초록 ▼

A method, and an article produced thereby, of providing a corroson-resistant, scratch-resistant, and stick-resistant, surface on a ferrous-metal-containing article, including forming microcavities in a ferrous-metal-containing article surface by ferritic nitrocarburization and seasoning the surface,

A method, and an article produced thereby, of providing a corroson-resistant, scratch-resistant, and stick-resistant, surface on a ferrous-metal-containing article, including forming microcavities in a ferrous-metal-containing article surface by ferritic nitrocarburization and seasoning the surface, including a non-stick agent deposited thereon. In preferred embodiments, the surface of the article including the exposed microcavities is oxidized before seasoning. The article includes cookware. Certain preferred embodiments include forming microcavities by ferritic nitrocarburization wherein the article is heated in an atmosphere including ammonia, nitrogen, and carbon-containing gas to a nitriding temperature of between about 800° F. and about 1300° F. for a time of about 0.5 hours to about 10 hours.

대표청구항 ▼

The invention claimed is: 1. A method of providing a stick-resistant surface on a ferrous-metal-containing culinary article comprising: a) forming microcavities in a ferrous-metal-containing culinary article having a food-contact surface by ferritic nitrocarburization; and b) seasoning the culinary

The invention claimed is: 1. A method of providing a stick-resistant surface on a ferrous-metal-containing culinary article comprising: a) forming microcavities in a ferrous-metal-containing culinary article having a food-contact surface by ferritic nitrocarburization; and b) seasoning the culinary article food-contact surface including depositing thereon a non-stick agent including one or more of the group comprising animal-based cooking oils, plant-based cooking coils and synthetic edible oils and heating the culinary article food-contact surface, thereby providing a stick-resistant surface on the culinary article. 2. The method of claim 1 wherein the culinary article comprises cookware. 3. The method of claim 2 wherein cookware comprises one or more of a pot, pan, frypan, skillet, griddle, wok, double boiler, dutch oven, grill, cooking sheet, cooking pan, burner racks, oven racks, deep-fry baskets, and rotisseries. 4. The method of claim 2 wherein cookware comprises a utensil. 5. The method of claim 2 wherein the culinary article comprises at least about 65% iron. 6. The method of claim 5 wherein the cookware is of a material comprising one or more of cast iron, low and high alloy steels, stainless steels, plain carbon steels and aluminized steels and combinations thereof. 7. The method of claim 1 wherein forming the microcavities by ferritic nitrocarburization comprises heating the culinary article in an atmosphere comprising ammonia, nitrogen, hydrogen and carbon-containing gas to a nitriding temperature of between about 800° F. and about 1300° F. 8. The method of claim 7 wherein forming the microcavities by ferritic nitrocarburization comprises heating the culinary article in an atmosphere comprising ammonia, nitrogen, hydrogen and carbon-containing gas to a nitriding temperature of between about 1000° F. and about 1100° F. 9. The method of claim 8 wherein the atmosphere comprises: between about 35% and about 60% by volume ammonia gas; between about 45% and about 65% by volume nitrogen; and between about 3% and about 8% by volume carbon-containing gas. 10. The method of claim 9 wherein the carbon-containing gas comprises one or more of methane, ethane, butane, pentane, propane, endothermic gas, exothermic gas, carbon monoxide and carbon dioxide. 11. The method of claim 10 wherein the atmosphere is essentially free of elemental oxygen. 12. The method of claim 11 where forming the microcavities by ferritic nitrocarburization is carried out at substantially atmospheric pressure. 13. The method of claim 7 wherein the culinary article is heated at the nitriding temperature for between about 0.5 hours and about 10 hours. 14. The method of claim 13 wherein the culinary article is heated at the nitriding temperature for between about 2 hours and about 4 hours. 15. The method of claim 1 wherein forming the microcavities by ferritic nitrocarburization comprises subjecting the article to ion-nitriding in a partial vacuum. 16. The method of claim 1 wherein forming the microcavities by ferritic nitrocarburization comprises exposing the culinary article to a fluidized bed nitriding furnace in a bed of refractory particles wherein the chamber is pressurized from between about 1 and about 4 bar. 17. The method of claim 1 wherein forming the microcavities by ferritic nitrocarburization comprises subjecting the article to a molten salt bath. 18. The method of claim 17 wherein the molten salt bath comprises cyanide or cynanate salts. 19. The method of claim 1 further comprising the step of oxidizing the culinary article food-contact surface including the microcavities after forming the microcavities in the ferrous-metal-containing article surface by ferritic nitrocarburization. 20. The method of claim 19 wherein oxidizing comprises oxidizing the article with air, steam or warm, moist air for between about 2 minutes and about 30 minutes at between about 500° F. and about 1000° F. 21. The method of claim 20 wherein the oxidizing comprises imparting a black iron oxide film to the culinary article food-contact surface, said film having a thickness of between about 0.3 μm and about 1.3 μm. 22. The method of claim 19 wherein oxidizing comprises: a) submerging the article in a molten salt bath at between about 400° F. and about 1000° F. for a time sufficient to impart a thin black iron oxide film on the surface of the article; and b) rinsing the article. 