초록 ▼

UV-crosslinkable acrylic hotmelt pressure sensitive adhesives comprising acrylic and vinyl monomers, and a polymerizable UV photoinitiator. The photoinitiator comprises a spacer comprising both ethylene oxide and urethane, or urea, carbonate, or siloxane functional groups. The ethylene oxide is dire

UV-crosslinkable acrylic hotmelt pressure sensitive adhesives comprising acrylic and vinyl monomers, and a polymerizable UV photoinitiator. The photoinitiator comprises a spacer comprising both ethylene oxide and urethane, or urea, carbonate, or siloxane functional groups. The ethylene oxide is directly bonded to the chromophore (e.g., benzophenone) moiety, while the urethane (or urea, carbonate, siloxane) is closely linked to the polymerizable moiety (e.g., styrenic C═C double bond).

대표청구항 ▼

The invention claimed is: 1. A photoinitiator having the structural formula where Z is S, O, CH2, or NH, R1-8 are independently H, Cl, Br, I, F, C1-24 alkoxy, C1-24 alkyl, or aryl; and wherein at least one of R1-8 must comprise a —W—X—Y group, where W is a C1-12 oxyalkylene

The invention claimed is: 1. A photoinitiator having the structural formula where Z is S, O, CH2, or NH, R1-8 are independently H, Cl, Br, I, F, C1-24 alkoxy, C1-24 alkyl, or aryl; and wherein at least one of R1-8 must comprise a —W—X—Y group, where W is a C1-12 oxyalkylene, X comprises tetramethyldisiloxane, and Y is —R9—C(R10)═CH2, where R9 is a linear or branched C2-10 alkylene or C2-10oxyalkylene, or arylene or derivative thereof, and R10 is H or CH3. 2. A photoinitiator having the structural formula where n=1-12. 3. The photoinitiator of claim 2 wherein n=1. 4. A photoinitiator having the structural formula where n=1-12. 5. The photoinitiator of claim 4 wherein n=1. 6. A photoinitiator having the structural formula 7. A UV curable acrylic polymer comprising the following monomer components: (a) from about 70 to about 95 parts by weight of acrylic or methacrylic acid derivative of the formula CH2═CH(R1)(COOR2), where R1 is H or CH3 and R2 is a C1-20 alkyl chain, (b) 0 to about 30 parts by weight of an acrylic or methacrylic acid derivative of the formula CH2═CH(R1)(COOR2), where R1 is H or CH3 and R2 is an hydroxyl-functional C1-20 alkyl chain, (c) 0 to about 20 parts by weight of an acrylic or vinyl compound containing a carboxy or anhydride functional group, (d) 0 to about 30 parts by weight of acrylic or vinyl compounds containing an amine, amide, urethane, epoxide or isocyanate functional group and (e) from about 0.01 to about 15 parts by weight of a photoinitiator having the structural formula where n=1-12. 8. A UV curable acrylic polymer comprising the following monomer components: (a) from about 70 to about 95 parts by weight of acrylic or methacrylic acid derivative of the formula CH2═CH(R1)(COOR2), where R1 is H or CH3 and R2 is a C1-20 alkyl chain, (b) 0 to about 30 parts by weight of an acrylic or methacrylic acid derivative of the formula CH2═CH(R1)(COOR2), where R1 is H or CH3 and R2 is an hydroxyl-functional C1-20 alkyl chain, (c) 0 to about 20 parts by weight of an acrylic or vinyl compound containing a carboxy or anhydride functional group, (d) 0 to about 30 parts by weight of acrylic or vinyl compounds containing an amine, amide, urethane, epoxide or isocyanate functional group and (e) from about 0.01 to about 15 parts by weight of a photoinitiator having the structural formula where n=1-12. 9. A UV curable acrylic polymer comprising the following monomer components: (a) from about 70 to about 95 parts by weight of acrylic or methacrylic acid derivative of the formula CH2═CH(R1)(COOR2), where R1 is H or CH3 and R2 is a C1-20 alkyl chain, (b) 0 to about 30 parts by weight of an acrylic or methacrylic acid derivative of the formula CH2═CH(R1)(COOR2), where R1 is H or CH3 and R2 is an hydroxyl-functional C1-20 alkyl chain, (c) 0 to about 20 parts by weight of an acrylic or vinyl compound containing a carboxy or anhydride functional group, (d) 0 to about 30 parts by weight of acrylic or vinyl compounds containing an amine, amide, urethane, epoxide or isocyanate functional group and (e) from about 0.01 to about 15 parts by weight of a photoinitiator having the structural formula 10. A UV curable hot melt pressure sensitive adhesive comprising (a) from about 70 to about 95 parts by weight of methyl acrylate, methyl methacrylate, n-butyl acrylate, 2-ethylhexyl acrylate, and/or isooctyl acrylate, (b) 0 to about 30 parts by weight of hydroxyethyl acrylate and/or hydroxypropyl acrylate, (c) 0 to about 20 parts by weight of acrylic acid or maleic anhydride, (d) 0 to about 30 parts by weight of 1 -vinyl-2-pyrrolidinone (NVP), t-octyl acrylamide, 2-(tert-butylamino)ethyl methacrylate (t-BAEM), acrylamide, glycidyl methacrylate, 3-Isopropenyl-α, α-dimethylbenzyl isocyanate (m-TMI®), or a compound of the following formula and (e) from about 0.01 to about 15 parts by weight of a photoinitiator selected from the group consisting of and where n=1-12. 11. The adhesive of claim 10 wherein component (e) of the acrylic polymer is where n=1-12. 12. The adhesive of claim 10 wherein component (e) of the acrylic polymer is where n=1-12. 13. The adhesive of claim 10, wherein component (e) of the acrylic polymer is