comprising slate particles embedded in a fused glass binder.
Golitz John T. (291 Otis Rd. Barrington Hills IL 60010) Mainieri John F. (2465 Mt. Herman Rd. Granville OH 43023) Bennett Bruce H. (1170 Scarlet Ct. Westerville OH 43081) Moore Richard D. (401 Pinetr, Ceramic products, of glass, fly ash and clay and methods of making the same.
Grodin Martin A. (Pittsburgh PA) Barch Herbert W. (Natrona Heights PA) Harvey Frank E. (Pittsburgh PA) Chardello Patrick C. (Pittsburgh PA), Method for reprocessing glass fibers.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.