초록

The invention relates to an antimicrobial adhesive and coating material which contains as the antimicrobial component metallic silver particles with a content of less than 5 ppm of silver, sodium and potassium ions.

대표청구항 ▼

The invention claimed is: 1. Antimicrobial adhesive or coating material which contains as the antimicrobial component metallic silver particles, wherein the silver particles are formed of highly porous aggregates having an average grain size of between 1 μm and 20 μm, the aggregates are f

The invention claimed is: 1. Antimicrobial adhesive or coating material which contains as the antimicrobial component metallic silver particles, wherein the silver particles are formed of highly porous aggregates having an average grain size of between 1 μm and 20 μm, the aggregates are formed of primary particles with an average grain size between 10 nm and 150 nm, and the primary particles are connected together by sinter necks, and the silver particles are mixed with a liquid organic component. 2. Antimicrobial adhesive or coating material as defined in claim 1, wherein the organic components are at least partially hardened after mixing in silver particles. 3. Antimicrobial adhesive or coating material as defined in claim 2, wherein the silver particles cooperate with the organic component after the organic component is at least partially hardened to release silver ions in an antimicrobial effective amount that is not cytotoxic. 4. Antimicrobial adhesive or coating material as defined in claim 3, wherein the silver particles are dispersed in the organic component in an amount equal to 0.1% to 5.0% by weight. 5. Antimicrobial adhesive or coating material as defined in claim 4, wherein the primary particles have an average grain size in the range of 80 to 140 nm. 6. Antimicrobial adhesive or coating material as defined in claim 1, wherein the aggregates have an average grain size of 10 μm to 20 μm. 7. Antimicrobial adhesive or coating material as defined in claim 1, wherein the aggregates have a porosity of up to 95%. 8. Antimicrobial adhesive or coating material as defined in claim 4, wherein the aggregates have a surface area of 3 to 6 m2 per gram. 9. Antimicrobial adhesive or coating material as defined in claim 1, wherein the silver has an essentially undisturbed lattice structure. 10. Antimicrobial adhesive or coating material as defined in claim 1, wherein the aggregates have a porosity of up to 95% and a surface area of 3 to 6 m2 per gram. 11. Antimicrobial adhesive or coating material as defined in claim 1, wherein it is made by mixing the organic component with at least one additional organic component. 12. Antimicrobial adhesive or coating material as defined in claim 1, wherein the silver particles are mixed immediately with the liquid organic component or immediately with a liquid precursor product of same. 13. Antimicrobial adhesive or coating material as defined in claim 1, wherein said metallic silver particles are present in an amount of from 0.01 to 5.0 weight %. 14. Antimicrobial adhesive or coating material as defined in claim 1, wherein the aggregates are completely infiltrated with the organic component. 15. Antimicrobial adhesive or coating material as defined in claim 1, wherein the organic component and/or an additional organic component is essentially composed of an acrylate or methacrylate. 16. Antimicrobial adhesive or coating material as defined in claim 1, wherein the organic component and/or an additional organic component is essentially composed of an epoxide, urethane, silicone or cyanoacrylate. 17. Antimicrobial adhesive or coating material as defined in claim 1, including a further constituent comprising a salt or a complex containing cations of at least one of the following metals: Au, Pt, Pd, Ir, Sn, Cu, Sb, Zn. 18. Antimicrobial adhesive or coating material as defined in claim 17, wherein the cations are bound in ion exchangers. 19. Antimicrobial adhesive or coating material as defined in claim 18, wherein the further constituent is a salt of a carboxylic acid. 20. Antimicrobial adhesive or coating material as defined in claim 1, wherein the adhesive or coating material is an adhesive. 21. Antimicrobial adhesive or coating material as defined in claim 1, wherein the organic component and/or an additional organic component contains one or more of the following constituents: solvent, filler material, pigment, binding agent, plasticizer, drying accelerator, fungicide. 22. Antimicrobial adhesive or coating material as defined in claim 1, wherein the adhesive or coating material is a lacquer, a paint or a dispersion which can be hardened. 23. A process of using the antimicrobial adhesive or coating material as defined in claim 1 comprising incorporating the antimicrobial adhesive or coating material in the manufacture and/or coating of wound coverings, bandages, incontinence products, medical devices, packaging materials, for the coating of walls of buildings, housings and/or components of technical devices. 24. Method for the manufacture of an antimicrobial adhesive or coating material as defined in claim 1, with the following steps: generating a silver vapor by sputtering or by vaporization in a vacuum recipient, condensing the silver vapor and forming silver particles of highly porous aggregates having an average grain size between 1 μm and 20 μm, the aggregates being formed of primary particles with an average grain size between 10 nm and 150 nm, and the primary particles are connected together by sinter necks, and mixing the silver particles in an antimicrobial effective amount with a liquid organic component. 25. Method as defined in claim 24, wherein the organic component is at least partially hardened after the mixing in of silver particles. 26. Method as defined in claim 25, wherein the silver particles cooperate with the organic component to release silver ions in an antimicrobial effective amount that is not cytotoxic. 27. Method as defined in claim 24, wherein the silver vapor is condensed during the vapor phase so that the aggregates are created from the primary particles. 28. Method as defined in claim 24, wherein the organic component or a precursor product of same is used as liquid. 29. Method as defined in claim 24, wherein the silver particles are added to a precursor product instead of the organic component and then the organic component is made. 30. Method as defined in claim 24, wherein 0.01 to 5.0 weight % of silver particles are added to the organic component. 31. Method as defined in claim 24, wherein the organic component is mixed with at least one further liquid organic component. 32. Method as defined in claim 24, wherein the organic component and/or the additional organic component are/is essentially composed of an acrylate or a methacrylate. 33. Method as defined in claim 24, wherein the organic component and/or the additional organic component are/is essentially composed of an epoxide, urethane, silicone or cyanoacrylate. 34. Method as defined in claim 24, including the additional step of adding to the organic component and/or the additional organic component a further constituent comprising a salt or a complex containing cations of at least one of the following metals: Au, Pt, Pd, Ir, Sn, Cu, Sb, Zn. 35. Method as defined in claim 34, wherein the cations are bound in ion exchangers and are added at least to the organic component. 36. Method as defined in claim 35, wherein the further constituent is a salt of carboxylic acid. 37. Method as defined in claim 24, wherein one or more of the following is/are added to the organic component and/or the additional organic component: solvent, filler material, pigment, binding agent, plasticizer, drying accelerator, fungicide. 38. Antimicrobial adhesive or coating material as defined in claim 1, wherein the silver particles are dispersed in the organic component in an amount equal to 0.1% to 5.0% by weight, the primary particles have an average grain size in the range of 80 to 140 nm, the aggregates have an average grain size of 10 μm to 20 μm, a porosity between 70% and 95% and a surface area of 3 to 6 m2 per gram. 39. Antimicrobial adhesive or coating material as defined in claim 38, wherein the silver particles cooperate with the organic component after the organic component is at least partially hardened to release silver ions in an antimicrobial effective amount that is not cytotoxic.