초록 ▼

The present invention comprises the nitrogen alloying of stainless steel with a gaseous nitrogen compound such as nitrogen gas (N2), or ammonia (NH3) at high temperature wherein the reaction pressure is lowered. A base powder with properties similar to those of a martensitic stainless steel is prepa

The present invention comprises the nitrogen alloying of stainless steel with a gaseous nitrogen compound such as nitrogen gas (N2), or ammonia (NH3) at high temperature wherein the reaction pressure is lowered. A base powder with properties similar to those of a martensitic stainless steel is prepared from a molten metal with the subsequent incorporation of selective additives such as cobalt, chromium, boron, copper, vanadium, niobium and mixtures thereof to improve high temperature resistance to scuffing and adhesive wear. The molten mixture is then atomized by water- or air-atomization to yield a base powder which is mixed with nitrogen or ammonia gas at various pressures in a static or fluidized bed to provide a nitrogen alloyed particulate, i.e., a nitrided particulate alloy. The powder is heated in a hot isostatic press under vacuum with argon gas at reduced pressure and later cooled to ambient temperature.

대표청구항 ▼

1. A process for nitriding stainless steel comprising: a) forming an alloy of martensitic stainless steel from scrap or other ferrous metal through the application of high temperature to liquefy the scrap or ferrous metal to a molten liquid;b) incorporating metal additives to form a molten mixture;c

1. A process for nitriding stainless steel comprising: a) forming an alloy of martensitic stainless steel from scrap or other ferrous metal through the application of high temperature to liquefy the scrap or ferrous metal to a molten liquid;b) incorporating metal additives to form a molten mixture;c) subjecting said molten mixture to water- or gas-atomization to yield a particulate base alloy powder;d) introducing hydrogen or argon gas in order to clean the surface of the powder prior to activation with nitrogen;e) removing the hydrogen or argon gas from the furnace;f) introducing nitrogen or ammonia gas at a partial pressure of from about 500 torr to about 1000 torr in a static or fluidized bed to nitrogen alloy the particulate base powder;g) quenching the nitrogen alloyed particulate base powder;h) heating the nitrogen alloyed powder in a hot iso-static press under vacuum at reduced pressure followed by the injection of argon gas at 1,000 psi;i) increasing the temperature to 1470° F. (800° C.) and the argon pressure to 15,000 psi;j) further increasing the temperature to 1920° F. (1050° C.) for four hours after which the consolidated particulate alloy powder is cooled to ambient temperature. 2. The process as recited in claim 1 further comprising an additional carburization treatment of the stainless steel surface through the secondary application of heat in combination with acetylene or methylene gas. 3. The process of claim 1 wherein said additives are selected from the group consisting of cobalt, chromium, boron, copper, vanadium, niobium and mixtures thereof. 4. The process of claim 3 wherein the particulate alloy formed contains said nitrogen within the individual particles. 5. The process of claim 4 wherein the incorporation of said additives creates a base powder with enhanced corrosion resistance, wear resistance and high temperature resistance. 6. The process of claim 5 whereby the nitrided stainless steel powder is maintained in the hot iso-static press in order to densify the powder into a solid. 7. The process of claim 6 wherein said nitrogen alloyed and densified steel is maintained in a vacuum furnace in the presence of hydrogen or argon gas in order to clean the surface thereof. 8. The process of claim 7 further comprising a second nitriding step after the stainless steel is cooled to ambient temperature consisting of: a) increasing the temperature to 1470° F. (800° C.) and the furnace pressure to 15,000 psi;b) adding argon or hydrogen gas for a time sufficient to clean the surface of said stainless steel;c) removing the hydrogen or argon gas from the furnace;d) introducing nitrogen or ammonia gas at a partial pressure of from about 500 torr to about 1000 torr;e) maintaining said increased temperature, andf) quenching and cooling the stainless steel. 9. The process as recited in claim 8 wherein said steel is hardened throughout. 10. The process as recited in claim 8 wherein said steel is furthered hardened on its surface. 11. The process as recited in claim 8 wherein prior to cooling the final product the temperature is raised to from about 900° F. (480° C.) to about 2500° F. (1370° C.). 12. The process as recited in claim 11 wherein said steel surface is further nitrided or carburized at a temperature of from about 1400° F. (760° C.) to about 2200° F. (1205° C.). 13. The process as recited in claim 12 wherein the quenched nitrided steel alloy is further stabilized in a nitrogen bath at sub-zero temperatures to ensure any remaining austenite is transformed into un-tempered martensite. 14. The process as recited in claim 13 wherein the stabilized nitrided steel is tempered to a specific core hardness.