The present invention provides a method for producing a water absorbing agent which excels in water absorption properties. In detail, the present invention provides a method for the production of a water absorbing agent, comprising a) a step of mixing a water absorbing resin, water, and a mixing aid
The present invention provides a method for producing a water absorbing agent which excels in water absorption properties. In detail, the present invention provides a method for the production of a water absorbing agent, comprising a) a step of mixing a water absorbing resin, water, and a mixing aid without adding a water-soluble radical polymerization initiator and an ethylenically unsaturated monomer and b) a step of irradiating the resultant mixture with ultraviolet rays while keeping the mixture with flowed state.
대표청구항▼
The invention claimed is: 1. A method for the production of a water absorbing agent, comprising a) a step of mixing a water absorbing resin, water, and a mixing aid without adding a water-soluble radical polymerization initiator and an ethylenically unsaturated monomer and b) a step of irradiating
The invention claimed is: 1. A method for the production of a water absorbing agent, comprising a) a step of mixing a water absorbing resin, water, and a mixing aid without adding a water-soluble radical polymerization initiator and an ethylenically unsaturated monomer and b) a step of irradiating the resultant mixture with ultraviolet rays while keeping the mixture in a flowing state. 2. A method according to claim 1, wherein the amount of the water to be mixed is not less than 1 weight part and less than 50 weight parts based on 100 weight parts of the water absorbing resin. 3. A method according to claim 1, wherein the mixing aid is at least one compound selected from the group consisting of surfactants, water-soluble polymer, hydrophilic organic solvents, water-soluble inorganic compounds, inorganic acid salts, and organic acid salts. 4. A method according to claim 1, wherein the mixing aid is added in an amount not less than 0.01 weight parts and less than 50 weight parts, based on 100 parts by weight of the water absorbent resin. 5. A method according to claim 1, wherein the mixing aid is mixed in the form of an aqueous solution with the water absorbing resin. 6. A method according to claim 5, wherein the aqueous solution has a surface tension in the range of 40 dynes/cm-75 dynes/cm. 7. A method according to claim 3, wherein the surfactant is polyoxyethylene alkyl ether. 8. A method according to claim 3, wherein the surfactant is polyethylene glycol. 9. A method according to claim 3, wherein the water-soluble inorganic compound is a water-soluble metal salt. 10. A method according to claim 1, wherein the water absorbing resin contains particles of a particle diameter of not less than 150 μm and less than 850 μm in a ratio amount in the range of 90 weight %-100 weight % of all the particles therein and has a weight average particle diameter (D50) of not less than 300 μm and less than 500 μm and a logarithmic standard deviation (σç) of particle distribution in the range of 0.20-0.45. 11. A method according to claim 1, wherein the absorbency of physiological saline against pressure of 2.07 kPa of the water absorbing agent is not less than 15 g/g and less than 50 g/g and is exalted by at least 1 g/g comparing with that of the water absorbing resin. 12. A method according to claim 1, wherein the water absorbent resin has an acid group and a neutralization ratio (mol % of the neutralized acid group in the whole acid group) in the range of 50-95 mol %. 13. A method according to claim 1, wherein the eluted soluble content of the water absorbing agent is not less than 0.1 weight parts and less than 30 weight parts, based on 100 weight parts of the water absorbing resin. 14. A method according to claim 1, wherein the irradiation with the ultraviolet rays is carried out under application of heat. 15. A method according to claim 1, wherein the water absorbing resin is obtained by polymerizing a monomer having acrylic acid (salt) as a main component thereof. 16. A method according to claim 1, wherein the water absorbing resin is obtained by preparing a water absorbing resin precursor having a low neutralization ratio and mixing the water absorbing resin precursor with a base. 17. A method according to claim 2, wherein the mixing aid is at least one compound selected from the group consisting of surfactants, water-soluble polymer, hydrophilic organic solvents, water-soluble inorganic compounds, inorganic acid salts, and organic acid salts. 18. A method according to claim 2, wherein the mixing aid is added in an amount not less than 0.01 weight parts and less than 50 weight parts, based on 100 parts by weight of the water absorbent resin. 19. A method according to claim 3, wherein the mixing aid is added in an amount not less than 0.01 weight parts and less than 50 weight parts, based on 100 parts by weight of the water absorbent resin. 20. A method according to claim 2, wherein the mixing aid is mixed in the form of an aqueous solution with the water absorbing resin. 21. A method according to claim 3, wherein the mixing aid is mixed in the form of an aqueous solution with the water absorbing resin.
Tian, Gonglu; Ondisco, Matthew Thomas; Bergman, David L.; Messner, Bernfried; Smith, Scott J., Particulate superabsorbent polymer composition having improved stability.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.