23. The method of claim 22 wherein the black iron oxide film has a thickness of between about 0.3 μm and about 1.3 μm. 24. The method of claim 1 wherein seasoning comprises: a) applying the non-stick agent to the culinary article food-contact surface; b) heating the applied non-stick agent and said surface for a time sufficient to bond the non-stick agent to the surface; and c) removing any unbonded non-stick agent. 25. The method of 24 wherein applying the non-stick agent comprises applying the non-stick agent in an amount sufficient to fill substantially all of the microcavities. 26. The method of claim 25 wherein the applied non-stick agent and culinary article food-contact surface is heated at a temperature of between about 300° F. and about 500° F. for between about 10 minutes and about 60 minutes. 27. The method of claim 1 wherein plant-based cooking oils comprise olive oil, soybean oil, canola oil, corn oil, sunflower oil, peanut oil, grape seed oil, safflower oil, cashew oil, sesame oil, rice bran oil, and combinations thereof. 28. The method of claim 27 wherein the plant-based cooking oil is grape seed oil. 29. A method of providing a stick-resistant surface on a ferrous-metal-containing article comprising: a) forming microcavities in a ferrous-metal-containing article surface by ferritic nitrocarburization; b) applying a non-stick agent including one or more of the group comprising animal-based cooking oils, plant-based cooking oils and synthetic edible oils to the article surface; and c) heating the applied non-stick agent and article surface for a time sufficient to bond the non-stick agent to the surface and removing any unbonded non-stick agent. 30. The method of claim 29 wherein plant-based cooking oils comprise olive oil, soybean oil, canola oil, corn oil, sunflower oil, peanut oil, grape seed oil, safflower oil, cashew oil, sesame oil, rice bran oil, and combinations thereof. 31. The method of claim 30 wherein the plant-based cooking oil is grape seed oil. 32. The method of claim 29 wherein the ferrous-metal-containing article comprises cookware. 33. The method of claim 32 wherein cookware comprises one or more of a pot, pan, frypan, skillet, griddle, wok, double boiler, dutch oven, grill, cooking sheet, cooking pan, burner racks, oven racks, deep-fry baskets, and rotisseries. 34. The method of claim 32 wherein cookware comprises a utensil. 35. The method of claim 29 wherein the ferrous-metal-containing article comprises at least about 65% iron. 36. The method of claim 35 wherein the ferrous-metal-containing article is of a material comprising one or more of cast iron, low and high alloy steels, stainless steels, plain carbon steels and aluminized steels and combinations thereof. 37. The method of claim 29 further comprising the step of oxidizing the article surface including the microcavities after forming the microcavities in the ferrous-metal-containing article surface by ferritic nitrocarburization. 38. A method of providing a corrosion-resistant, stick-resistant surface on a ferrous-metal-containing cookware article comprising: a) forming microcavities in a cookware article surface by ferritic nitrocarburization; b) applying a non-stick agent including one or more of the group comprising animal-based cooking oils, plant-based cooking oils, and synthetic edible oils to the cookware article surface, thereby providing a non-stick agent film over substantially all of the microcavities deposited thereon and removing any unbonded non-stick agent; and c) heating the applied non-stick agent and cookware article surface at a temperature of between about 300° F. and about 500° F. for between about 10 minutes and about 60 minutes. 39. The method of claim 38 wherein plant-based cooking oils comprise olive oil, soybean oil, canola oil, corn oil, sunflower oil, peanut oil, grape seed oil, safflower oil, cashew oil, sesame oil, rice bran oil and combinations thereof. 40. The method of claim 39 wherein the plant-based cooking oil is grape seed oil. 41. A culinary article comprising: a) a ferrous-metal-containing surface defining microcavities formed therein by ferritic-nitrocarburization; and b) a seasoned non-stick film including one or more of the group comprising animal-based cooking oils, plant-based cooking oils, and synthetic edible oils bonded to the surface of the culinary article, thereby providing a non-stick agent film over substantially all of the microcavities. 42. The culinary article of claim 41 wherein a culinary article comprises pots, pans, frypans, skillets, griddles, woks, grills, double boilers, dutch ovens, forks, knives, spoons, spatulas, cooling sheets, cooking pans, burner racks, deep-fry baskets, rotisserie, whisks, ladles, skimmers, and tongs. 43. The culinary article of claim 41 wherein the ferrous-metal-containing surface has a thickness of at least about 0.025 inch to about 1.0 inch. 44. The culinary article of claim 41 wherein the culinary article comprises at least 65% iron. 45. The culinary article of claim 44 wherein the culinary article comprises one or more of grey cast iron, ductile iron, malleable iron, low and high alloy steels, stainless steel, plain carbon steels, and aluminized steel. 46. The culinary article of claim 41 further comprising an oxidation layer on the surface and the microcavities, wherein the non-stick agent is applied to the oxidation layer. 47. The culinary article of claim 46 wherein the oxidation layer comprises a thin tightly adherent layer comprised substantially of black iron oxide and the oxidation layer has a thickness of between about 0.3 μm and about 1.3 μm.