Method for the production of highly pure metallic nano-powders
원문보기
IPC분류정보
국가/구분
United States(US) Patent
등록
국제특허분류(IPC7판)
B22F-009/16
B22F-009/20
출원번호
UP-0518227
(2003-06-19)
등록번호
US-7544229
(2009-07-01)
우선권정보
IL-150325(2002-06-19)
국제출원번호
PCT/IL03/000522
(2003-06-19)
§371/§102 date
20051017
(20051017)
국제공개번호
WO03/000491
(2003-12-31)
발명자
/ 주소
Garbar, Arkady
De La Vega, Fernando
Matzner, Einat
출원인 / 주소
Cima NanoTech Israel Ltd.
대리인 / 주소
Fish & Richardson P.C.
인용정보
피인용 횟수 :
4인용 특허 :
6
초록▼
The present invention discloses a novel method for the production of metallic nano-powder. This cost-effective, simple process is customized for a full-scale production of metallic nano-powders containing a first metal, and comprising the following of forming an alloy comprising said first metal and
The present invention discloses a novel method for the production of metallic nano-powder. This cost-effective, simple process is customized for a full-scale production of metallic nano-powders containing a first metal, and comprising the following of forming an alloy comprising said first metal and at least one soluble metal; applying first thermal treatment in the manner homogenized alloy is obtained; applying a cold work to the homogenized alloy so thin strips are obtained; applying a second thermal treatment to the alloy until a phase composition of predetermined characteristics is obtained; subjecting the said alloy to a leaching agent adapted to effectively leach out the least one soluble metal; filtering and washing the powder; washing the powder; drying the powder; coating the powder with chemicals; and then de-agglomerating the coated powder. The present invention also discloses a cost-effective and highly pure metallic powder produced by the method defined above.
대표청구항▼
The invention claimed is: 1. A method for producing a metal nano-powder comprising: (a) forming an alloy comprising a first metal and a second metal that is different from the first metal; (b) subjecting the alloy to a leaching agent effective to leach out the second metal and form a metal nano-pow
The invention claimed is: 1. A method for producing a metal nano-powder comprising: (a) forming an alloy comprising a first metal and a second metal that is different from the first metal; (b) subjecting the alloy to a leaching agent effective to leach out the second metal and form a metal nano-powder; (c) washing and filtering the metal nano-powder; (d) drying the washed and filtered metal nano-powder; (e) coating the dried metal nano-powder with a chemical reagent to form a coated metal nano-powder wherein the chemical reagent is selected from the group consisting of sorbitan esters, polyoxyethylene esters, alcohols, glycerin, polyglycols, organic acid, organic acid salts, organic acid esters, thiols, phosphines, low molecular weight polymers, and combinations thereof; and (f) de-agglomerating the coated metal nano-powder. 2. A method according to claim 1 further comprising thermally treating the alloy prior to leaching. 3. A method according to claim 2 comprising thermally treating the alloy at a temperature between 460 and 610° C. 4. A method according to claim 1 further comprising cold working the alloy to create thin strips comprising the alloy prior to leaching. 5. A method according to claim 4 further comprising thermally treating the alloy prior to cold working. 6. A method according to claim 5 comprising thermally treating the alloy at a temperature of about 400° C. 7. A method according to claim 1 further comprising de-agglomerating the coated metal nano-powder using a jet mill. 8. A method according to claim 1 further comprising de-agglomerating the coated metal nano-powder using a mechanical disperser, a mechanical homogenizer, an ultrasonic homogenizer, or combination thereof. 9. A method according to claim 1 wherein the first metal is selected from the group consisting of silver, copper, nickel, cobalt, titanium, palladium, platinum, gold, iridium, and combinations thereof. 10. A method according to claim 1 wherein the second metal is selected from the group consisting of aluminum, zinc, magnesium, tin, copper, and silver. 11. A method according to claim 1 wherein the leaching agent is selected from the group consisting of sodium hydroxide, potassium hydroxide, and combinations thereof. 12. A method according to claim 1 wherein the leaching agent is selected from the group consisting of acetic acid, hydrochloric acid, formic acid, sulfuric acid, nitric, acid, hydrofluoric acid, and combinations thereof. 13. A method according to claim 1 wherein the metal nano-powder comprises an alloy. 14. A method according to claim 10 wherein the metal nano-powder comprises an alloy of silver and at least one other metal element selected from Group I, Group IV, Group V, Group VI, Group VII, and Group VIII of the Periodic Table of Elements. 15. A method according to claim 1 comprising coating the metal nano-powder with at least two different chemical reagents. 16. A method for producing a metal nano-powder comprising: (a) forming an alloy comprising a first metal and a second metal that is different from the first metal; (b) subjecting the alloy to a first thermal treatment to form a thermally treated alloy; (c) cold working the thermally treated alloy to form thin strips comprising the alloy; (d) subjecting the thin strips to a second thermal treatment to form thermally treated thin strips comprising the alloy; (e) subjecting the thermally treated thin strips to a leaching agent effective to leach out the second metal to form a metal nano-powder; (f) washing, filtering, and then drying the metal nano-powder; (g) coating the dried metal nano-powder with a chemical reagent to form a coated metal nano-powder wherein the chemical reagent is selected from the group consisting of sorbitan esters, polyoxyethylene esters, alcohols, glycerin, polyglycols, organic acid, organic acid salts, organic acid esters, thiols, phosphines, low molecular weight polymers, and combinations thereof; and (h) de-agglomerating the coated metal nano-powder. 17. A method for producing a metal nano-powder comprising: (a) forming an alloy comprising a first metal and a second metal that is different from the first metal; (b) subjecting the alloy to a leaching agent effective to leach out the second metal and form a metal nano-powder; (c) washing and filtering the metal nano-powder; (d) drying the washed and filtered metal nano-powder; (e) coating the dried metal nano-powder with 1-5 wt. %, based upon the weight of the metal nano-powder, of a chemical reagent to form a coated metal nano-powder, wherein the chemical reagent is selected from the group consisting of sorbitan esters, polyoxyethylene esters, alcohols, glycerin, polyglycols, organic acid, organic acid salts, organic acid esters, thiols, phosphines, low molecular weight polymers, and combinations thereof; and (f) de-agglomerating the coated metal nano-powder. 18. A method according to claim 17 comprising coating the metal nano-powder with (a) 1-5 wt. %, based upon the weight of the metal nano-powder, of a primary chemical reagent and (b) 0.1-2.5 wt. %, based upon the weight of the metal nano-powder, of a secondary chemical reagent to form the coated metal nano-powder.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (6)
Khasin Ernst (Rishon LeZion ILX), Method of producing high-purity ultra-fine metal powder.
Zhou Peizheng ; Lee Lap-Keung ; Zhou Jinglai,CNX ; Lu Yijun,CNX ; Li Guohui,CNX, Skeletal iron catalyst having improved attrition resistance and product selectivity in slurry-phase synthesis processes.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.