초록 ▼

The invention provides a preform insulating end cone suitable for forming the end cone of a pollution control device. The preform insulating end cone includes a cone shaped intumescent or non-intumescent sheet material. The sheet material has a plurality of slits enabling the sheet material to be co

The invention provides a preform insulating end cone suitable for forming the end cone of a pollution control device. The preform insulating end cone includes a cone shaped intumescent or non-intumescent sheet material. The sheet material has a plurality of slits enabling the sheet material to be cone shaped. A shape retaining element is in intimate contact with the intumescent sheet material. The shape retaining element enables the intumescent sheet material to maintain a cone shape. The invention also provides methods of making preform insulating end cones of the invention.

대표청구항 ▼

What is claimed is: 1. A method of making a pollution control device, said method comprising: forming a flexible and self-supporting insulating end cone comprising a single, continuous piece of resilient and compressible non-intumescent insulating material, the insulating material comprising inorga

What is claimed is: 1. A method of making a pollution control device, said method comprising: forming a flexible and self-supporting insulating end cone comprising a single, continuous piece of resilient and compressible non-intumescent insulating material, the insulating material comprising inorganic fibers and an organic binder, and the insulating end cone having a three dimensional cone shape, where said forming comprises shaping non-intumescent insulating material into the three dimensional cone shape using a mold; and disposing the insulating end cone within a gap between inner and outer end cone housings of the pollution control device, wherein the insulating end cone is dimensioned so as to fill the gap between the end cone housing, such that there is no air space between the insulating end cone and either end cone housing, the insulating end cone maintains its three dimensional cone shape under the force of gravity, when placed on a level surface prior to said disposing, and the insulating end cone exhibits a resiliency value of about 35 to about 97 percent when evaluated using the Resiliency Test Method. 2. The method according to claim 1, wherein prior to said disposing step, the single, continuous piece of non-intumescent insulating material is compressed by a factor of 1 to 10. 3. The method according to claim 2, wherein the single, continuous piece of non-intumescent insulating material is physically compressed by resin bonding. 4. A method of making a self-supporting insulating end cone having a three dimensional cone shape, said method comprising: forming a flexible and self-supporting insulating end cone comprising a single, continuous piece of resilient and compressible non-intumescent insulating material, the insulating material comprising inorganic fibers and an organic binder, and the insulating end cone having a three dimensional cone shape, where said forming comprises shaping non-intumescent insulating material into the three dimensional cone shape using a mold, wherein the insulating end cone is dimensioned so as to fill the gap between an inner and outer end cone housing of a pollution control device, such that there is no air space between the insulating end cone and either end cone housing, the insulating end cone maintains its three dimensional cone shape under the force of gravity, when placed unsupported on a level surface, and the insulating end cone exhibits a resiliency value of about 35 to about 97 percent when evaluated using the Resiliency Test Method. 5. The method according to claim 4, wherein the non-intumescent insulating material is compressible by a factor of 1 to 10. 6. The method according to claim 4, wherein the insulating material further comprises an inorganic filler. 7. The method according to claim 4, wherein the insulating material further comprises from about 60 to about 98 dry weight percent inorganic fiber and from about 2 to about 25 dry weight percent organic binder. 8. The method according to claim 7, wherein the insulating material further comprises about 90 percent inorganic fiber and about 10 percent organic binder. 9. The method according to claim 4, wherein the insulating material further comprises one or more inorganic binders. 10. The method according to claim 1, wherein the insulating end cone has a wall thickness of from about 0.5 to about 15 mm. 11. The method according to claim 4, wherein the insulating end cone has a wall thickness of from about 0.5 to about 15 mm. 12. The method according to claim 4, wherein the insulating material comprises essentially shot-free ceramic fibers that contain less than 5 percent by weight of shot or non-fibrous particulate material. 13. The method according to claim 4, wherein the insulating material comprises essentially shot-free ceramic fibers that contain less than 1 percent by weight of shot or non-fibrous particulate material. 14. The method according to claim 12, wherein the essentially shot-free ceramic fibers are selected from the group consisting of alumina-boria-silica fibers, alumina-silica fibers, alumina-phosphorus pentoxide fibers, zirconia-silica fibers, zirconia-alumina fibers, and alumina fibers. 15. The method according to claim 2, wherein the insulating end cone is compressed to a mount density of about 0.05 and 0.60 grams per cubic centimeter such that the insulating material is able to repeatedly undergo a reduction in thickness while hot and spring back to substantially its original thickness when cooled. 16. The method according to claim 5, wherein insulating material has a density in the range of 0.05 to 0.30 grams per cubic centimeter and is able to repeatedly undergo a reduction in thickness while hot and spring back to substantially its original thickness when cooled. 17. The method according to claim 4, wherein the inorganic fibers comprise at least one of polycrystalline alumina fiber and refractory ceramic fiber. 18. The method according to claim 4, wherein the organic binder is selected from the group consisting of emulsions of organic polymers, elastomers in latex form, natural rubber lattices, styrene-butadiene lattices, butadiene acrylonitrile lattices, lattices of acrylate, methacrylate polymers and copolymers, thermoplastic polymers and polymer resins, natural rubber, styrene-butadiene rubber, other elastomeric polymer resins, acrylic latex and polyvinyl acetate.