초록 ▼

Thermoplastic polyether polyurethane polymers are disclosed which are mixed with a crosslinking agent to achieve long run times in a melt spinning process to make elastic fibers. The crosslinking agent is preferably a polyether or polyester polyol reacted with a diisocyanate. A melt spinning process

Thermoplastic polyether polyurethane polymers are disclosed which are mixed with a crosslinking agent to achieve long run times in a melt spinning process to make elastic fibers. The crosslinking agent is preferably a polyether or polyester polyol reacted with a diisocyanate. A melt spinning process is also disclosed using a polyether polyurethane with a crosslinking agent. Long melt spinning run times can be achieved without experiencing excessive pressure buildup in the spinneret and fiber breakage. The thermoplastic polyether polyurethane polymers are made by reacting: (1) a blend of two or more hydroxyl terminated intermediates wherein one intermediate is a polyether intermediate and has a higher number average molecular weight than the other said polyether intermediates, and wherein the weighted average number average molecular weight of said blend is greater than 1200 Daltons; (2) at least one polyisocyanate; and (3) at least one hydroxyl terminated chain extender. Melt spun fibers disclosed have excellent dye pickup, bleach resistance, and color fastness. The melt spun fibers can be dyed with polyester fibers and retain excellent physical properties.

대표청구항 ▼

1. A process for producing melt spun thermoplastic polyurethane fibers comprising: (a) melting in an extruder a TPU polymer made by the one shot process and having a shore hardness of from 65 A to 95 A and formed by the reaction of:(i) a first hydroxyl terminated polyether intermediate having a numb

1. A process for producing melt spun thermoplastic polyurethane fibers comprising: (a) melting in an extruder a TPU polymer made by the one shot process and having a shore hardness of from 65 A to 95 A and formed by the reaction of:(i) a first hydroxyl terminated polyether intermediate having a number average molecular weight of from 1500 to 4000 Daltons;(ii) a second hydroxyl terminated polyether intermediate having a number average molecular weight of from 700 to 1500 Daltons;(iii) at least one aromatic hydroxyl terminated chain extender; and(iv) at least one polyisocyanate; wherein said first hydroxyl terminated polyether intermediate is present in larger amount than said second hydroxyl terminated polyether intermediate, wherein the weight ratio of the first polyether hydroxyl terminated intermediate to the second hydroxyl terminated intermediate is from about 60:40 to about 90:10 and wherein said first hydroxyl terminated polyether intermediate has a higher number average molecular weight than said second hydroxyl terminated polyether intermediate, and wherein the weighted average number average molecular weight of said first and said second hydroxyl terminated intermediate is at least 1200 Daltons; (b) adding to said melted thermoplastic polyurethane polymer at least one crosslinking agent made from reacting (i) a hydroxyl terminated polyol selected from the group consisting of polyether, polyester, polycaprolactone, polycarbonate, and mixtures thereof, and (ii) at least one polyisocyanate, wherein said crosslinking agent is added to said melted thermoplastic polyurethane polymer by the method selected from the group consisting of adding said crosslinking agent in said extruder and adding said crosslinking agent after said polymer exits said extruder;(c) feeding said melted thermoplastic polyurethane polymer mixed with said crosslinking agent to at least one spinneret;(d) passing said melted polymer containing said crosslinking agent through said spinneret to produce melt spun fibers;(e) cooling said fibers; and(f) winding said fibers onto bobbins. 2. The process of claim 1 wherein said crosslinking agent is added to said melted thermoplastic polyurethane polymer after said polymer exits said extruder and wherein said crosslinking agent and said polymer are mixed with a dynamic mixer. 3. The process of claim 1 wherein said crosslinking agent is added to said melted thermoplastic polyurethane polymer after said polymer exits said extruder and wherein said crosslinking agent and said polymer are mixed with a static mixer. 4. The process of claim 1 wherein said crosslinking agent is made from reacting a polyester or polyether hydroxyl terminated polyol and diisocyanate. 5. The process of claim 4 wherein said crosslinking agent has a number average molecular weight of from about 1,500 to about 2,800 Daltons. 6. The process of claim 1 wherein said bobbins are wound at a speed of from about 100 to about 3000 meters per minute. 7. The process of claim 6 wherein said bobbins are wound at a speed of from about 300 to about 1200 meters per minute. 8. The process of claim 1 wherein said fibers have a size less than 240 denier. 9. The process of claim 8 wherein said fibers have a size of from about 10 to less than about 240 denier. 10. The process of claim 2 wherein said dynamic mixer is attached to the exit end of said extruder. 11. The process of claim 10 wherein said dynamic mixer comprises a feed screw, a barrel and mixing pins, wherein said feed screw rotates within said barrel and said mixing pins are attached to said barrel and extending toward the centerline of said feed screw. 12. The process of claim 1 wherein said melted polymer and said crosslinking agent have reached greater than 20 percent reaction completion as they exit said spinneret, as evidenced by the disappearance of NCO groups. 13. The process of claim 12 wherein reaction is from about 40 percent to about 50 percent complete.