Methods and systems for preparing gypsum slurry containing a cellulose ether
IPC분류정보
국가/구분
United States(US) Patent
등록
국제특허분류(IPC7판)
B28B-001/26
B27N-003/00
A61K-009/127
B01J-013/02
B01J-013/04
C04B-016/08
C04B-020/00
C04B-038/00
C04B-009/04
C04B-011/00
C04B-028/14
출원번호
UP-0811479
(2007-06-11)
등록번호
US-7803296
(2010-10-21)
발명자
/ 주소
Miller, David Paul
Liu, Qingxia
Yu, Qiang
출원인 / 주소
United States Gypsum Company
대리인 / 주소
Greer, Burns & Crain, Ltd.
인용정보
피인용 횟수 :
8인용 특허 :
33
초록▼
A method for forming a gypsum slurry comprises the steps of combining gypsum and water to form a slurry, combining cellulose ether with at least a second material configured to delay solubilization of the cellulose ether, and adding the combined cellulose ether and at least a second material to the
A method for forming a gypsum slurry comprises the steps of combining gypsum and water to form a slurry, combining cellulose ether with at least a second material configured to delay solubilization of the cellulose ether, and adding the combined cellulose ether and at least a second material to the slurry.
대표청구항▼
What is claimed is: 1. A method for preparing a gypsum slurry useful for making a gypsum board product comprising the steps of: obtaining calcined gypsum and water in the form of a slurry; preparing an emulsion of cellulose ether as a dispersed phase with at least a second material as a continuous
What is claimed is: 1. A method for preparing a gypsum slurry useful for making a gypsum board product comprising the steps of: obtaining calcined gypsum and water in the form of a slurry; preparing an emulsion of cellulose ether as a dispersed phase with at least a second material as a continuous phase, said emulsion being configured to delay solubilization of said cellulose ether; and adding said emulsion to said slurry, wherein said cellulose ether is solid and wherein said at least a second material comprises water at an elevated temperature selected to maintain said cellulose ether in solid form. 2. A method for preparing the gypsum slurry as defined by claim 1, wherein the obtaining step further comprises combining calcined gypsum and water to form a slurry in a mixer, and wherein the method further comprises the steps of: depositing said slurry on a moving receiver downstream from said mixer; and wherein said preparing step results in the emulsion whereby said cellulose ether is solubilized in said slurry only after said slurry has been deposited on said moving receiver. 3. A method for preparing the gypsum slurry as defined by claim 2 wherein the method is substantially continuous, and wherein the method further includes the steps of using at least one sensor to measure at least one physical property of said slurry at a location downstream from said mixer, and changing one or more of the quantity and quality of said emulsion being added to said slurry in response to a change in said slurry at least one physical property. 4. A method for preparing the gypsum slurry as defined by claim 1 wherein: said cellulose ether comprises one or more of ethyl cellulose, propyl cellulose, hydroxypropyl cellulose, and methyl cellulose; and said cellulose ether is provided in a weight ratio of between about 0.3 to 2 parts cellulose ether per about 99.7 to about 98 parts dry calcined gypsum. 5. A method for preparing the gypsum slurry as defined by claim 1 and further including the step of adding a foam to said slurry, and wherein the step of adding said emulsion to said slurry is performed after or simultaneous with the step of adding said foam to said slurry. 6. A method for making the gypsum slurry as defined by claim 1 wherein the method is further for making a gypsum board product, wherein the obtaining step further comprises combining water and said gypsum in a mixer, and wherein the method further comprises the steps of: depositing said slurry on a moving receiver downstream from said mixer; and wherein said emulsion releases said dispersed phase cellulose ether into said slurry after said slurry has been deposited on said moving receiver. 7. A method for making the gypsum slurry as defined by claim 1 wherein said emulsion comprises an inverted emulsion, wherein the method is further for making a gypsum board product, wherein the obtaining step further comprises combining water and said calcined gypsum in a mixer, and wherein the method further comprises the steps of: depositing said slurry on a moving receiver; and removing excess water from said slurry after depositing said slurry on said moving receiver resulting in a change in the surface tension of said slurry, and wherein said inverted emulsion reverses phases whereby said dispersed phase cellulose ether is released into said slurry as a result of said change in said surface tension. 8. A method for making the gypsum slurry as defined by claim 7 wherein the step of removing excess water comprises removing excess water through one or more of drying said slurry or allowing said calcined gypsum to absorb said excess water. 9. A method for preparing a a fiberboard product, comprising: mixing gypsum dihydrate with water to form a slurry; adding a cellulosic fiber to said slurry; heating said slurry under pressure to convert said gypsum dihydrate to a hemihydrate; preparing an emulsion of cellulose ether as a dispersed phase with at least a second material as a continuous phase, said emulsion being configured to delay solubilization of said cellulose ether; transferring said slurry to a headbox; and transferring said slurry from said headbox to one or more presses; and, adding said emulsion to said slurry at said headbox; and wherein said emulsion releases said dispersed phase cellulose ether into said slurry after said slurry has been transferred to said one or more presses. 