Catalyst composition for treating heavy feedstocks
원문보기
IPC분류정보
국가/구분
United States(US) Patent
등록
국제특허분류(IPC7판)
C10G-047/04
C10G-047/00
C10G-011/02
C10G-011/00
C10G-011/05
출원번호
UP-0313135
(2008-11-17)
등록번호
US-7594995
(2009-10-12)
우선권정보
CA-2539231(2006-03-10)
발명자
/ 주소
Shen, Baojian
Gao, Jinsen
Xu, Chunming
Zhao, Liang
Li, Xianfeng
Wu, Pei
출원인 / 주소
State Key Laboratory of Heavy Oil Processing
대리인 / 주소
Johnson, Kenneth H
인용정보
피인용 횟수 :
0인용 특허 :
4
초록▼
The present invention provides a catalyst and a process for its preparation and its use in cracking heavy feedstocks. The catalyst comprises one or more zeolites having a controlled silica to alumina ratio and preferably treated with alkali in the presence of a matrix component selected from the gro
The present invention provides a catalyst and a process for its preparation and its use in cracking heavy feedstocks. The catalyst comprises one or more zeolites having a controlled silica to alumina ratio and preferably treated with alkali in the presence of a matrix component selected from the group consisting of clays, synthetic matrix other than pillared clay, and mixtures thereof. The catalyst are particularly useful in treating heavy feedstock such as residues from oil sands processing.
대표청구항▼
What is claimed is: 1. A process for the fluidized cracking of a hydrocarbon feedstock having a boiling point above 300° C. at a temperature from 500° C. to 800° C. and a pressure from 103.3 kPa to 6.89×103 kPa to produce more than 15% of C2-4 olefins, and gasoline and diesel cuts as co-products, a
What is claimed is: 1. A process for the fluidized cracking of a hydrocarbon feedstock having a boiling point above 300° C. at a temperature from 500° C. to 800° C. and a pressure from 103.3 kPa to 6.89×103 kPa to produce more than 15% of C2-4 olefins, and gasoline and diesel cuts as co-products, and having a coke make of less than 18% comprising contacting the feedstock with a catalyst prepared by a process comprising forming a slurry of from 15 to 55 weight % of a matrix component selected from the group consisting of clays, synthetic matrix other than pillared clay, and mixtures thereof and from 10 to 20 weight % of a sol or gel of a binder selected from the group consisting of oxides of aluminum, silicon, and mixtures thereof and from 0 to 15 weight % of an oxide of a grouo IVB or VB metal adding thereto from 10 to 75 weight % of a mixture of one or more zeolites selected from the group consisting of: (i) not less than 10 weight %, based on the total weight of zeolites, of a zeolite having a silica to alumina ratio from 25 to 200 and up to 12 rings in a structural unit which has been treated with less than 0.5 molar alkaline solution at a temperature from 20° C. to 350° C. to reduce the silica to alumina ratio to less than 45, said alkaline treated zeolite having a meso-large pore BET surface area of greater than 50 m2/g; (ii) a zeolite having a silica alumina ratio from 10 to 70 and up to 12 rings in a structural unit and a meso large pore size BET surface area less than 40 m2/g; (iii) a beta zeolite having a structure in which the silica to aluminum ratio is less than 100; (iv) a Y-faujasite type zeolite having a structure in which silica to alumina ratio is less than 30; the sum of components (i), (ii), (iii) and (iv) adding up to 100 weight % of the zeolite components in said catalysts, wherein one or more of said zeolite components have been subjected to one or more of the following treatments (a) impregnating said zeolite with a phosphorus compound to provide from 0.2 to 15 weight % calculated as P2O5 based on the weight of the zeolite and either currently or subsequently treating the impregnated zeolite with steam or water at a temperature from 110° C. to 800° C. at a pressure from 103.3 kPa to 6.89×103 kPa for a time from 0.1 to 20 hours; (b) treating said zeolite with one or more group VB, VI B, VIIB, VIII and Cu metal compounds to provide from 0.1 to 10 weight % of the metal based on the weight of the zeolite; (c) treating said zeolite with one or more rare earth compounds to provide from 0.1 to 10 weight % of the oxide of the rare earth metal based on the weight of the zeolite; forming particulates of said catalyst having a size from 0.001 to 0.8 mm. 2. The process according to claim 1, wherein the temperature is from 530° C. to 770° C. 3. The process according to claim 2, wherein the process is continuous and is conducted in a reactor having at least one side riser to introduce fresh catalyst, regenerated catalyst or a mixture thereof into the reactor and a regenerator with cyclones to decoke the catalyst and separate the catalyst from the off gases. 4. The process of claim 1, wherein zeolite component (i) has a silica to alumina ratio less than 40. 5. The process of claim 4, wherein zeolite component (i) is present in an amount from 10 to 90 weight % of the total zeolite content. 6. The process of claim 5, wherein the phosphorus content in the catalyst is from 0.2 to 15 weight % based on the total weight of the catalyst. 7. The process of claim 6, wherein said zeolite, said catalyst or both are treated with a phosphorus compound selected from the group consisting of ammonium dihydrogen phosphate and diammonium hydrogen phosphate, ammonium hypophosphate, ammonium orthophosphate, ammonium dihydrogen orthophosphate, ammonium hydrogen orthophosphate, triammonium phosphate, phosphine halides and organic phosphates, phosphines, and phosphates, and combinations thereof. 8. The process of claim 7, wherein zeolite component (i) is selected from the group consisting of ZSM-5, ZSM-8, ZSM-11, ZSM-12, ZSM-35, ZSM-38 and mixtures thereof. 9. The process of claim 8, wherein the group VB, VIB, VIIB VIII and Cu elements are selected from the group consisting of V, Cr, Mn, Co, Ni, Cu, and mixtures thereof. 10. The process of claim 9, wherein zeolite component (i) has a meso-large pore BET surface area greater than 80 m2/g. 11. The process of claim 10, wherein zeolite component (ii) is selected from the group consisting of ZSM-5, ZSM-8, ZSM-11, ZSM-12, ZSM-35, ZSM-38 and mixtures thereof. 12. The process of claim 1, wherein zeolite components (ii), (iii) and (iv) or a mixture there of are present in a total amount from 10 to 90 weight % of the zeolite components. 13. The process of claim 1, wherein said catalyst is formed into particles by one or more processes selected from the group consisting of: (i) spray drying the resulting slurry at a temperature from 100° C. to 650° C., followed by calcining the resulting solid at a temperature from 500° C. to 800° C.; (ii) drying the resulting slurry at a temperature from 100° C. to 150° C.; calcining the resulting solid at a temperature from 500° C. to 800° C. and subjecting it to a comminution step; and (iii) by extruding the resulting slurry and drying the resulting extrudate. 14. The process of claim 1, wherein the final particle size for the catalyst is from 0.005 to 0.150 mm. 15. The process of claim 1, wherein the resulting catalyst is further treated with from 0 to 15 weight % of a phosphorus compound calculated as P2O5 based on the weight of the catalyst.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (4)
Rieck Hans-Peter (Hofheim am Taunus DEX) Kalz Hans-Jrgen (Hofheim am Taunus DEX), Aluminosilicates having a zeolite structure, and process for the manufacture thereof.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.