초록

A decorative laminate is provided and includes a core with at least one epoxy resin impregnated fiberboard sheet. The decorative laminate also includes at least one decorative layer provided adjacent to the core. A method of forming a decorative laminate is also provided.

대표청구항 ▼

1. A decorative laminate comprising: a core comprising at least one epoxy resin impregnated fiberboard sheet, wherein the epoxy resin impregnated fiberboard sheet comprises a sheet of fiberboard impregnated with epoxy resin; andat least one decorative layer provided adjacent to the core,wherein the

1. A decorative laminate comprising: a core comprising at least one epoxy resin impregnated fiberboard sheet, wherein the epoxy resin impregnated fiberboard sheet comprises a sheet of fiberboard impregnated with epoxy resin; andat least one decorative layer provided adjacent to the core,wherein the decorative laminate defines a flexural strength in the range of from about 110 to about 130 MPa under ISO 178. 2. The decorative laminate of claim 1, wherein the thickness of the at least one epoxy resin impregnated fiberboard sheet ranges from about 2 mm to about 10 mm. 3. The decorative laminate of claim 1, wherein the thickness of the at least one epoxy resin impregnated fiberboard sheet ranges from about 4 mm to about 8 mm. 4. The decorative laminate of claim 1, wherein the at least one epoxy resin impregnated fiberboard sheet comprises from about 15 wt. % to about 40 wt. % epoxy resin. 5. The decorative laminate of claim 1, wherein the at least one epoxy resin impregnated fiberboard sheet comprises from about 25 wt. % to about 35 wt. % epoxy resin. 6. The decorative laminate of claim 1, further comprising an overlay sheet adjacent to the decorative layer. 7. The decorative laminate of claim 1, wherein the core further comprises at least one impregnated Kraft paper sheet overlaying the at least one epoxy resin impregnated fiberboard sheet. 8. The decorative laminate of claim 7, wherein the at least one impregnated Kraft paper sheet is selected from the group consisting of pigmented bleached Kraft paper, unpigmented bleached Kraft paper, pigmented α-cellulose paper, unpigmented α-cellulose paper, and combinations thereof. 9. The decorative laminate of claim 7, wherein the at least one impregnated Kraft paper sheet is impregnated with epoxy resin, wherein the epoxy resin comprises from about 1 wt. % to about 10 wt. % of the Kraft paper sheet. 10. The decorative laminate of claim 7, wherein at least one impregnated Kraft paper sheet is impregnated with a combination of epoxy resin and phenolic formaldehyde, wherein the epoxy resin comprises from about 1 wt. % to about 10 wt. % of the impregnated Kraft paper sheet and the phenolic formaldehyde comprises from about 20 wt. % to about 30 wt. % of the impregnated Kraft paper sheet. 11. The decorative laminate of claim 1, wherein the at least one epoxy impregnated fiberboard sheet is covered by at least one impregnated Kraft paper sheet on each major surface of the epoxy resin impregnated fiberboard sheet. 12. The decorative laminate of claim 1, wherein the density of the core of the decorative laminate ranges from about 1.15 g/cm3 to about 1.35 g/cm3. 13. The decorative laminate of claim 1, wherein the density of the core of the decorative laminate ranges from about 1.20 g/cm3 to about 1.30 g/cm3. 14. A method of making the decorative laminate of claim 1 comprising: providing the core;placing the at least one decorative layer adjacent to the core; and applying heat and pressure to the decorative layer and core in an amount sufficient to cure and form a decorative laminate, wherein the density of the core of the decorative laminate ranges from about 1.15 g/cm3 to about 1.35 g/cm3. 15. The method of claim 14, further comprising overlaying the at least one impregnated Kraft paper sheet on the at least one epoxy resin impregnated fiberboard sheet to form the core. 16. The method of claim 15, wherein the at least one impregnated Kraft paper sheet is impregnated with epoxy resin, wherein the epoxy resin comprises from about 1 wt. % to about 10 wt. % of the Kraft paper sheet. 17. The decorative laminate of claim 1, wherein the decorative laminate comprises from about 60 wt. % to about 80 wt. % cellulosic material. 18. The decorative laminate of claim 1, wherein the decorative laminate defines a flexural modulus in the range of from about 9000 to about 10,000 MPa under ISO 178. 19. The decorative laminate of claim 1, wherein the decorative laminate defines a dimensional stability in the cross-direction of 0.30 to 0.15% and a dimensional stability of 0.15 to 0.07% in the machine direction under ISO 4586-1-11B. 20. A decorative laminate comprising: a core comprising at least one epoxy resin impregnated fiberboard sheet, wherein the epoxy resin impregnated fiberboard sheet comprises a sheet of fiberboard impregnated with epoxy resin; andat least one decorative layer provided adjacent to the core,wherein the decorative laminate defines a flexural modulus in the range of from about 9000 to about 10,000 MPa under ISO 178. 21. The decorative laminate of claim 20, wherein the core further comprises at least one impregnated Kraft paper sheet overlaying the at least one epoxy resin impregnated fiberboard sheet. 22. A decorative laminate comprising: a core comprising at least one epoxy resin impregnated fiberboard sheet, wherein the epoxy resin impregnated fiberboard sheet comprises a sheet of fiberboard impregnated with epoxy resin; andat least one decorative layer provided adjacent to the core,wherein the decorative laminate defines a dimensional stability in the cross-direction of 0.30 to 0.15% and a dimensional stability of 0.15 to 0.07% in the machine direction under ISO 4586-1-11B. 23. The decorative laminate of claim 22, wherein the core further comprises at least one impregnated Kraft paper sheet overlaying the at least one epoxy resin impregnated fiberboard sheet.