10. A method for making the gypsum fiberboard product as defined by claim 9 wherein said emulsion comprises an inverted emulsion, and further comprising the steps of: reducing the excess water content of said slurry while said slurry is in said one or more presses wherein the surface tension of said slurry changes; and, wherein said inverted emulsion reverses phases when said surface tension sufficiently changes in said one or more presses. 11. A method for preparing the slurry as defined by claim 9 wherein said one or more presses comprise a drying press followed by a setting press, and wherein said emulsion releases said dispersed phase cellulose ether primarily in said setting press. 12. A method for preparing the slurry as defined by claim 1 wherein the board product is a wallboard and wherein the method is further for making the wallboard product, wherein the obtaining step comprises mixing gypsum hemihydrate with water in a mixer, wherein the step of adding said emulsion to said slurry is performed in said mixer, and further including the steps of: transferring said slurry from said mixer onto a first continuous sheet of wallboard facing material being carried on a conveyor; depositing a second continuous sheet of wallboard facing material on said deposited slurry to define the wallboard; drying said wallboard in at least one of a kiln or oven, and, configuring said emulsion to release said cellulose ether into said slurry while said wallboard is dried in said at least one of a kiln or oven. 13. A method for preparing the gypsum slurry as defined by claim 1 wherein the method is further for making a gypsum board product, wherein the obtaining step further comprises combining said gypsum with said cellulose ether in a mixer, the method further comprising the step of depositing said slurry on a moving receiver downstream from said mixer, wherein said slurry in said mixer is at a first temperature, and wherein said elevated temperature is greater than said first temperature and is selected to substantially prevent said cellulose ether from solubilizing in said slurry until said slurry has been deposited on said moving receiver. 14. A method for preparing the gypsum slurry as defined by claim 1 wherein the method is continuous, wherein the obtaining step is performed using a first water supply, wherein the step of combining said cellulose ether with said at least a second material is performed using a second water supply configured to provide said water at a temperature of at least about 150° F. (66° C.). 15. A method for preparing the gypsum slurry as defined by claim 14 wherein said second supply comprises a bypass from said first supply, wherein said temperature is at least about 160° F. (71° C.), and further comprising using a heat exchanger to heat said second water supply passing through said bypass to said second water supply temperature. 16. A method for preparing the gypsum slurry as defined by claim 1 wherein the method is carried out continuously, wherein the obtaining step is performed in a mixer and wherein said water is introduced into said mixer through use of a plurality of nozzles, wherein said emulsion is introduced into said mixer using no more than about half of said plurality of nozzles, and wherein said water is heated to a temperature of at least about 160° F. (71° C.) prior to combining with said cellulose ether. 17. A method for preparing the gypsum slurry as defined by claim 1 wherein said cellulose ether material is a solid, and wherein said elevated temperature is at least about 180° F. (82° C.), and wherein said obtaining step is performed using an eductor communicating with said mixer. 18. A method for preparing a gypsum slurry, comprising: obtaining calcined gypsum and water in the form of a slurry; preparing an emulsion of cellulose ether as a dispersed phase with at least a second material as a continuous phase, said emulsion being configured to delay solubilization of said cellulose ether; adding said emulsion to said slurry; and adding a cross linker to said slurry, wherein said cross linker comprises said at least a second material, wherein said methyl cellulose and said cross linker are solids, and wherein the step of combining said cellulose ether with said at least a second material comprises causing said particles of solid cellulose ether to adhere to particles of said cross linker. 19. A method for preparing the gypsum slurry as defined by claim 18 wherein said cellulose ether comprises a powder and wherein the step of combining said methyl cellulose with said cross linker comprises spray coating said cellulose ether with said cross linker. 20. A method for preparing the gypsum slurry as defined by claim 18 wherein said cross linker solubilizes in said gypsum slurry earlier than said methyl cellulose. 21. A method for preparing the gypsum slurry as defined by claim 18 wherein said cross linker is provided in a weight ratio of between about 0.05-0.5% in said slurry. 22. A method for preparing the gypsum slurry as defined by claim 18 wherein the step of adding said cross linker comprises adding said cross linker as the dispersed phase in said emulsion, and further includes the step of depositing said slurry on a moving receiver, and wherein said emulsion is configured to release said cross linker into said slurry after said slurry has been deposited on said moving receiver.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (33)
Redelius Gsta (Nynshamn SEX), Bitumen emulsion and its use.
Sucech Steven W. (Lake Villa IL) Hinshaw Stewart E. (Sweetwater TX) Nemeth Bradley S. (Bedford IN) Buster Kip R. (Burlington IA), Method for preparing uniformly foamed gypsum product with less foam agitation.
Sang, Yijun; Song, Weixin D.; Chan, Cesar; Lee, Chris C., Method of preparing pregelatinized, partially hydrolyzed starch and related methods and products.
Sang, Yijun; Lee, Chris C.; Chan, Cesar; Song, Weixin David, Pregelatinized starch with mid-range viscosity, and product, slurry and methods related thereto.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.