초록 ▼

A method of forming a porous honeycomb substrate including a non-woven fibrous ceramic body is provided herein. The fibrous ceramic body is substantially composed of intertangled ceramic fiber forming a rigid three-dimensional matrix. Washcoat and catalyst materials can be applied to at least partia

A method of forming a porous honeycomb substrate including a non-woven fibrous ceramic body is provided herein. The fibrous ceramic body is substantially composed of intertangled ceramic fiber forming a rigid three-dimensional matrix. Washcoat and catalyst materials can be applied to at least partially coat the honeycomb channels. The porous honeycomb substrate provides an improved substrate for use in filtration applications such as exhaust particulate filtration of internal combustion engines.

대표청구항 ▼

What is claimed is: 1. A method of forming a porous substrate comprising: mixing ceramic fibers with a liquid to form a formable mixture; adding a catalyst; forming a green substrate; sintering the green substrate to form a rigid composite fibrous structure having fibers arranged in a non-woven thr

What is claimed is: 1. A method of forming a porous substrate comprising: mixing ceramic fibers with a liquid to form a formable mixture; adding a catalyst; forming a green substrate; sintering the green substrate to form a rigid composite fibrous structure having fibers arranged in a non-woven three-dimensional matrix having pore space occupying at least 60% of the volume within the fibrous structure, the sintering step forming fiber-to-fiber bonds in the rigid composite fibrous structure, the rigid composite fibrous structure having a honeycomb arrangement of channels; and wherein step of adding a catalyst is preformed before the sintering step. 2. The method according to claim 1 wherein the step of adding a catalyst is preformed before the forming step. 3. The method according to claim 1 wherein the step of adding a catalyst is performed during the mixing step. 4. The method according to claim 3 wherein the catalyst is mixed with the fibers and liquid. 5. The method according to claim 3 wherein the catalyst is added to the liquid. 6. The method according to claim 1 wherein the catalyst is in the form of a liquid. 7. The method according to claim 1 wherein the catalyst adheres to the fibers during sintering. 8. The method according to claim 1 wherein the catalyst is located within the pore space in the three-dimensional matrix. 9. The method according to claim 1 further comprising forming channels, and wherein the catalyst located in the channels. 10. The method according to claim 1 wherein the catalyst is at least one of palladium, platinum, rhodium, chromium, nickel, rhenium, ruthenium, silver, osmium, iridium, vanadium, gold, iridium and magnesium. 11. The method according to claim 1 wherein the catalyst is organic. 12. The method according to claim 1 wherein the catalyst is at least one of a non-metallic catalyst, a rare earth catalyst, a base metal catalyst, a precious metal catalyst and a noble metal catalyst. 13. The method according to claim 1 wherein the catalyst comprises at least one of an oxidation catalyst, a reduction catalyst, a two-way catalyst, a three-way catalyst, a four-way catalyst, a NOx adsorber, and mixtures thereof. 14. The method according to claim 1 wherein the catalyst is suitable for catalyzing an oxidation reaction of a hydrocarbon. 15. The substrate according to claim 1, wherein the catalyst is added in an amount of about 5 to about 150 grams per cubic foot in the rigid composite fibrous structure.