The present invention refers to a multilayer heat shrinkable film characterized by a combination of desirable properties, such as high shrinkage, good optical properties, excellent sealability and stack sealability. The invention further is directed to a method of producing said film. The invention
The present invention refers to a multilayer heat shrinkable film characterized by a combination of desirable properties, such as high shrinkage, good optical properties, excellent sealability and stack sealability. The invention further is directed to a method of producing said film. The invention is further directed to the use of said film or bags and pouches made therefrom for packaging goods as for example food products. The invention also refers to tubes made with the film.
대표청구항▼
1. A multi-layer heat shrinkable film comprising at least an anti-sealing coating layer, an outer layer and an inner sealing layer, the film having a shrinkage of at least 10% measured according to ASTM 2732 in water at 90° C. in at least one of MD, TD directions, where the coating layer has been ap
1. A multi-layer heat shrinkable film comprising at least an anti-sealing coating layer, an outer layer and an inner sealing layer, the film having a shrinkage of at least 10% measured according to ASTM 2732 in water at 90° C. in at least one of MD, TD directions, where the coating layer has been applied onto the outer layer of the film by solution coating, the outer layer comprises polystyrene homopolymer and/or copolymer, and wherein the coating layer provides an anti-sealing effect and is a radiation curable coating. 2. A multi-layer heat shrinkable film comprising at least an anti-sealing coating layer, an outer layer and an inner sealing layer, the film having a shrinkage of at least 10% measured according to ASTM 2732 in water at 90° C. in at least one of MD, TD directions, where the coating layer has been applied onto the outer layer of the film by solution coating, the outer layer comprises polystyrene homopolymer and/or copolymer, and wherein the coating layer provides an anti-sealing effect and comprises nitrocellulose, one or more polyamides, a blend of nitrocellulose and polyamides, polyvinyl butyral, or nitrocellulose and polyurethane based plasticizer. 3. A multi-layer heat shrinkable film comprising at least an anti-sealing coating layer, an outer layer and an inner sealing layer, the film having a shrinkage of at least 40 percent in both machine and transverse directions measured according to ASTM 2732 in water at 90° C., where the coating layer has been applied onto the outer layer of the film by solution coating, the outer layer comprises polystyrene homopolymer and/or copolymer, and wherein the coating layer provides an anti-sealing effect. 4. The film of claim 1, 2 or 3, wherein the coating applied to the outer surface is substantially transparent. 5. The film of claim 1, 2, or 3, where the film includes an oxygen barrier layer. 6. The film of claim 5, where the oxygen barrier layer is one of PVDC, EVOH, polyamide and polyester. 7. The film of claim 1, 2, or 3, where the film is radiated prior to or after the coating process. 8. The film of claim 1, 2, or 3, wherein the inner layer comprises at least one homogeneous alpha olefin copolymer. 9. The film of claim 2, where the coating layer comprises polyvinyl butyral. 10. The film of claim 2, where the coating layer comprises nitrocellulose and polyurethane based plasticizer. 11. The film of claim 1, 2, or 3, where the outer layer comprises polystyrene homopolymer and/or styrene butadiene copolymer. 12. A bag, tube or pouch comprising a film of claim 1, 2, or 3. 13. A method for producing a film in accordance with claim 1, 2, or 3, wherein the heat shrinkable film is manufactured and the coating is subsequently applied or laminated onto the outer layer to form the complete film. 14. The method of claim 13, wherein the heat shrinkable film is irradiated before or after the coating process. 15. The method of claim 13, wherein the coating is applied and then cured with heat drying, radiation curing, or UV curing. 16. The method of claim 13, wherein the solution coating is applied to the film by printing the solution onto the film. 17. A method of packaging food, the method comprising: a) providing a food item; andb) placing the food item in the bag, tube or pouch of claim 12. 18. The method of claim 14, wherein the coating is applied and then cured with heat drying, radiation curing, or UV curing. 19. A method of packaging food, the method comprising: a) providing a food item; andb) placing the food item in the film of claim 1, 2, or 3.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (44)
Richards David C. (Wokingham GBX) Williams Maurice S. (Cranleigh GBX) Ward Brian (Blackwater GBX), Apparatus and methods for using packs of flexible tubing in packaging.
Chou Richard T. (Wilmington DE) Deak Gedeon I. (Wilmington DE), Blends of ethylene vinyl alcohol copolymer and amorphous polyamide, and multilayer containers made therefrom.
Richards David C. (Wokingham GBX) Williams Maurice S. (Cranleigh GBX) Ward Brian (Blackwater GBX), Cassette containing flexible tubing to be dispensed therefrom.
Yoshimura Isao (Kanagawa JPX) Mizukami Osamu (Kawasaki JPX) Hata Hideo (Yokohama JPX) Kageyama Junichi (Yokohama JPX) Kaneko Takashi (Kawasaki JPX), Cold drawn high-orientation multilayered film and process for manufacture of said film.
Eggers Holger,DEX ; Kaschel Gregor,DEX ; Gasse Andreas,DEX, Flexible, polyamide-containing multi-layer film having an improved thermo-forming capacity due to moistening.
Bornstein Norman D. (Spartanburg SC) D\Entremont Donald J. (Greenville SC) Weinberg Alan S. (Greenville SC) Schirmer Henry G. (Spartanburg SC) Sun Joseph Zu (Spartanburg SC), Heat shrinkable multi-layer film of hydrolyzed ethylene vinyl acetate and a cross-linked olefin polymer.
Nishimoto Yoshiharu (Iwaki JPX) Yamazaki Kengo (Iwaki JPX) Oosugi Tooru (Niihari JPX), Heat-shrinkable laminated film and process for producing the same.
Ahlgren, Kelly R.; Babrowicz, Robert; Bekele, Solomon; Childress, Blaine C.; Havens, Marvin R.; Herran, Vincent W.; Moffitt, Ronald D.; Shah, Gautam P.; Wofford, George D., High impact strength film containing single site catalyzed copolymer.
Garland Steven B. (Simpsonville SC) d\Entremont Donald J. (Spartanburg SC), High shrink energy/high modulus thermoplastic multi-layer packaging film and bags made therefrom.
Walton Kim L. (Lake Jackson TX) Patel Rajen M. (Lake Jackson TX) Chum Pak-Wing S. (Lake Jackson TX) Obijeski Todd J. (Houston TX), Packaging and wrapping film.
Lustig Stanley (Park Forest IL) Mack Nancy M. (Chicago IL) Schuetz Jeffrey M. (Woodridge IL) Vicik Stephen J. (Darien IL), Process for making biaxially stretched, heat shrinkable VLDPE films.
Lustig Stanley (Park Forest IL) Mack Nancy M. (Chicago IL) Schuetz Jeffrey M. (Woodridge IL) Vicik Stephen J. (Darien IL), Process for making puncture resistant, heat-shrinkable films containing very low density polyethylene.
Lustig Stanley (Park Forest IL) Mack Nancy M. (Chicago IL) Schuetz Jeffrey M. (Woodridge IL) Vicik Stephen J. (Darien IL), Puncture resistant, heat-shrinkable films containing very low density polyethylene.
Lustig Stanley (Park Forest IL) Mack Nancy M. (Chicago IL) Schuetz Jeffrey M. (Woodridge IL) Vicik Stephen J. (Darien IL), Puncture resistant, heat-shrinkable films containing very low density polyethylene.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.