The present invention discloses a copolymer composition for use in or as a polymeric binder in an intumescent coating, said copolymer composition comprising a blend of a Newtonian copolymer and of a reticulated copolymer, wherein the Newtonian copolymer is comprised of p-methylstyrene repeat units a
The present invention discloses a copolymer composition for use in or as a polymeric binder in an intumescent coating, said copolymer composition comprising a blend of a Newtonian copolymer and of a reticulated copolymer, wherein the Newtonian copolymer is comprised of p-methylstyrene repeat units and 2-ethylhexylacrylate repeat units, and wherein the reticulated copolymer is comprised of p-methylstyrene repeat units and 2-ethylhexylacrylate repeat units. The present invention further reveals a method of manufacturing an intumescent coating comprising the step of (a) dissolving a Newtonian and a reticulated copolymer in a solvent, wherein the Newtonian copolymer is comprised of p-methylstyrene repeat units and 2-ethylhexylacrylate repeat units, wherein the reticulated copolymer is comprised of p-methylstyrene repeat units and 2-ethylhexylacrylate repeat units, and wherein the solvent is selected from the group consisting of organic solvents and water, (b) optionally, adding a chlorinated paraffin to the solvent, (c) homogenizing the mixture in the solvent, wherein one or more additives selected from the group consisting of conventional reactive pigments systems, dispersants, plasticizers, defoamers, thickeners, chlorinated paraffin solvents, waxes, fillers, fibers, and anti-settling agents are added to the solvent during the homogenizing step.
대표청구항▼
What is claimed is: 1. A method of manufacturing an intumescent coating comprising the step of (a) dissolving a Newtonian and a reticulated copolymer in a solvent, wherein the Newtonian copolymer is comprised of p-methylstyrene repeat units and 2-ethylhexylacrylate repeat units, wherein the reticul
What is claimed is: 1. A method of manufacturing an intumescent coating comprising the step of (a) dissolving a Newtonian and a reticulated copolymer in a solvent, wherein the Newtonian copolymer is comprised of p-methylstyrene repeat units and 2-ethylhexylacrylate repeat units, wherein the reticulated copolymer is comprised of p-methylstyrene repeat units and 2-ethylhexylacrylate repeat units, and wherein the solvent is selected from the group consisting of organic solvents and water, and (b) homogenizing the mixture in the solvent, wherein an anti-settling agent and at least one additive selected from the group consisting of conventional reactive pigments systems, dispersants, plasticizers, defoamers, thickeners, chlorinated paraffin solvents, waxes, fillers, and fibers is added to the solvent during the homogenizing step. 2. A method as specified in claim 1 wherein the Newtonian copolymer is further comprised of p-tert-butylstyrene repeat units. 3. A method as specified in claim 1 wherein the reticulated copolymer is further comprised of p-tert-butylstyrene repeat units. 4. A method as specified in claim 1 wherein the reticulated copolymer is a thixotropic copolymer. 5. A method as specified in claim 1 wherein the reticulated copolymer is a pseudo-plastic copolymer. 6. A method as specified in claim 1 wherein the ratio of p-methylstyrene to 2-ethylhexylacrylate in the reticulated copolymer is within the range of 90/10 to 75/25. 7. A method as specified claim 1 wherein the Newtonian copolymer is further comprised of isobutylmethacrylate. 8. A method as specified in claim 1 wherein the reticulated copolymer is further comprised of isobutylmethacrylate. 9. A method as specified in claim 1 wherein the Newtonian copolymers is obtained by emulsion polymerization. 10. A method as specified in claim 1 wherein the reticulated copolymers is obtained by emulsion polymerization. 11. A method as specified in claim 1 wherein a chlorinated paraffin is added to the solvent in step (a). 12. A method of manufacturing an intumescent coating comprising the step of (a) dissolving a Newtonian and a reticulated copolymer in a solvent, wherein the Newtonian copolymer is comprised of p-methylstyrene repeat units and 2-ethylhexylacrylate repeat units, wherein the reticulated copolymer is comprised of p-methylstyrene repeat units and 2-ethylhexylacrylate repeat units, and wherein the solvent is selected from the group consisting of organic solvents and water, and (b) homogenizing the mixture in the solvent wherein (i) a foam-forming substance, (ii) a carbon forming substance, and (iii) at least one additive selected from the group consisting of conventional reactive pigments systems, dispersants, plasticizers, defoamers, thickeners, chlorinated paraffin solvents, waxes, fillers, fibers and anti-settling agents are added to the solvent during the homogenizing step. 13. A method as specified in claim 12 wherein the foam-forming substance is an ammonium salt of phosphoric acid. 14. A method as specified in claim 12 wherein the carbon forming substance is selected from the group consisting of pentaerythritol, dipentaerythritol, tripentaerythritol and polycondensates of pentaerythritol. 15. A method as specified in claim 1, wherein the solvent is an organic solvent. 16. A method as specified in claim 1 wherein the solvent is water. 17. A method as specified in claim 12 wherein the foam-forming substance is polyphosphoric acid. 18. A method as specified in claim 12 wherein the foam-forming substance is ammonium polyphosphate. 19. A method as specified in claim 1 wherein the ratio of p-methylstyrene to 2-ethylhexylacrylate in the reticulated copolymer is within the range of 90/10 to 50/50. 20. A method as specified in claim 1 wherein the ratio of p-methylstyrene to 2-ethylhexylacrylate in the reticulated copolymer is within the range of 80/20 to 50150.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (3)
Korper George W., Correction fluid marker and formulation for fluid.
Braden Jennifer T. (Stow OH) Burroway Gary L. (Doylestown OH) Bullard Herbert L. (Norton OH) Tedeschi Donald A. (Uniontown OH), Thixotropic thickening agent for aqueous systems.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.