초록 ▼

The present disclosure relates to improved efficient and effective systems and methods of manufacturing hydrophilic polyethersulfone (PES) membrane suitable for commercial applications and the resultant hydrophilic polyethersulfone (PES) membrane suitable for commercial applications produced thereby

The present disclosure relates to improved efficient and effective systems and methods of manufacturing hydrophilic polyethersulfone (PES) membrane suitable for commercial applications and the resultant hydrophilic polyethersulfone (PES) membrane suitable for commercial applications produced thereby and includes methods of manufacturing hydrophilic polyethersulfone (PES) membrane comprising the acts of: providing hydrophobic PES membrane; prewetting the hydrophobic PES membrane in a sufficient amount of a liquid having a sufficiently low surface tension; exposing the wet hydrophobic PES membrane to a sufficient amount of an aqueous solution of oxidizer; and after the exposing act, heating the hydrophobic PES membrane for a sufficient time at a sufficient temperature and methods of manufacturing hydrophilic polyethersulfone (PES) membrane comprising the acts of: providing gel PES membrane; exposing the gel PES membrane to a sufficient amount of an aqueous solution of oxidizer; and after the exposing act, heating the hydrophobic PES membrane for a sufficient time at a sufficient temperature and the resulting products.

대표청구항 ▼

What is claimed is: 1. A method of manufacturing hydrophilic polyethersulfone (PES) membrane comprising the acts of: providing hydrophobic PES membrane; prewetting the hydrophobic PES membrane in an amount of a liquid having a low surface tension; exposing the wet hydrophobic PES membrane to an amo

What is claimed is: 1. A method of manufacturing hydrophilic polyethersulfone (PES) membrane comprising the acts of: providing hydrophobic PES membrane; prewetting the hydrophobic PES membrane in an amount of a liquid having a low surface tension; exposing the wet hydrophobic PES membrane to an amount of an aqueous solution of oxidizer; after the exposing act, heating the hydrophobic PES membrane at a predetermined temperature; during the heating act, operatively positioning the PES membrane in a saturated water steam medium; and continuously moving the PES membrane through the saturated water steam medium. 2. The method of claim 1 further comprising the act of: after the prewetting act, washing the resultant membrane with water. 3. The method of claim 2 further comprising the act of: after the heating act, drying the resultant membrane. 4. The method of claim 3 wherein, during the drying act, the resultant membrane is exposed to heat of about 70° C. to about 95° C. 5. The method of claim 3 wherein the washing act is partly performed before the membrane oxidation act. 6. The method of claim 2 wherein, during the heating act the hydrophobic PES membrane is heated at about 90° C. to about 95° C. for about 15 minutes. 7. The method of claim 1 wherein the oxidizer is selected from the group consisting of: Ammonium persulfate (NH4)2S2O8, Hydrogen peroxide (H2O2), Bleach (HClO), Permanganate (MnO4-), Ozone (O3) or Dichromate (Cr2O8-2) and combinations thereof. 8. The method of claim 1 wherein, during the heating act, the PES membrane is contained in a sufficient aqueous solution of sufficient oxidizer to cause oxidation of the membrane. 9. The method of claim 1 further comprising the act of: after the heating act, washing the resultant membrane with water for a sufficient time in order to sufficiently remove the remains of the oxidizer therefrom. 10. The method of claim 1 wherein, the oxidizer comprises: Ammonium persulfate (NH4)2S2O8. 11. The method of claim 1 further comprising the acts of: after the exposing act in the solution of oxidizer, operatively positioning the membrane between two films so that the membrane is sandwiched therebetween; and continuously moving the sandwiched membrane through at lest one heating zone. 12. A method of manufacturing hydrophilic polyethersulfone (PES) membrane comprising the acts of: providing gel PES membrane; exposing the gel PES membrane to an amount of an aqueous solution of oxidizer; after the exposing act, heating the hydrophobic PES membrane; during the heating act, operatively positioning the PES membrane in a saturated water steam medium; and continuously moving the PES membrane through the saturated water steam medium. 13. The method of claim 12 wherein the oxidizer is selected from the group consisting of: Ammonium persulfate (NH4)2S2O8, Hydrogen peroxide (H2O2), Bleach (HClO), Permanganate (MnO4-), Ozone (O3) or Dichromate (Cr2 O8-2) and combinations thereof. 14. The method of claim 12 further comprising the acts of: after the exposing act in the solution of oxidizer, operatively positioning the membrane between two films so that the membrane is sandwiched therebetween; and continuously moving the sandwiched membrane through at lest one heating zone.