In order to synthesize semi-interpenetrating polymer networks (semi-IPNs) with molecular sieve characteristics, polyetherimide/bismaleimide (PEI/BMI) chromophore composites were made through sol-gel technique. A tunable and compatible chemical structure with fine morphology was obtained through in s
In order to synthesize semi-interpenetrating polymer networks (semi-IPNs) with molecular sieve characteristics, polyetherimide/bismaleimide (PEI/BMI) chromophore composites were made through sol-gel technique. A tunable and compatible chemical structure with fine morphology was obtained through in situ controlled sol-gel polymerization, crosslinking, chemical modification and membrane fabrication. The novel semi-IPN, synthesized and assembled by using ethanol as polar protic modifier and pore former, had a superior structure and morphology suitable for making gas separation membranes. These semi-IPN membranes gave fifteen times higher gas flux without significant decrease in their gas permselectivity than membranes prepared from pure PEL The chemical structures of these novel semi-IPNs were characterized by using FTIR, XPS and SEM. It was discovered for the first time that in situ simultaneous ethoxylation, anionic polymerization of BMI and imide modifications were responsible for creating the new chemical structure and molecular morphology that was different from traditional BMI resins. In addition to the superior structure, this chemical processes have the advantages of using simple green chemistry, ambient temperature and does not require initiators for polymerization.
대표청구항▼
The invention claimed is: 1. A semi-interpenetrating polymer network(IPN), comprising a homogeneous blend of in situ polymerized BMI monomer within a glassy thermoplastic PEI polymer having an electron acceptor group, and having the structure wherein represents a connection to the rest of the
The invention claimed is: 1. A semi-interpenetrating polymer network(IPN), comprising a homogeneous blend of in situ polymerized BMI monomer within a glassy thermoplastic PEI polymer having an electron acceptor group, and having the structure wherein represents a connection to the rest of the molecule. 2. A polymer network according to claim 1, wherein the BMI to PEI weight ratio is from 0.1 to 25%. 3. A process for the preparation of a semi-interpenetrating polymer network(IPN), comprising a homogeneous blend of in situ polymerized BMI monomer within a glassy thermoplastic polymer having an electron acceptor group, the process comprising (a) dissolving a BMI monomer and a glassy thermoplastic polymer having an electron acceptor group in a dipolar aprotic solvent and including ethyl alcohol, and (b) in situ polymerizing the BMI monomer within the thermoplastic polymer at ambient temperature and pressure while mixing to provide a homogeneous solution, for a time sufficient to polymerize, but not so long as to result in phase separation of the BMI and thermoplastic polymers. 4. A process according to claim 3, wherein phase separation is indicated by formation of an opaque solution. 5. A process according to claim 4, wherein the thermoplastic polymer is PEI or polysulfone. 6. A process according to claim 5, wherein the thermoplastic polymer is PEI. 7. A process according to claim 5, wherein the reaction time is up to 80 days. 8. A process according to claim 6, wherein the reaction time is 11 to 24 days under ambient light. 9. A process according to claim 8, wherein the solvent is NMP. 10. A process according to claim 9, wherein ethyl alcohol is provided in an amount of ⅕ of the solvent weight. 11. A process according to claim 10, wherein the BMI to PEI weight ratio is 0.1 to 25%. 12. A process according to claim 11, which includes the additional step of casting the homogeneous polymer solution on a flat surface and immersing in water, before any phase separation takes place to provide a fine membrane surface structure having dispersed thermosetting polymer phase of less than 1 micron in diameter. 13. A process according to claim 12, wherein the homogeneous polymer solution contains 25-35%(w/w) of polymer. 14. A process according to claim 12, wherein the homogeneous polymer solution contains 19 to 19.5%(w/w) of polymer. 15. A gas separation membrane, cast from a homogeneous polymer solution containing a semi-interpenetrating polymer network(IPN) according to claim 1. 16. A membrane according to claim 15, for separation of CO2 from a mixture of CO2 and CH4, or from a mixture of CO2 and N2. 17. A process for separation of CO2 from a mixture of CO2 and CH4, or from a mixture of CO2 and N2, with a gas separation membrane according to claim 15, including increasing permselectivity of the membrane by increasing CO2 feed concentration. 18. A polymer network according to claim 1, wherein the BMI to PEI weight ratio is 0.2 to 11%. 19. A process according to claim 11, wherein the BMI to PEI weight ratio is 0.2 to 11%. 20. A process according to claim 9, wherein the homogenous polymer solution contains 29% (w/w) of polymers.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (7)
Don Roderic C. (Newark DE) Gillespie ; Jr. John W. (Hockessin DE) McKnight Steven H. (Dover DE), Bonding techniques for high performance thermoplastic compositions.
Yamasaki, Kazuyuki; Yamamoto, Kimio; Watanabe, Masanobu; Kan, Kojiro; Nakayama, Yoshio, Membrane filter material having excellent organic solvent resistance, method for formation of membrane filter and process for preparation of bismaleimide polymer to be used for membrane filter.
Pater Ruth H. ; Hansen Marion G., Process for controlling morphology and improving thermal mechanical performance of high performance interpenetrating and.
Liu, Kunlei; Frimpong, Reynolds A.; Liu, Kun, Hybrid process using a membrane to enrich flue gas CO2 with a solvent-based post-combustion CO2 capture system.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.