초록 ▼

The present invention is directed to a rubber compound, such as for use in tires, containing one or more polyoxyalkylene amines, such as to reduce the amount of silane coupling agent conventionally used therein. The presence of the polyoxyalkylene amine(s) allows for the silane coupling agent to be

The present invention is directed to a rubber compound, such as for use in tires, containing one or more polyoxyalkylene amines, such as to reduce the amount of silane coupling agent conventionally used therein. The presence of the polyoxyalkylene amine(s) allows for the silane coupling agent to be present in a low percent by weight of silica without substantially sacrificing the performance characteristics of the rubber compound. In one embodiment, the rubber compound includes 100 phr of a natural elastomer, a synthetic elastomer, or combinations thereof, no less than about 20 phr silica, a silane coupling agent present in an amount no more than 8% by weight of the silica, and about 2 phr to about 10 phr of at least one polyoxyalkylene amine defined by a primary amino group attached to the terminus of a polyether backbone.

대표청구항 ▼

What is claimed is: 1. A rubber compound comprising: 100 parts of an elastomer selected from the group consisting of polybutadiene, polyisoprene, natural rubber, isoprene-butadiene copolymer, emulsion polymerized styrene-butadiene, solution-polymerized styrene-butadiene rubber, and combinations the

What is claimed is: 1. A rubber compound comprising: 100 parts of an elastomer selected from the group consisting of polybutadiene, polyisoprene, natural rubber, isoprene-butadiene copolymer, emulsion polymerized styrene-butadiene, solution-polymerized styrene-butadiene rubber, and combinations thereof, wherein the elastomer is the total elastomer of the rubber compound; silica; a silane coupling agent; at least one polyoxyalkylene amine defined by a primary or secondary amino group attached to the terminus of a polyether backbone; and epoxidized soybean oil. 2. The rubber compound of claim 1 wherein the at least one polyoxyalkylene amine is defined by a primary amino group attached to the terminus of a polyether backbone. 3. The rubber compound of claim 1 wherein the polyoxyalkylene amine is selected from the group consisting of a polyoxyalkylene monoamine, a polyoxyalkylene diamine, and a polyoxyalkylene triamine. 4. The rubber compound of claim 1 wherein the polyoxyalkylene amine is a polyoxyalkylene diamine. 5. The rubber compound of claim 3 wherein the polyoxyalkylene amine is a polyoxyalkylene diamine defined by H2NCH(C2H5)CH2(OCH(C2H5)CH2)nNH2 wherein n is from 1 to about 30. 6. The rubber compound of claim 4 wherein the silane coupling agent is a bis (ω-trialkoxyalkylsilyl) polysulfide, a ω-mercaptoalkyl-trialkoxysilane, or combinations thereof. 7. The rubber compound of claim 1 wherein the polyether backbone is defined by alkylene oxide groups selected from the group consisting of propylene oxide (PO), ethylene oxide (EO), butylene oxide (BO), and mixtures thereof. 8. A tire comprising the rubber compound of claim 1. 9. The rubber compound of claim 1 comprising: no less than 20 phr silica; the silane coupling agent present in an amount no more than 8% by weight of silane coupling agent based on the weight of silica; about 2 phr to about 10 phr of the at least one polyoxyalkylene amine; and about 1 phr to about 10 phr epoxidized soybean oil. 10. The rubber compound of claim 9 wherein the silane coupling agent is present in an amount less than 6% by weight of silica. 11. The rubber compound of claim 9 wherein the silane coupling agent is present in an amount less than 4% by weight of silica. 12. The rubber compound of claim 9 wherein the polyoxyalkylene amine is present in a total amount of from about 4 phr to about 8 phr. 13. The rubber compound of claim 9 wherein the silica is present in an amount from about 40 phr to about 80 phr, the silane coupling agent is present in an amount no more than 6% by weight of the silica, and the polyoxyalkylene amine is a polyoxyalkylene diamine present in an amount from about 4 phr to about 8 phr. 14. The rubber compound of claim 13 wherein the polyoxyalkylene diamine is H2NCH(C2H5)CH2(OCH(C2H5)CH2)nNH2, wherein n is from 1 to about 30. 15. The rubber compound of claim 13 wherein the epoxidized soybean oil is present in an amount from about 3 phr to about 8 phr. 16. A rubber compound comprising: a natural elastomer, a synthetic elastomer, or combinations thereof; silica; a silane coupling agent; and at least one polyoxyalkylene diamine defined by H2NCH(C2H5)CH2 (OCH(C2H5)CH2)nNH2, wherein n is from 1 to about 30. 17. The rubber compound of claim 16 comprising: 100 phr of the natural elastomer, synthetic elastomer, or combinations thereof; no less than 20 phr silica; the silane coupling agent present in an amount no more than 8% by weight of silane coupling agent based on the weight of silica; and about 2 phr to about 10 phr of the at least one polyoxyalkylene diamine. 18. The rubber compound of claim 16 wherein the silane coupling agent is present in an amount less than 6% by weight of silica. 19. The rubber compound of claim 18 wherein the silane coupling agent is present in an amount less than 4% by weight of silica 20. A tire comprising the rubber compound of claim 16.