A method of producing a water resistant fiber-cement product. The water repelling agent can be added or applied to the fiber-cement or indeed the material forming the fiber cement at a number of different stages in the process. The resultant material has increased water impermeability over conventio
A method of producing a water resistant fiber-cement product. The water repelling agent can be added or applied to the fiber-cement or indeed the material forming the fiber cement at a number of different stages in the process. The resultant material has increased water impermeability over conventional fiber-cement products.
대표청구항▼
The invention claimed is: 1. A water resistant fibre-cement product, wherein the fibre-cement has incorporated therein a water repelling agent that is integrally associated with the fibre-cement product, wherein the water repelling agent is a long chain terpolymer derived from a polymer selected fr
The invention claimed is: 1. A water resistant fibre-cement product, wherein the fibre-cement has incorporated therein a water repelling agent that is integrally associated with the fibre-cement product, wherein the water repelling agent is a long chain terpolymer derived from a polymer selected from the group consisting of ethylene, vinyl chloride, and vinyl laurate and combinations thereof, the terpolymer incorporated in an amount between 0.5% to 10% by weight of the total materials used to produce the fibre-cement product. 2. The water resistant fibre-cement product according to claim 1, wherein the water repelling agent is incorporated on the surface of the fibre-cement. 3. The water resistant fibre-cement product according to claim 1, wherein the terpolymer includes silane based functional groups. 4. The water resistant fibre-cement product according to claim 1, wherein the water repelling agent is in a proportion of between about 1% to 7%, by weight of the total materials used to produce the fibre-cement. 5. The water resistant fibre-cement product according to claim 1, wherein the water repelling agent is in a proportion of between about 0.5-2.0%, by weight of the total materials used to produce the fibre-cement. 6. The water resistant fibre-cement product according to claim 1, wherein the water repelling agent is in a proportion of between about substantially 2-10% by weight of the total materials used to produce the fibre-cement. 7. The water resistant fibre-cement product according to claim 1, wherein the water resistant quality of a formed product is not reduced by autoclaving. 8. The water resistant fibre-cement product according to claim 1, wherein the product is selected from the group consisting of a board, plank, tile, panel, interior cladding material and exterior cladding material. 9. A method of producing a water resistant fibre-cement product, the method including incorporating a water repelling agent with a fibre-cement material, wherein the water repelling agent is a long chain terpolymer derived from a polymer selected from the group consisting of ethylene, vinyl chloride, or vinyl laurate and combinations thereof, the terpolymer incorporated in an amount between 0.5% to 10% by weight of the total materials used to produce the fibre-cement material; forming a fibre-cement product, whereby the water repelling agent is integrally associated with the fibre-cement. 10. A method according to claim 9, wherein the water repelling agent is a long chain terpolymer derived from ethylene, vinyl chloride, and/or vinyl laurate. 11. A method according to claim 10, wherein the terpolymer includes silane based functional groups. 12. A method according to claim 9, wherein the water repelling agent is added to the fibre-cement as a dispersion and/or emulsion. 13. A method according to claim 12, wherein the dispersion and/or emulsion includes the water repelling agent suspended in a solution selected from the group consisting of water, an alkaline solution, and lime water. 14. A method according to claim 9, wherein the water resistant fibre-cement product is selected from the group consisting of a water resistant fibre-cement board tile, panel, and exterior cladding material. 15. A method according to claim 9, wherein the method includes the step of autoclaving the fibre-cement product. 16. A method according to claim 9, wherein the method includes a step of air curing the fibre-cement product.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (15)
Singer, Robert; Goetze, Richard; Maier, Karl; Kerbl, Maximilian, Alkaline resistant primer and the use thereof.
Hager Rudolf,DEX ; Kreuzpointner Marianne,DEX ; Mayer Hans,DEX, Emulsions of organosilicon compounds for imparting water repellency to building materials.
Gleeson, James A.; Paradis, Kalynne H.; Sloane, Brian P.; Melmeth, David L.; Seligman, Dean M., Fiber cement building materials with low density additives.
Gleeson, James A.; Paradis, Kalynne H.; Sloane, Brian P.; Melmeth, David L.; Seligman, Dean M., Fiber cement building materials with low density additives.
Gleeson, James A.; Paradis, Kalynne H.; Sloane, Brian P.; Melmeth, David L.; Seligman, Dean M., Fiber cement building materials with low density additives.
Gleeson, James A.; Paradis, Kalynne H.; Sloane, Brian P.; Melmeth, David L.; Seligman, Dean M., Fiber cement building materials with low density additives.
Merkley, Donald J.; Luo, Caidian, Method and apparatus for reducing impurities in cellulose fibers for manufacture of fiber reinforced cement composite materials.
Merkley, Donald J.; Luo, Caidian, Method and apparatus for reducing impurities in cellulose fibers for manufacture of fiber reinforced cement composite materials.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.