초록
▼
A weld process cuitable for repairing precipitation-strengthened superalloys, and particularly gamma prime-strengthened nickel-based superalloys. The process entails forming a weldment in a cavity present in a surface of an article formed of a precipitation-strengthened superalloy. The cavity has a
A weld process cuitable for repairing precipitation-strengthened superalloys, and particularly gamma prime-strengthened nickel-based superalloys. The process entails forming a weldment in a cavity present in a surface of an article formed of a precipitation-strengthened superalloy. The cavity has a root region and a cap region between the root region and the surface of the article. A solid body formed of a superalloy composition is placed in the root region of the cavity so as to occupy a first portion but not a second portion of the root region. A first filler material formed of a solid solution-strengthened superalloy is then weld-deposited in the second portion of the root region. Subsequently, a second filler material formed of a precipitation-strengthened superalloy is weld-deposited in the cap region of the cavity.
대표청구항
▼
What is claimed is: 1. A process of forming a weldment in a cavity present in a surface of an article formed of a first precipitation-strengthened superalloy, the cavity having a root region and a cap region between the root region and the surface of the article, the process comprising the steps of
What is claimed is: 1. A process of forming a weldment in a cavity present in a surface of an article formed of a first precipitation-strengthened superalloy, the cavity having a root region and a cap region between the root region and the surface of the article, the process comprising the steps of: placing a solid body in only the root region of the cavity, the solid body being sized to occupy a central portion but not a peripheral portion between the central portion and side walls of the root region of the cavity, the solid body being formed of a superalloy composition; depositing by welding a first filler material in the peripheral portion of the root region such that in combination the solid body and the first filler material completely fill the root region but are not present in the cap region, the first filler material being formed of a solid solution-strengthened superalloy; depositing by welding a second filler material in the cap region of the cavity to form a weldment that fills the cavity and comprises the solid body and the first and second filler materials, the second filler material being formed of a second precipitation-strengthened superalloy; and then heat treating the weldment, wherein the heat-treated weldment contains the solid body and the first filler material which in combination completely fill the root region of the cavity and contains the second filler material in the cap region of the cavity. 2. The process according to claim 1, wherein the first and second precipitation-strengthened superalloys, the superalloy composition of the solid body, and the solid solution-strengthened superalloy of the first filler material are nickel-based superalloys. 3. The process according to claim 1, wherein at least one of the superalloy composition and the solid solution-strengthened superalloy is more ductile than the first and second precipitation-strengthened superalloys. 4. The process according to claim 1, wherein the superalloy composition of the solid body and the solid solution-strengthened superalloy of the first filler material are more ductile than the first and second precipitation-strengthened superalloys. 5. The process according to claim 1, wherein the superalloy composition of the solid body is a solid solution-strengthened superalloy. 6. The process according to claim 1, wherein the superalloy composition of the solid body is a precipitation-strengthened superalloy. 7. The process according to claim 1, wherein the cavity extends through the article so as to define an opening on a second surface of the article. 8. The process according to claim 1, wherein the first portion of the cavity occupied by the solid body is a central portion of the root region of the cavity, and the second portion of the root region of the cavity is a peripheral portion of the root region. 9. The process according to claim 1, wherein prior to the placing step the cavity is machined to define a laterally-opposed pair of side walls and a longitudinally-opposed pair of end walls, each of the side walls and end walls being inclined relative to a normal direction to the surface of the article. 10. The process according to claim 9, wherein the side walls are inclined relative to the normal direction at angles that are less than angles at which the end walls are inclined relative to the normal direction. 11. The process according to claim 1, wherein the second filler material completely covers the first filler material and the solid body at the surface of the article. 12. The process according to claim 1, wherein the article is a single-crystal casting of the first precipitation-strengthened superalloy. 13. A process of forming a weldment in a cavity present in a surface of a single-crystal casting formed of a first precipitation-strengthened nickel-based superalloy, the cavity having a root region and a cap region between the root region and the surface of the casting, the process comprising the steps of: securing a solid body in the root region of the cavity, the solid body being sized to fill a central portion but not a peripheral portion between the central portion and side walls of the root region of the cavity, the solid body being formed of a superalloy composition; welding a first filler material in the peripheral portion of the root region such that in combination the solid body and the first filler material completely fill the root region but are not present in the cap region, the first filler material being formed of a solid solution-strengthened nickel-based superalloy; welding a second filler material in the cap region of the cavity so as to cover the solid body and the first filler material and form a weldment that completely fills the cavity and comprises the solid body and the first and second filler materials, the second filler material being formed of a second precipitation-strengthened nickel-based superalloy; and then heat treating the weldment, wherein the heat-treated weldment contains the solid body and the first filler material which in combination completely fill the root region of the cavity and contains the second filler material in the cap region of the cavity. 14. The process according to claim 13, wherein at least one of the superalloy composition of the solid body and the solid solution-strengthened nickel-based superalloy of the first filler material is more ductile than the first and second precipitation-strengthened nickel-based superalloys. 15. The process according to claim 13, wherein the superalloy composition of the solid body is a solid solution-strengthened superalloy, and the solid solution-strengthened nickel-based superalloys of the solid body and the first filler material are more ductile than the first and second precipitation-strengthened nickel-based superalloys. 16. The process according to claim 13, wherein the superalloy composition of the solid body is a precipitation-strengthened superalloy. 17. The process according to claim 13, wherein the cavity extends through the casting so as to define an opening on a second surface of the casting. 18. The process according to claim 13, wherein prior to the placing step the cavity is machined to have an oblong shape and define a laterally-opposed pair of side walls and a longitudinally-opposed pair of end walls, each of the side walls and end walls being inclined relative to a normal direction to the surface of the article, the side walls being inclined relative to the normal direction at angles that are less than angles at which the end walls are inclined relative to the normal direction.