초록 ▼

A method of producing the low glare, high print gloss paper of the invention comprises the steps of providing a paper substrate, coating the substrate with an aqueous coating composition having, as a dry parts by weight per 100 parts of pigment, 50-90 parts coarse delaminated clay pigment having a p

A method of producing the low glare, high print gloss paper of the invention comprises the steps of providing a paper substrate, coating the substrate with an aqueous coating composition having, as a dry parts by weight per 100 parts of pigment, 50-90 parts coarse delaminated clay pigment having a particle size of 8-12 microns and 10-20 parts calcium carbonate having a particle size of between 0.7 and 1.1 microns, drying the coating; and supercalendering the coated substrate with at least two passes per side with rolls having a surface roughness of 90-130 Ra. The step of supercalendering imparts a Parker Print-Surf roughness of 1.7-2.2 microns and a sheet gloss of about 25-30. Four color printing produces a print gloss of 65-70 and a delta gloss of at least 38.

대표청구항 ▼

What is claimed is: 1. A method of producing a low glare, high print gloss paper, comprising the steps of: providing a paper substrate; coating the substrate at a rate of at least 3 pound per ream of an aqueous coating composition having, as a dry parts by weight per 100 parts of pigment, 50-90 par

What is claimed is: 1. A method of producing a low glare, high print gloss paper, comprising the steps of: providing a paper substrate; coating the substrate at a rate of at least 3 pound per ream of an aqueous coating composition having, as a dry parts by weight per 100 parts of pigment, 50-90 parts coarse delaminated clay pigment having a particle size of 8-12 microns and 10-20 parts calcium carbonate having a particle size of between 0.7 and 1.1 microns, and a binder; drying the coating; and supercalendering the coated substrate with at least two passes per side with rolls having a surface roughness of about 130 micro-inches Ra. 2. A method of producing a low glare, high print gloss paper as in claim 1, wherein the step of supercalendering imparts a Parker Print-Surf roughness of about 1.7-2.2 microns. 3. A method of producing a low glare, high print gloss paper as in claim 1, wherein the step of supercalendering imparts a sheet gloss of about 25-30. 4. A method of producing a low glare, high print gloss paper, comprising the steps of: providing a paper substrate; coating the substrate with a coating composition having, as a dry parts by weight per 100 parts of pigment, 50-90 parts coarse delaminated clay pigment having a particle size of 8-12 microns and 10-20 parts calcium carbonate having a particle size of between 0.7 and 1.1 microns, and a binder; drying the coating; and supercalendering the coated substrate with rough surfaced rolls and passing the substrate through a smoothing nip comprising at least one smooth steel roll to impart to the paper surface a sheet gloss level no greater than 30 and a Parker Print-Surf roughness of 1.8 to 2.2 microns. 5. The method of producing a low glare, high print gloss paper of claim 1 wherein the supercalendering step includes passing the substrate through a smoothing nip comprising at least one smooth steel roll after calendaring with said rolls having a surface roughness of about 130 micro-inches Ra. 6. A method of producing a low glare, high print gloss paper, comprising the steps of: providing a paper substrate; coating the substrate with a coating composition having, as a dry parts by weight per 100 parts of pigment, 50-90 parts coarse delaminated clay pigment having a particle size of 8-12 microns, and a binder; drying the coating; calendering the coated substrate with rough surfaced rolls; and passing the substrate through a smoothing nip comprising at least one smooth steel roll after calendaring with said rough surfaced rolls; said calendering and smoothing steps imparting to the sheet a gloss level no greater than 30 and a Parker Print-Surf roughness of about 1.7 to 2.2 microns. 7. The method of producing a low glare, high print gloss paper of claim 6, wherein said rough surfaced rolls have a surface roughness of about 130 micro-inches Ra.