초록 ▼

Alkali-free glasses are disclosed which can be used to produce substrates for flat panel display devices, e.g., active matrix liquid crystal displays (AMLCDs). The glasses contain iron and tin as fining agents, and preferably are substantially free of arsenic and antimony. In certain embodiments, th

Alkali-free glasses are disclosed which can be used to produce substrates for flat panel display devices, e.g., active matrix liquid crystal displays (AMLCDs). The glasses contain iron and tin as fining agents, and preferably are substantially free of arsenic and antimony. In certain embodiments, the glasses are also substantially free of barium. Methods for producing alkali-free glass sheets using a downdraw process (e.g., a fission process) are also disclosed.

대표청구항 ▼

What is claimed is: 1. A method for producing glass sheets that are substantially free of alkali metal oxide by a downdraw process comprising selecting, melting, and fining batch materials so that the glass making up the sheets comprises SiO2, Al2O3, B2O3, MgO, CaO, and SrO, and has: (i) an iron co

What is claimed is: 1. A method for producing glass sheets that are substantially free of alkali metal oxide by a downdraw process comprising selecting, melting, and fining batch materials so that the glass making up the sheets comprises SiO2, Al2O3, B2O3, MgO, CaO, and SrO, and has: (i) an iron content expressed as Fe2O3 in the range of 0.010-0.033 mole percent; and (ii) a tin content expressed as SnO2 in the range of 0.017-0.112 mole percent: wherein: (a) the fining is performed without the use of substantial amounts of either arsenic or antimony; and (b) a population of 50 sequential glass sheets produced by the downdraw process from the melted and fined batch materials has an average gaseous inclusion level of less than 0.05 gaseous inclusions/cubic centimeter, where each sheet in the population has a volume of at least 500 cubic centimeters. 2. A method for producing glass sheets that are substantially free of alkali metal oxides by a downdraw process comprising: (a) selecting batch materials so that the glass making up the sheets comprises SiO2, Al2O3, B2O3, MgO, CaO, and SrO; (b) producing molten glass by melting and fining the batch materials selected in step (a), said fining being performed using at least one fining agent; (c) producing glass sheets using the molten glass of step (b); (d) measuring the iron content expressed as Fe2O3 and the tin content expressed as SnO2 of the glass making up the glass sheets of step (c); and (e) if the iron content measured in step (d) is outside the range of 0.010-0.033 mole percent or if the tin content measured in step (d) is outside the range of 0.017-0.112 mole percent, repeating steps (a) through (d) until the iron content measured in step (d) is in the range of 0.010-0.033 mole percent and the tin content measured in step (d) is in the range of 0.017-0.112 mole percent. 3. The method of claim 2 wherein the fining of step (b) is performed without the use of substantial amounts of either arsenic or antimony. 4. The method of claim 2 or 3 wherein after step (e), a population of 50 sequential glass sheets produced by the downdraw process from the melted and fined batch materials has an average gaseous inclusion level of less than 0.05 gaseous inclusions/cubic centimeter, where each sheet in the population has a volume of at least 500 cubic centimeters.