초록

The present invention provides for a color stable antimicrobial coatings and coating systems comprising a silver ion-exchange type antimicrobial agent. In particular, coatings and coating systems having little, if any, discoloration are provided with no loss of antimicrobial efficacy.

대표청구항 ▼

We claim: 1. A substantially color stable antimicrobial coating system comprising an epoxy resin-based or wax-based coating composition and from about 1 wt. % to about 30 wt. % based on the total solids content of the coating composition of an antimicrobial metal-ion containing, ion-exchange type i

We claim: 1. A substantially color stable antimicrobial coating system comprising an epoxy resin-based or wax-based coating composition and from about 1 wt. % to about 30 wt. % based on the total solids content of the coating composition of an antimicrobial metal-ion containing, ion-exchange type inorganic antimicrobial agent said antimicrobial agent comprising from about 0.1 wt. % to about 25 wt. % silver ions and 0.1 wt. % to about 25 wt. % copper ions, based on the weight of the antimicrobial agent, and wherein the weight ratio of the silver ions to the copper ions is from about 1:10 to about 10:1. 2. The antimicrobial coating system of claim 1 wherein the antimicrobial agent is present in an amount of from about 2 wt. % to about 25 wt. % based on the total solids. 3. The antimicrobial coating system of claim 1 wherein the antimicrobial agent is present in an amount of from about 4 wt. % to about 20 wt. % based on the total solids. 4. The antimicrobial coating system of claim 1 wherein the antimicrobial agent comprises from about 0.3 wt. % to about 15 wt. % silver ions and 0.3 wt. % to about 15 wt. % copper ions, based on the weight of the antimicrobial agent, and wherein the weight ratio of the silver ions to the capper ions is from about 1:5 to about 5:1. 5. The antimicrobial coating system of claim 1 wherein the antimicrobial agent comprises from about 0.3 wt. % to about 15 wt. % silver ions and 0.3 wt. % to about 15 wt. % copper ions, based on the weight of the antimicrobial agent, and wherein the weight ratio of the silver Ions to the copper ions is from about 1:2.5 to about 2.5:1. 6. The antimicrobial coating system of claim 1 wherein the antimicrobial metal ion-containing inorganic antimicrobial agent comprises ion-exchange type ceramic particles. 7. The antimicrobial coating system of claim 6 wherein the ceramic particles are selected from the group consisting of zeolites, hydroxyapatites, and zirconium phosphates. 8. The antimicrobial coating system of claim 6 wherein the ceramic particles are zeolite. 9. The antimicrobial coating system of claim 1 comprising a single coating composition containing the antimicrobial agent. 10. The antimicrobial coating system of claim 1 comprising at least two coating compositions, an epoxy resin-based or wax-based base layer coating composition and a top layer coating composition, wherein at least the base layer coating composition comprises the antimicrobial agent. 11. The antimicrobial coating system of claim 10 wherein both coating compositions comprise the antimicrobial agent. 12. The antimicrobial coating system of claim 11 wherein the base layer coating composition, when cured, is a non-hydrophilic material and the top layer coating composition, when cured, is a (a) hydrophilic material or (b) a non-hydrophilic material that is either (i) skin forming, provided that the thickness of the top coat is such that an adequate number of particles of the antimicrobial agent are not skinned over so as to preclude the presence at the surface of the top coat of an antimicrobially effective amount of the antimicrobial agent, or (ii) non skin forming with respect to the antimicrobial agent. 13. The antimicrobial coating system of claim 12 wherein the top layer coating composition cures to a hydrophilic material that is readily eroded. 14. The antimicrobial coating system of claim 13 wherein the cured hydrophilic material selected from the group consisting of poly(alkylene ether) esters, polyacrylates, polymethacrylates, polyurethanes, polyamides, polyacrylamides, polymethacrylamides, polyvinylpyrrolidinones, polyureas, polysaccharides, polyvinylacetates, polyvinylalcohols, copolymers of the foregoing, copolymers having a substantial presence of hydrophilic monomers used in the foregoing and blends of any two or more of the foregoing. 15. The antimicrobial coating system of claim 1 wherein the coating composition is curable thermoset composition. 16. The antimicrobial coating system of claim 1 further comprising a second antimicrobial agent which is independently selected from the group consisting of metal salts, antimicrobial metal or metal ion containing water soluble glasses, ion-exchange type antimicrobial metal agents and combinations thereof provided that the selected antimicrobial agent at the level used, does not markedly effect discoloration in the cured coating. 17. The antimicrobial coating system of claim 1 wherein the coating composition is an acrylic wax-based coating. 18. The antimicrobial coating system of claim 1 wherein the coating composition is an urethane or polyurethane wax-based coating. 19. The antimicrobial coating system of claim 1 wherein the coating composition is an epoxy novalak resin. 20. The antimicrobial coating system of claim 1 wherein the coating composition is an epoxy polyester resin.