초록 ▼

This invention is directed to a process for making solid, typically particulate, water-swellable material comprising coated water-swellable, preferably hydrogel-forming polymers, which are coated with a coating agent, which is such that it does not rupture when the polymers swell in a liquid, e.g.,

This invention is directed to a process for making solid, typically particulate, water-swellable material comprising coated water-swellable, preferably hydrogel-forming polymers, which are coated with a coating agent, which is such that it does not rupture when the polymers swell in a liquid, e.g., water or saline water. Hereto, the coating agent is extensible in wet state and comprises thereto a wet-extensible material that has a tensile stress at break in the wet state of at least 1 MPa. Typically, the coating agent comprises thereto an elastomeric polymeric material. The invention also relates to solid (particulate) water-swellable material obtainable by the process of the invention.

대표청구항 ▼

1. A process for making a water-swellable material, comprising coated superabsorbent polymer particles and a flow aid, the process comprising the steps of: a) obtaining superabsorbent polymer particles, wherein the superabsorbent polymer is selected from the group consisting of polymers formed from

1. A process for making a water-swellable material, comprising coated superabsorbent polymer particles and a flow aid, the process comprising the steps of: a) obtaining superabsorbent polymer particles, wherein the superabsorbent polymer is selected from the group consisting of polymers formed from monomers of acrylic acid, methacrylic acid, α-chloroacrylic acid, α-cyanoacrylic acid, β-methylacrylic acid (crotonic acid), α-phenylacrylic acid, β-acryloxypropionic acid, sorbic acid, α-chlorosorbic acid, angelic acid, cinnamic acid, p-chlorocinnamic acid, β-stearylacrylic acid, itaconic acid, citroconic acid, mesaconic acid, glutaconic acid, aconitic acid, maleic acid, fumaric acid, tricarboxyethylene, maleic anhydride, and combinations thereof;b) applying a coating agent to at least part of the superabsorbent polymer particles to obtain the water-swellable material, said coating agent being applied in an amount of at least 1% by weight of the water-swellable material, wherein said coating agent comprises a polyurethane, is wet- extensible, and has a tensile stress at break in the wet state of at least 1 Mpa;c) simultaneously or subsequently to step b), adding a flow aid to the polymers of step a). 2. A process according to claim 1, wherein the coating agent has a wet-elongation of at least 400%. 3. A process according to claim 1, wherein the coating agent has a tensile stress at break in the wet state of at least 3 MPa. 4. A process according to claim 1, wherein the coating agent has, in the wet state, a wet secant elastic modulus at 400% elongation (SMwet400%) of at least 0.5 MPa. 5. A process according to claim 1 wherein the coating agent in step b) is applied in a fluid form, the form being selected from the group consisting of a solution, a dispersion, and a hotmelt. 6. A process according to claim 1, wherein said process further comprises an annealing step of submitting the resulting coated superabsorbent polymer particles of step b) to a heat treatment at a temperature of at least 70° C. 7. A process according to claim 1, wherein the superabsorbent polymer particles have a CCRC value of at least 30 g/g. 8. A process according to claim 1 wherein the superabsorbent polymer particles of step a) are liquid-containing and at least partially swollen, comprising said liquid at a level of from 0.5 g/g to about 20 g/g. 9. A process according to claim 1, wherein the coating agent has a first glass transition temperature of 0° C. or less. 10. A process for making a water-swellable material, comprising coated superabsorbent polymer particles and a flow aid, the process comprising the steps of: a) obtaining superabsorbent polymer particles, wherein the superabsorbent polymer is selected from the group consisting of polymers formed from monomers of acrylic acid, methacrylic acid, α-chloroacrylic acid, a-cyanoacrylic acid, β-methylacrylic acid (crotonic acid), α-phenylacrylic acid, β-acryloxypropionic acid, sorbic acid, α-chlorosorbic acid, angelic acid, cinnamic acid, p-chlorocinnamic acid, β-stearylacrylic acid, itaconic acid, citroconic acid, mesaconic acid, glutaconic acid, aconitic acid, maleic acid, fumaric acid, tricarboxyethylene, maleic anhydride, and combinations thereof; andb) applying a coating agent to at least part of the superabsorbent polymer particles, said coating agent being applied in an amount of at least 1% by weight of the water-swellable material, wherein said coating agent comprises a polyurethane, is wet- extensible, and has a tensile stress at break in the wet state of at least 1 Mpa;c) adding a flow aid and heat treating the resulting coated water-swellable polymers of step b) to obtain the water-swellable material comprising coated superabsorbent polymer particles. 11. A process according to claim 10 comprising wherein said heat treating step involves submitting the coated superabsorbent polymer particles to a temperature of at least 140° C. for a predetermined time.