초록 ▼

In preferred embodiments, the present invention provides methods of controllably making a vinyl polymer hydrogel having desired physical properties without chemical cross links or radiation. The gelation process is modulated by controlling, for example, the temperature of a resultant vinyl polymer m

In preferred embodiments, the present invention provides methods of controllably making a vinyl polymer hydrogel having desired physical properties without chemical cross links or radiation. The gelation process is modulated by controlling, for example, the temperature of a resultant vinyl polymer mixture having a gellant or using active ingredients provided in an inactive gellant complex. In accordance with a preferred embodiment, the method of manufacturing a vinyl polymer hyrodgel includes the steps of providing a vinyl polymer solution comprising a vinyl polymer dissolved in a first solvent; heating the vinyl polymer solution to a temperature elevated above the melting point of the physical associations of the vinyl polymer, mixing the vinyl polymer solution with a gellant, wherein the resulting mixture has a higher Flory interaction parameter than the vinyl polymer solution; inducing gelation of the mixture of vinyl polymer solution and gellant; and controlling the gelation rate to form a viscoelastic solution, wherein workability is maintained for a predetermined period, thereby making a vinyl polymer hydrogel having the desired physical property. In further preferred embodiments, the present invention provides physically crosslinked hydrogels produced by controlled gellation of viscoelastic solution wherein workability is maintained for a predetermined period. In another aspect, the present invention provides kits for use in repairing intervertebral disks or articulated joints including components that form the vinyl polymer hydrogel and a dispenser.

대표청구항 ▼

We claim: 1. A method of making an injectable thetagel solution for injection into a region, wherein the method comprises the steps of: dissolving polyvinyl alcohol (PVA) molecules in a first solution to form a PVA solution, wherein the first solution has a Flory interaction parameter (chi value) t

We claim: 1. A method of making an injectable thetagel solution for injection into a region, wherein the method comprises the steps of: dissolving polyvinyl alcohol (PVA) molecules in a first solution to form a PVA solution, wherein the first solution has a Flory interaction parameter (chi value) that is not sufficient for gelation; contacting the PVA solution with a second solution in a controlled manner, wherein after the contacting the combination of both solutions has a Flory interaction parameter (chi value) that is sufficient for gelation, and thereby forms an injectable thetagel solution; and maintaining for a period of time the injectable thetagel solution at a temperature such that it is in a workable state, wherein the injectable thetagel solution can be injected into a region, and therein gel in situ after the injection to form in the region a polymer hydrogel that has physical crosslinks between PVA molecules, wherein the polymer hydrogel is formed without chemical crosslinkers, irradiation or thermal cycling. 2. The method according to claim 1, wherein the first solution comprises one or more selected from the group consisting of deionized water and dimethylsulfoxide. 3. The method according to claim 1, wherein the second solution comprises one or more selected from the group consisting of salts, alcohols, polyols, amino acids, sugars, proteins, and polysaccharides. 4. The method according to claim 1 wherein the hydrogel is anisotropic in one or more properties. 5. The method according to claim 1, wherein the contacting comprises mixing. 6. The method of claim 1, wherein the injectable thetagel solution comprises about 1.0 to about 50.0 weight percent polyvinyl alcohol. 7. The method of claim 1, wherein after the contacting the Flory interaction parameter is 0.25 to 1.0. 8. The method of claim 1, wherein the PVA solution contains one or more non-gelling components. 9. The method of claim 1, further comprising hyaluronic acid. 10. The method of claim 1, further comprising polyacrylic acid. 11. The method of claim 1, further comprising a therapeutic agent. 12. The method of claim 1, wherein the region is a body space selected from the group consisting of a joint space or space within a vertebral disk. 13. A method for forming a polymer hydrogel within a region, wherein the method comprises the steps of: (I) injecting an injectable thetagel solution into a region, wherein the injectable thetagel solution is produced by: (A) dissolving polyvinyl alcohol (PVA) molecules in a first solution to form a PVA solution, wherein the first solution has a Flory interaction parameter (chi value) that is not sufficient for gelation; (B) contacting the PVA solution with a second solution in a controlled manner, wherein after the contacting the combination of both solutions has a Flory interaction parameter (chi value) that is sufficient for gelation, and thereby forms the injectable thetagel solution; and (C) maintaining for a period of time the injectable thetagel solution at a temperature such that it is in a workable state; and (II) allowing the injectable thetagel solution to gel in situ after the injection to form in the region a polymer hydrogel that has physical crosslinks between PVA molecules, wherein the polymer hydrogel is formed without chemical crosslinkers, irradiation or thermal cycling. 14. The method according to claim 13, wherein the first solution comprises one or more selected from the group consisting of deionized water and dimethylsulfoxide. 15. The method according to claim 13, wherein the second solution comprises one or more selected from the group consisting of salts, alcohols, polyols, amino acids, sugars, proteins, and polysaccharides. 16. The method according to claim 13 wherein the hydrogel is anisotropic in one or more properties. 17. The method according to claim 13, wherein the contacting comprises mixing. 18. The method of claim 13, wherein the injectable thetagel solution comprises about 1.0 to about 50.0 weight percent polyvinyl alcohol. 19. The method of claim 13, wherein after the contacting the Flory interaction parameter is 0.25 to 1.0. 20. The method of claim 13, wherein the PVA solution contains one or more non-gelling components. 21. The method of claim 13, further comprising hyaluronic acid. 22. The method of claim 13, further comprising polyacrylic acid. 23. The method of claim 13, further comprising a therapeutic agent. 24. The method of claim 13, wherein the region is a body space selected from the group consisting of a joint space or space within a vertebral disk.