초록 ▼

A cutting tool made of surface-coated cubic boron nitride-based ultrahigh pressure sintered material, comprising a cutting insert main body formed by ultrahigh pressure sintering of compact composed of titanium nitride, aluminum and/or aluminum oxide, and boron nitride, and a hard coating layer vapo

A cutting tool made of surface-coated cubic boron nitride-based ultrahigh pressure sintered material, comprising a cutting insert main body formed by ultrahigh pressure sintering of compact composed of titanium nitride, aluminum and/or aluminum oxide, and boron nitride, and a hard coating layer vapor deposited on the main body. The main body has a texture containing cubic boron nitride, titanium nitride and reaction product. The hard coating layer has a lower layer of composite nitride having a composition of [Ti1-XAlX]N, where X is in a range from 0.40 to 0.60 in an atomic ratio, and the upper layer comprises a thin layer A having the composition of [Ti1-XAlX]N, where X is in a range from 0.40 to 0.60 in an atomic ratio, and a thin layer B consisting of a Ti nitride (TiN). The upper layer has a consisting of the thin layer A and a thin layer B layered alternately.

대표청구항 ▼

What is claimed is: 1. A cutting tool made of surface-coated cubic boron nitride-based ultrahigh pressure sintered material, comprising:a main body consisting of ultrahigh pressure sintered material formed by ultrahigh pressure sintering of a compact having a composition of, in mass %, 13 to 30% of

What is claimed is: 1. A cutting tool made of surface-coated cubic boron nitride-based ultrahigh pressure sintered material, comprising:a main body consisting of ultrahigh pressure sintered material formed by ultrahigh pressure sintering of a compact having a composition of, in mass %, 13 to 30% of titanium nitride, 6.5 to 18% of aluminum and/or aluminum oxide and a balance of boron nitride,under an observation using a scanning electron microscope, the main body showing a texture such that an ultrahigh pressure sintering reaction product is present at the interface between a cubic boron nitride phase constituting a disperse phase and a titanium nitride phase constituting a continuous phase; anda hard coating that is vapor-deposited on the surface of the main body and has a lower layer of an average layer thickness in a range from 1.5 to 3 μm and an upper layer of an average layer thickness in a range from 0.3 to 3 μm, wherein:surface roughness Ra of the main body is 0.05 or more and 1.0 or less;the lower layer of the hard coating layer consists of a vapor-deposited composite nitride of Ti and Al having the composition of [Ti1-XAlX]N, where X is in a range from 0.40 to 0.60 in an atomic ratio; andthe upper layer of the hard coating layer is vapor-deposited on the surface of the lower layer, having thin layers A consisting of a composite nitride of Ti and Al having the composition of [Ti1-XAlX]N, where X is in a range from 0.40 to 0.60 in an atomic ratio, and thin layers B consisting of a Ti nitride (TiN), and has a structure in which the thin layers A and the thin layers B are layered alternately such that an average layer thickness of each single thin layer A is in a range of 0.05 to 0.3 μm, an average layer thickness of each single thin layer B is in a range of 0.05 to 0.3 μm,wherein the hard coating further comprises a titanium nitride layer of 0.01 to 0.5 μm in thickness interposed between the main body and the lower layer.